Process for producing anti-blocking and low pressure moldable diallyl phthalate resin molding materials
Assignee: Fujitsu Ltd
•
Filing: 1976-12-08
•
Granted: 1977-08-09
•
Expires: 1996-12-08
Abstract
Abstract A diallyl phthalate resin prepolymer is milled at a temperature of 40 DEG to 100 DEG C together with reinforcing glass fiber and at least one finely divided inorganic filler in the presence of t-butylperoxy 2-ethylhexanoate and at least one other organic peroxide having a half life of one hour at a temperature within the range from 120 DEG to 150 DEG C, cooled and comminuted to provide a molding material which is anti-blocking and has a good workability and shelf stability. The material can be molded at relatively low pressures to moldings of an excellent bending strength.
Inventors
- 👤 Shiroh Takeda
- 👤 Yuji Nagai
- 👤 Takenori Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:01
CPC Classifications
C; C08; C08F; C08F118/00; C08F118/14; C08F118/16; C08F118/18
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
106 words
A process for the production of anti-blocking and low pressure moldable diallyl phthalate resin molding materials, wherein a mixture of 100 parts by weight of at least one diallyl phthalate resin prepolymer 50 to 150 parts by weight of glass fiber, 30 to 200 parts by weight of at least one finely divided inorganic filler, 0.1 to 1.0 part by weight of t-butylperoxy 2-ethylhexanoate and 1.5 to 4.0 parts by weight of at least one organic peroxide having a half life of 1 hour at a temperature within the range of from 120° to 150° C., is milled at a temperature of 40° to 100° C.
Claim 2
Dependent Claim
106 words
A process for the production of anti-blocking and low pressure moldable diallyl phthalate resin molding materials, wherein a mixture of 100 parts by weight of at least one diallyl phthalate resin prepolymer 50 to 150 parts by weight of glass fiber, 30 to 200 parts by weight of at least one finely divided inorganic filler, 0.1 to 1.0 part by weight of t-butylperoxy 2-ethylhexanoate and 1.5 to 4.0 parts by weight of at least one organic peroxide having a half life of 1 hour at a temperature within the range of from 120° to 150° C., is milled at a temperature of 40° to 100° C.
Claim 3
Dependent Claim
27 words
A process in accordance with claim 1 wherein said organic peroxide is selected from the group consisting of t-butylperoxy laurate, t-butylperoxy benzoate, dicumyl peroxide and cyclohexanone peroxide.
Claim 4
Dependent Claim
135 words
A process in accordance with claim 1 wherein said finely divided inorganic filler comprises (i) 6 to 30% by weight, based on the total weight of the mixture of finely divided particles of an inorganic material selected from the group consisting of calcium carbonate, silica, diatomaceous earth, kaolin and talc, said particles having an average particle size in the range 1 to 50 μm, provided that at least 30% by weight of the particles have an actual particle size in the range 20 to 100 μm, in combination with (ii) 8 to 30% by weight, based on the total weight of the mixture, of finely divided particles of an inorganic material capable of imparting a dilatant property to the prepolymer when molten, said last-mentioned particles having an average particle size of less than 1 μm.
Claim 5
Dependent Claim
33 words
A process in accordance with claim 3 wherein said last-mentioned particles are present in the mixture in an amount of 8 to 20% by weight based on the total weight of the mixture.
Claim 6
Dependent Claim
46 words
A process in accordance with claim 1, wherein said finely divided inorganic filler comprises 10 to 50% by weight, based on the total weight of the mixture, of finely divided particles of calcium carbonate, said particles having a particle size of not greater than 0.08 μm.
Claim 7
Dependent Claim
35 words
A process in accordance with claim 5 wherein said particles of calcium carbonate are present in the mixture in an amount of 20 to 45% by weight based on the total weight of the mixture.
References Cited (Backward Citations)
US3579484A
Cited
US3898192A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |