Graphite-base filling material for the decomposition of alkali metal amalgams and method of producing same
Assignee: Individual
•
Filing: 1975-04-21
•
Granted: 1977-08-16
•
Expires: 1995-04-21
Abstract
Abstract A graphite-base filling material for the decomposition of alkali metal amalgams, said material containing titanium carbide and incorporating the ingredients in an amount between 69 and 35 wt % for the graphite and between 31 and 65 wt % for the titanium carbide. The method of producing the material disclosed consists in that a carbon filler, a carbon-containing binding agent and titanium or titanium carbide or titanium oxide are intermixed. The titanium or said titanium compounds is used in an amount between 24.8 and 52 wt %, the titanium carbide or titanium oxide being taken in terms of titanium. The mixture obtained is moulded and the blanks moulded are fired at a temperature between 500° and 1200° C. Next, the blanks fired are graphitized at a temperature between 1700° and 1800° C.
Inventors
- 👤 Vladimir Petrovich Chviruk
- 👤 Nina Vasilievna Koneva
- 👤 Alexandr Afanasievich Kilkinov
- 👤 Alexandr Viktorovich Demin
- 👤 Nikolai Nikolaevich Shipkov
- 👤 Konstantin Alexeevich Kosinsky
- 👤 Georgy Mikirtychevich Kamarian
- 👤 Ernest Elizarovich Nemirovsky
- 👤 Igor Nikolaevich Samokhin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:26
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/522; C04B35/56; C04B35/5607; C04B35/5611; C25; C25B; C25B1/00; C25B1/01; C25B1/34; C25B1/36; C25B1/42
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
222 words
A method of producing a graphite-base filling material for the decomposition of alkali metal amalgams and containing between 69 and 35 weight percent of graphite and between 31 and 65 weight percent of titanium carbide, comprising forming a mixture at a temperature of about 100° C containing a carbon filler in powder form, selected from the group consisting of petroleum coke, shale coke, and graphite, and in an amount ranging between 15 and 45.2 weight percent, a carbon-containing binding agent selected from the group consisting of coal pitch, petroleum pitch, and phenol-formaldehyde resin in an amount ranging between 18 and 30 weight percent, and a titanium substance selected from the group consisting of titanium, titanium carbide, and titanium oxide, said titanium substance being in the form of a powder having a particle size of about from 40 to 250 microns and being employed in an amount ranging between 24.8 and 52.0 weight percent based on the amount of titanium present, moulding the resulting mixture into blanks of a desired size and shape, firing the thus-moulded blanks at a temperature of about from 500° to 1200° C for a period of time between 30 and 400 hours, and graphitizing the resulting fired blanks at a temperature of about from 1700° to 1800° C for a period of time between 10 and 50 hours.
Claim 2
Independent Claim
222 words
A method of producing a graphite-base filling material for the decomposition of alkali metal amalgams and containing between 69 and 35 weight percent of graphite and between 31 and 65 weight percent of titanium carbide, comprising forming a mixture at a temperature of about 100° C containing a carbon filler in powder form, selected from the group consisting of petroleum coke, shale coke, and graphite, and in an amount ranging between 15 and 45.2 weight percent, a carbon-containing binding agent selected from the group consisting of coal pitch, petroleum pitch, and phenol-formaldehyde resin in an amount ranging between 18 and 30 weight percent, and a titanium substance selected from the group consisting of titanium, titanium carbide, and titanium oxide, said titanium substance being in the form of a powder having a particle size of about from 40 to 250 microns and being employed in an amount ranging between 24.8 and 52.0 weight percent based on the amount of titanium present, moulding the resulting mixture into blanks of a desired size and shape, firing the thus-moulded blanks at a temperature of about from 500° to 1200° C for a period of time between 30 and 400 hours, and graphitizing the resulting fired blanks at a temperature of about from 1700° to 1800° C for a period of time between 10 and 50 hours.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein the carbon filler is petroleum coke.
Claim 4
Dependent Claim
12 words
The method of claim 1 wherein the carbon filler is shale coke.
Claim 5
Dependent Claim
11 words
The method of claim 1 wherein the carbon filler is graphite.
Claim 6
Dependent Claim
12 words
The method of claim 1 wherein the binding agent is coal pitch.
Claim 7
Dependent Claim
12 words
The method of claim 1 wherein the binding agent is petroleum pitch.
Claim 8
Dependent Claim
12 words
The method of claim 1 wherein the binding agent is phenol-formaldehyde resin.
Claim 9
Dependent Claim
11 words
The method of claim 1 wherein the titanium substance is titanium.
Claim 10
Dependent Claim
12 words
The method of claim 1 wherein the titanium substance is titanium carbide.
Claim 11
Dependent Claim
12 words
The method of claim 1 wherein the titanium substance is titanium oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-15 | 1981-02-14 | 1981-08-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-15 | 1985-02-14 | 1985-08-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-15 | 1989-02-14 | 1989-08-16 | $7700.00 | Window Closed / Lapsed |