Process for the manufacture of fire retardant particleboard
Assignee: Champion International Corp
•
Filing: 1975-10-09
•
Granted: 1977-08-02
•
Expires: 1995-10-09
Abstract
Abstract A process for manufacturing a unique fire retardant particleboard includes the supersaturation of wood chips, followed by spraying of the wood chips with an aqueous solution of borate and sulfuric acid, after which the sprayed wood chips are allowed to stand for a period of time to become impregnated and saturated with the aqueous solution. The impregnated wood chips are then allowed to dry, after which a urea formaldehyde adhesive is applied to the wood chips, and the chips are consolidated to form the fire resistant wood particleboard.
Inventors
- 👤 Robert P. Coyle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:52
CPC Classifications
C; C08; C08L; C08L97/00; C08L97/02; B; B27; B27N; B27N9/00; C08L61/00; C08L61/20; C08L61/22; C08L61/24; B27K; B27K2200/00; B27K2200/10; B27K2240/00; B27K2240/30; B27K3/00; B27K3/02; B27K3/0278; B27K3/16; B27K3/163; B27K3/32; B27K5/00; B27K5/001; B27K5/04; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/253; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2998; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31957
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
138 words
A process for manufacturing fire resistant particleboard, comprising the steps of: a. spraying wood chips having a moisture content of 125-150% of the weight of the dry wood chips, with an aqueous solution of a borate and sulfuric acid heated to a temperature of about 150°-225° F., said aqueous solution having a pH of about 4.0-6.0; b. storing said sprayed wood chips for a stand time of approximately 10-20 minutes to permit said chips to become thoroughly impregnated and saturated with said aqueous solution; c. drying said impregnated wood chips; d. applying a urea-formaldehyde adhesive to said impregnated wood chips in an amount in the range of about 2% to 12% by weight based on the dry weight of the wood chips; and e. consolidating the wood chips under heat and pressure to form the fire-resistant wood particleboard.
Claim 2
Dependent Claim
138 words
A process for manufacturing fire resistant particleboard, comprising the steps of: a. spraying wood chips having a moisture content of 125-150% of the weight of the dry wood chips, with an aqueous solution of a borate and sulfuric acid heated to a temperature of about 150°-225° F., said aqueous solution having a pH of about 4.0-6.0; b. storing said sprayed wood chips for a stand time of approximately 10-20 minutes to permit said chips to become thoroughly impregnated and saturated with said aqueous solution; c. drying said impregnated wood chips; d. applying a urea-formaldehyde adhesive to said impregnated wood chips in an amount in the range of about 2% to 12% by weight based on the dry weight of the wood chips; and e. consolidating the wood chips under heat and pressure to form the fire-resistant wood particleboard.
Claim 3
Dependent Claim
37 words
A process as defined by claim 1 wherein said borate is borax (Na 2 B 4 O 7 .X H 2 O) wherein X has a value selected from the group consisting of 0, 5 and 10.
Claim 4
Dependent Claim
42 words
A process as defined by claim 1 wherein the amount of aqueous solution sprayed onto the wood chips is in the range of approximately 10% to 40% by weight based on the weight of the dry wood content of the wood chips.
References Cited (Backward Citations)
US3321421A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-01 | 1981-01-31 | 1981-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-01 | 1985-01-31 | 1985-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-01 | 1989-01-31 | 1989-08-02 | $7700.00 | Window Closed / Lapsed |