Method of making a resin-metal composite grinding wheel
Assignee: Saint Gobain Abrasives Inc
•
Filing: 1976-01-23
•
Granted: 1977-08-16
•
Expires: 1996-01-23
Abstract
Abstract A metal-resin composite material consisting of a continuous metal matrix and a continuous resin matrix fabricated by hot-pressing a mixture of precursors, the precursors for the metal matrix including an elemental metal having a melting point below 450° C, the metal matrix including an intermetallic compound or alloy having a melting point above 500° C, and the continuous resin matrix being fabricable at a temperature above 250° C. Such composite materials have particular utility as a bonding matrix for premium abrasives such as diamond and boron nitride, to form grinding tools.
Inventors
- 👤 Richard H. Sioui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 08:36
CPC Classifications
B; B24; B24D; B24D18/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
160 words
A method of making grinding wheels containing premium abrasives selected from the group consisting of diamond and abrasive boron nitride having a bond matrix consisting of two interlocked continuous phases, one of metal and one of an organic polymer which remains solid at 250° C and below, said metal matrix consisting of a least two metals at least one selected from the group consisting of tin, bismuth, and indium and at least one selected from the group consisting of iron, cobalt, tantalum, manganese, nickel, titanium, silver, and copper and including a phase melting above 250° C, comprising mixing powdered metal, including at least one metal melting below the temperature stability limit of the resin, with abrasive grits, and with an organic resin or resin precursor in powdered form, subjecting such mixture to heat and pressure in a mold such that the metal and resin individually coalesce to form continuous separate interlocked phases throughout which the abrasive particles are uniformly distributed.
Claim 2
Independent Claim
160 words
A method of making grinding wheels containing premium abrasives selected from the group consisting of diamond and abrasive boron nitride having a bond matrix consisting of two interlocked continuous phases, one of metal and one of an organic polymer which remains solid at 250° C and below, said metal matrix consisting of a least two metals at least one selected from the group consisting of tin, bismuth, and indium and at least one selected from the group consisting of iron, cobalt, tantalum, manganese, nickel, titanium, silver, and copper and including a phase melting above 250° C, comprising mixing powdered metal, including at least one metal melting below the temperature stability limit of the resin, with abrasive grits, and with an organic resin or resin precursor in powdered form, subjecting such mixture to heat and pressure in a mold such that the metal and resin individually coalesce to form continuous separate interlocked phases throughout which the abrasive particles are uniformly distributed.
Claim 3
Dependent Claim
15 words
A method as in claim 1 in which the resin employed is a polyimide powder.
Claim 4
Dependent Claim
19 words
A method as in claim 1 in which the volume ratio of resin to metal is 90/10 to 30/70.
Claim 5
Dependent Claim
70 words
A method as in claim 3 in which the abrasive grits are present in an amount of from 10 to 30 volume percent of the total bond plus abrasive volume, the resin is selected from the group consisting of phenol-formaldehyde and polyimide resins, the metal powders are copper and tin in a weight ratio of copper to tin of from 50/50 to 70/30, and the abrasive is copper clad diamond.
Claim 6
Dependent Claim
22 words
A method as in claim 3 in which the abrasive is nickel clad cubic boron nitride and the bond is phenol-formaldehyde resin.
Claim 7
Dependent Claim
31 words
A method as in claim 3 in which the premium abrasive containing matrix is mounted on a core of the same composition except that silicon carbide is substituted for the diamond.
References Cited (Backward Citations)
US2150886A
Cited
US2258774A
Cited
US2243105A
Cited
GB1279413A
Cited
US3650715A
Cited
US3664819A
Cited
US3615302A
Cited
US3850590A
Cited
US3868233A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-15 | 1981-02-14 | 1981-08-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-15 | 1985-02-14 | 1985-08-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-15 | 1989-02-14 | 1989-08-16 | $7700.00 | Window Closed / Lapsed |