Abstract A method for preparation of ionically crosslinked ethylene copolymers having excellent physical properties, which comprises melt blending a copolymer of (a) ethylene and (b) an alpha , beta -ethylenically unsaturated carboxylic acid ester selected from the group consisting of isopropyl acrylate, isopropyl methacrylate, tert-butyl acrylate and tert-butyl methacrylate with (c) a metal compound selected from the group consisting of the acetates, formates and oxides of the metals having 1 to 3 valences in Groups I, II, III, IV-A and VIII of the Periodic Table, and keeping the resulting molten blend at a temperature of 200 DEG to 320 DEG C to give in one step an ionically crosslinked ethylene copolymer which comprises the monomer unit components of the formulae: [W] ( CH2CH2) [X] <IMAGE> [Y] <IMAGE> [Z] <IMAGE> wherein R1 is a hydrogen atom or a methyl group, R2 is an isopropyl group or a tert-butyl group, M is a metal atom having 1 to 3 valences in Groups I, II, III, IV-A and VIII of the Periodic Table and n is an integer corresponding to the valence of the metal represented by M in a molar proportion of w : x : y : z which satisfy the relationships of the equations: (1) <IMAGE> (2) <IMAGE> WHEREIN EITHER ONE OF X AND Z CAN BE ZERO.
A method for preparation of ionically crosslinked ethylene copolymers, which comprises melt blending a copolymer comprising as the essential monomer unit components (a) ethylene and (b) at least one α,β-ethylenically unsaturated carboxylic acid ester selected from the group consisting of isoproyl acrylate, isopropyl methacrylate, tert-butyl acrylate and tert-butyl methacrylate with (c) at least one metal compound selected from the group consisting of the acetates, formates and oxides of zinc, magnesium, calcium and sodium, and maintaining the resulting molten blend at a temperature of about 200° to 320° C to give in one step an ionically crosslinked ethylene copolymer which comprises the monomer unit components of the formulae: ##STR5## wherein R 1 is a hydrogen atom or a methyl group, R 2 is an isopropyl group or a tert-butyl group, M is a metal atom from said metal compound (c), and n is an integer corresponding to the valence of the metal represented by M in a molar proportion of w : x : y : z which satisfy the relationships of the equations: ##STR6## wherein either one of x and z can be zero.
Claim 2
Independent Claim
184 words
A method for preparation of ionically crosslinked ethylene copolymers, which comprises melt blending a copolymer comprising as the essential monomer unit components (a) ethylene and (b) at least one α,β-ethylenically unsaturated carboxylic acid ester selected from the group consisting of isoproyl acrylate, isopropyl methacrylate, tert-butyl acrylate and tert-butyl methacrylate with (c) at least one metal compound selected from the group consisting of the acetates, formates and oxides of zinc, magnesium, calcium and sodium, and maintaining the resulting molten blend at a temperature of about 200° to 320° C to give in one step an ionically crosslinked ethylene copolymer which comprises the monomer unit components of the formulae: ##STR5## wherein R 1 is a hydrogen atom or a methyl group, R 2 is an isopropyl group or a tert-butyl group, M is a metal atom from said metal compound (c), and n is an integer corresponding to the valence of the metal represented by M in a molar proportion of w : x : y : z which satisfy the relationships of the equations: ##STR6## wherein either one of x and z can be zero.
Claim 3
Dependent Claim
13 words
The method according to claim 1 wherein the metal compound is an acetate.