Method of compacting shaped powdered objects
Assignee: Westinghouse Electric Corp
•
Filing: 1972-12-22
•
Granted: 1977-08-09
•
Expires: 1992-12-22
Abstract
Abstract A method for densifying to near theoretical density a shaped body of compacted powdered particles, particularly of a refractory material, by preforming a shaped body of compacted particles of a powdered material characterized by voids, enclosing the shaped body within a loose mass of a pressure-transmitting powder disposed within a confining mold, applying a unidirectional pressure to the pressure-transmitting powder within the mold in order to compress the shaped body more compactly while heating the body to at least the densification temperature of the body, preferably in a controlled atmosphere, the temperature and/or pressure being increased incrementally up to the densification temperature of the refractory material, whereby substantially all voids within the compacted shaped body are collapsed.
Inventors
- 👤 Frederick F. Lange
- 👤 Gerald R. Terwilliger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 07:44
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593; B; B22; B22F; B22F3/00; B22F3/12; B22F3/14; B22F3/15
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
214 words
In the method of producing a substantially fully dense shaped member of a refractory powdered material having a given densification temperature, the steps comprising: a. forming a shaped body from refractory powdered material said shaped body characterized by voids and being larger than, but similar to, the desired final shape of the member, b. surrounding the shaped body with a confined mass of a transverse diameter of at least twice that of the maximum transverse dimension of the body, of a non-reactive, non-fusible pressure-transmitting powder having a melting point above the given densification temperature of body, the shaped body being symmetrically or centrally disposed within the confined mass, c. applying an initial pressure undirectionally to the confined mass of pressure-transmitting powder and the body therein, and heating the body to a temperature substantially below its densification temperature, d. thereafter, incrementally increasing the temperature of the body until the given densification temperature is reached and concurrently incrementally increasing the unidirectional pressure to the confined pressure-transmitting powder, the pressure being isostatically transmitted to the body, whereby the voids in the body are substantially completely eliminated and the body has been compacted to the desired shape, and e. thereafter, cooling the shaped body and releasing the pressure, and separating the formed shaped body from the pressure-transmitting powder.
Claim 2
Dependent Claim
214 words
In the method of producing a substantially fully dense shaped member of a refractory powdered material having a given densification temperature, the steps comprising: a. forming a shaped body from refractory powdered material said shaped body characterized by voids and being larger than, but similar to, the desired final shape of the member, b. surrounding the shaped body with a confined mass of a transverse diameter of at least twice that of the maximum transverse dimension of the body, of a non-reactive, non-fusible pressure-transmitting powder having a melting point above the given densification temperature of body, the shaped body being symmetrically or centrally disposed within the confined mass, c. applying an initial pressure undirectionally to the confined mass of pressure-transmitting powder and the body therein, and heating the body to a temperature substantially below its densification temperature, d. thereafter, incrementally increasing the temperature of the body until the given densification temperature is reached and concurrently incrementally increasing the unidirectional pressure to the confined pressure-transmitting powder, the pressure being isostatically transmitted to the body, whereby the voids in the body are substantially completely eliminated and the body has been compacted to the desired shape, and e. thereafter, cooling the shaped body and releasing the pressure, and separating the formed shaped body from the pressure-transmitting powder.
Claim 3
Dependent Claim
30 words
The method of claim 1 in which the material from which the body is formed comprises at least one material selected from the group consisting of refractory metals and ceramics.
Claim 4
Dependent Claim
40 words
The method of claim 1 in which the shaped body consists of MgO modified Si 3 N 4 and the temperature at which the body is densified is from 1600° C. to 1700° C., depending upon the amount of MgO.
Claim 5
Dependent Claim
23 words
The method of claim 3 in which the shaped body consists essentially of Si 3 N 4 and a minor amount of MgO.
Claim 6
Dependent Claim
27 words
The method of claim 1 in which the pressure-transmitting powder consists essentially of at least one material selected from the group consisting of boron nitride and graphite.
Claim 7
Dependent Claim
94 words
The method of claim 1 in which the pressure-transmitting powder is boron nitride and the body comprises a refractory ceramic and an initial pressure of the order of 1000 psi is applied and the initial temperature is about 1000° C., and thereafter a pressure of 2000 psi is applied while the temperature is increased up to about 1650° C., then a pressure of 3000 psi is applied and the temperature increased up to about 1700° C., and finally a pressure of 4000 psi is applied while the temperature increases up to about 1750° C.
Claim 8
Dependent Claim
32 words
The method of claim 1 wherein the heating and compression are done alternately in increments of from about 50° C. to 300° C. and of from 50 psi to about 1000 psi.
Claim 9
Dependent Claim
27 words
The method of claim 1 wherein the pressure-transmitting powder initially forms a semi-rigid mold around the shaped body which mold is compactible upon subsequent increases in pressure.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |