Process for the production of polyolefin powder
Assignee: Tonen General Sekiyu KK
•
Filing: 1975-11-19
•
Granted: 1977-07-26
•
Expires: 1995-11-19
Abstract
Abstract Spherical polyolefin (or modified polyolefin) powders having high bulk density, narrow particle size distribution and good powder flowability are prepared by cooling a polyolefin solution comprising a solvent and nonsolvent for the polyolefin and containing a small amount of an inorganic compound and, if desired, water. The polyolefin powders are suitable for powder coating. Suitable solvents are hydrocarbons, such as hexane, heptane, etc., and a mixture of hydrocarbon and nonsolvent for polyolefin such as methyl alcohol, ethyl alcohol, isopropyl alcohol, etc. The ratio of a hydrocarbon/nonsolvent is 95/5 - 30/70, preferably 90/10 - 50/50. Suitable inorganic compounds are phosphoric acid, sulfuric acid, sulfurous acid, hydrochloric acid, sodium hydroxide, potassium hydroxide, ammonium hydroxide, inorganic salts thereof, etc. and the most preferable inorganic compound is phosphoric acid.
Inventors
- 👤 Hiroshi Inoue
- 👤 Makoto Yoda
- 👤 Shozo Wada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:37
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/14; C08J2323/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
88 words
A process for the production of a fine polyolefin powder which comprises precipitating the polyolefin from a solution of the said polyolefin in a mixture of a solvent and non-solvent therefor, said mixture having a ratio of solvent to non-solvent in the range of about 95:5 to about 30:70 parts by weight, in the presence of about 5 to about 500 ppm by weight, of an inorganic compound capable of forming an ion or ion pair in water or the non-solvent and then drying the precipitated polyolefin powder.
Claim 2
Dependent Claim
88 words
A process for the production of a fine polyolefin powder which comprises precipitating the polyolefin from a solution of the said polyolefin in a mixture of a solvent and non-solvent therefor, said mixture having a ratio of solvent to non-solvent in the range of about 95:5 to about 30:70 parts by weight, in the presence of about 5 to about 500 ppm by weight, of an inorganic compound capable of forming an ion or ion pair in water or the non-solvent and then drying the precipitated polyolefin powder.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein water is also present in an amount of up to about 2.0% by weight.
Claim 4
Dependent Claim
19 words
The process of claim 1 wherein the ratio of solvent to non-solvent is 90:10 to 50:50 parts by weight.
Claim 5
Dependent Claim
29 words
The process of claim 1 wherein the polyolefin is present in the amount of 5 to 50 parts by weight of polyolefin per 100 parts by weight of solvent.
Claim 6
Dependent Claim
90 words
A process for the production of a fine polyolefin powder which comprises dissolving the polyolefin in a mixture of a solvent with a non-solvent therefor, said mixture having a ratio of solvent to non-solvent in the range of about 95:5 to 30:70 parts by weight, precipitating the polyolefin from the mixture by cooling in the presence of about 5 to about 500 ppm by weight of an inorganic compound capable of producing an ion or ion pair in the non-solvent or in water, and then drying the precipitated polyolefin powder.
Claim 7
Dependent Claim
90 words
A process for the production of a fine polyolefin powder which comprises dissolving the polyolefin in a mixture of a solvent with a non-solvent therefor, said mixture having a ratio of solvent to non-solvent in the range of about 95:5 to 30:70 parts by weight, precipitating the polyolefin from the mixture by cooling in the presence of about 5 to about 500 ppm by weight of an inorganic compound capable of producing an ion or ion pair in the non-solvent or in water, and then drying the precipitated polyolefin powder.
Claim 8
Dependent Claim
20 words
The process of claim 5 wherein water is also present in an amount of up to about 2.0% by weight.
Claim 9
Dependent Claim
22 words
The process of claim 6 wherein the solvent is selected from the group consisting of aliphatic hydrocarbons, aromatic hydrocarbons, and halogenated hydrocarbons.
Claim 10
Dependent Claim
25 words
The process of claim 7 wherein the non-solvent is selected from the group consisting of acetone methyl alcohol, ethyl alcohol, isopropyl alcohol and n-butyl alcohol.
Claim 11
Dependent Claim
18 words
The process of claim 6 wherein the polyolefin is dissolved at a temperature of 60° to 300° C.
Claim 12
Dependent Claim
12 words
The process of claim 6 wherein the inorganic compound is phosphoric acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-25 | 1981-01-24 | 1981-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-25 | 1985-01-24 | 1985-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-25 | 1989-01-24 | 1989-07-26 | $7700.00 | Window Closed / Lapsed |