Production of p-phenylene sulfide polymers
Assignee: Phillips Petroleum Co
•
Filing: 1975-05-27
•
Granted: 1977-08-02
•
Expires: 1995-05-27
Abstract
Abstract A method is provided for producing p-phenylene sulfide polymers by contacting a p-dihalobenzene, an alkali metal sulfide, an organic amide, and a lithium salt selected from among lithium carbonate and lithium borates at polymerization conditions. The use of the lithium carbonate or lithium borates in addition to the other compounds contacted to form a composition results in p-phenylene sulfide polymers of higher molecular weight than produced without the lithium compounds, as evidenced by higher viscosity and lower melt flow of the polymer than produced by compared methods.
Inventors
- 👤 Robert W. Campbell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:22
CPC Classifications
C; C08; C08G; C08G75/00; C08G75/02; C08G75/0204; C08G75/025; C08G75/0254
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
61 words
A method for producing polymers comprising: a. forming a composition by contacting at least one p-dihalobenzene, at least one alkali metal sulfide, at least one organic amide, and at least one lithium salt selected from the group consisting of lithium carbonate and lithium borates, and b. maintaining at least a portion of said composition at polymerization conditions to produce a polymer.
Claim 2
Independent Claim
61 words
A method for producing polymers comprising: a. forming a composition by contacting at least one p-dihalobenzene, at least one alkali metal sulfide, at least one organic amide, and at least one lithium salt selected from the group consisting of lithium carbonate and lithium borates, and b. maintaining at least a portion of said composition at polymerization conditions to produce a polymer.
Claim 3
Dependent Claim
66 words
A method of claim 1 wherein a first composition comprising: a. a mixture of at least one alkali metal sulfide, at least one of said lithium salts, and at least one organic amide is formed, and b. at least a portion of said mixture is contacted with at least one p-dihalobenzene under polymerization conditions for a period of time sufficient to form a p-phenylene sulfide polymer.
Claim 4
Dependent Claim
98 words
A method of claim 1 where said p-dihalobenzene is represented by the formula ##STR2## where each X is selected from the group consisting of chlorine, bromine, and iodine, and each R is selected from the group consisting of hydrogen and hydrocarbyl in which the hydrocarbyl can be an alkyl, cycloalkyl, or aryl radical or combination thereof such as alkaryl or aralkyl, the total number of carbon atoms in each molecule being within the range of 6 to about 24, with the proviso that in at least 50 mole percent of the p-dihalobenzene employed each R must be hydrogen.
Claim 5
Dependent Claim
98 words
A method of claim 2 wherein the p-dihalobenzene is represented by the formula ##STR3## where each X is selected from the group consisting of chlorine, bromine, and iodine, and each R is selected from the group consisting of hydrogen and hydrocarbyl in which the hydrocarbyl can be an alkyl, cycloalkyl, or aryl radical or combination thereof such as alkaryl or aralkyl, the total number of carbon atoms in each molecule being within the range of 6 to about 24, with the proviso that in at least 50 mole percent of the p-dihalobenzene employed each R must be hydrogen.
Claim 6
Dependent Claim
47 words
A method of claim 3 wherein the mole ratio of p-dihalobenzene to alkali metal sulfide is within the range of about 0.9:1 to about 2:1, and the mole ratio of the lithium salt to alkali metal sulfide is within the range of about 0.05:1 to about 4:1.
Claim 7
Dependent Claim
47 words
A method of claim 4 wherein the mole ratio of p-dihalobenzene to alkali metal sulfide is within the range of about 0.9:1 to about 2:1, and the mole ratio of the lithium salt to alkali metal sulfide is within the range of about 0.05:1 to about 4:1.
Claim 8
Dependent Claim
56 words
A mehtod of claim 5 wherein the polymerization conditions present comprise a reaction temperature within the range of about 125° C. to about 450° C., a pressure sufficient to maintain the p-dihalobenzene and organic amide substantially in the liquid phase and the reaction time is in the range of about 10 minutes to about 72 hours.
Claim 9
Dependent Claim
56 words
A method of claim 6 wherein the polymerization conditions present comprise a reaction temperature within the range of about 125° C. to about 450° C., a pressure sufficient to maintain the p-dihalobenzene and organic amide substantially in the liquid phase and the reaction time is in the range of about 10 minutes to about 72 hours.
Claim 10
Dependent Claim
60 words
A method of claim 8 wherein said p-dihalobenzene is p-dichlorobenzene, said alkali metal sulfide is sodium sulfide, said organic amide is N-methyl-2-pyrrolidone, and said lithium salt is lithium carbonate; the reaction temperature is within the range of about 175° C. to about 350° C. and the reaction time is within the range of about 1 hour to about 8 hours.
Claim 11
Dependent Claim
60 words
A method of claim 8 wherein said p-dihalobenzene is p-dichlorobenzene, said alkali metal sulfide is sodium sulfide, said organic amide is N-methyl-2-pyrrolidone, and said lithium salt is lithium metaborate; the reaction temperature is within the range of about 175° C to about 350° C. and the reaction time is within the range of about 1 hour to about 8 hours.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-01 | 1981-01-31 | 1981-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-01 | 1985-01-31 | 1985-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-01 | 1989-01-31 | 1989-08-02 | $7700.00 | Window Closed / Lapsed |