Production of p-phenylene sulfide polymers
Assignee: Phillips Petroleum Co
•
Filing: 1975-05-27
•
Granted: 1977-07-26
•
Expires: 1995-05-27
Abstract
Abstract A method is provided for producing p-phenylene sulfide polymers by contacting at least one p-dihalobenzene, at least one alkali metal sulfide, at least one organic amide and at least one alkali metal sulfonate at polymerization conditions. The use of an alkali metal sulfonate in addition to the other compounds contacted to form the reaction mixture results in a p-phenylene sulfide polymer of higher molecular weight than is produced without the alkali metal sulfonate, as evidenced by higher inherent viscosity and lower melt flow of the polymer than produced by the compared methods.
Inventors
- 👤 Robert W. Campbell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:58
CPC Classifications
C; C08; C08G; C08G75/00; C08G75/02; C08G75/0204; C08G75/025; C08G75/0254
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
53 words
A method for producing polymers comprising: a. forming a composition by contacting at least one p-dihalobenzene, at least one alkali metal sulfide, at least one organic amide, and at least one alkali metal sulfonate, and b. maintaining at least a portion of said composition at polymerization conditions to produce a p-phenylene sulfide polymer.
Claim 2
Independent Claim
53 words
A method for producing polymers comprising: a. forming a composition by contacting at least one p-dihalobenzene, at least one alkali metal sulfide, at least one organic amide, and at least one alkali metal sulfonate, and b. maintaining at least a portion of said composition at polymerization conditions to produce a p-phenylene sulfide polymer.
Claim 3
Independent Claim
61 words
A method for producing polymers comprising: a. forming a first composition of at least one alkali metal sulfide, at least one organic amide, and at least one alkali metal sulfonate, and b. contacting at least one p-dihalobenzene with at least a portion of said first composition under polymerization conditions for a period of time sufficient to form a p-phenylene sulfide polymer.
Claim 4
Independent Claim
61 words
A method for producing polymers comprising: a. forming a first composition of at least one alkali metal sulfide, at least one organic amide, and at least one alkali metal sulfonate, and b. contacting at least one p-dihalobenzene with at least a portion of said first composition under polymerization conditions for a period of time sufficient to form a p-phenylene sulfide polymer.
Claim 5
Dependent Claim
98 words
A method of claim 1 wherein said p-dihalobenzene is represented by the formula ##STR2## where each X is selected from the group consisting of chlorine, bromine, and iodine, and each R is selected from the group consisting of hydrogen and hydrocarbyl in which the hydrocarbyl can be an alkyl, cycloakyl, or aryl radical or combination thereof such as alkaryl or aralkyl, the total number of carbon atoms in each molecule being within the range of 6 to about 24, with the proviso that in at least 50 mole percent of the p-dihalobenzene employed each R must be hydrogen.
Claim 6
Dependent Claim
98 words
A method of claim 2 wherein said p-dihalobenzene is represented by the formula ##STR3## where each X is selected from the group consisting of chlorine, bromine, and iodine, and each R is selected from the group consisting of hydrogen and hydrocarbyl in which the hydrocarbyl can be an alkyl, cycloakly, or aryl radical or combination thereof such as alkaryl or aralkyl, the total number of carbon atoms in each molecule being within the range of 6 to about 24, with the proviso that in at least 50 mole percent of the p-dihalobenzene employed each R must be hydrogen.
Claim 7
Dependent Claim
46 words
A method of claim 3 wherein the mole ratio of p-dihalobenzene to alkali metal sulfide is within the range of about 0.9:1 to about 2:1, the mole ratio of alkali metal sulfonate to alkali metal sulfide is within the range of about 0.05:1 to about 4:1.
Claim 8
Dependent Claim
46 words
A method of claim 4 wherein the mole ratio of p-dihalobenzene to alkali metal sulfide is within the range of about 0.9:1 to about 2:1, the mole ratio of alkali metal sulfonate to alkali metal sulfide is within the range of about 0.05:1 to about 4:1.
Claim 9
Dependent Claim
54 words
A method of claim 5 wherein the polymerization conditions comprise a reaction temperature within the range of about 125° C. to about 450° C., the reaction pressure is sufficient to maintain the p-dihalobenzene substantially in the liquid phase and the reaction time is within the range of about 10 minutes to about 72 hours.
Claim 10
Dependent Claim
54 words
A method of claim 6 wherein the polymerization conditions comprise a reaction temperature within the range of about 125° C. to about 450° C., the reaction pressure is sufficient to maintain the p-dihalobenzene substantially in the liquid phase and the reaction time is within the range of about 10 minutes to about 72 hours.
Claim 11
Dependent Claim
69 words
A method of claim 7 wherein the alkali metal sulfonates are represented by the formula R'SO 3 M, where R' is a hydrocarbyl radical selected from alkyl, cycloalkyl, aryl, and combinations thereof such as alkaryl or aralkyl, with the number of carbon atoms in each R' being within the range of 1 to about 20 and M is an alkali metal selected from lithium, sodium, potassium, rubidium, and cesium.
Claim 12
Dependent Claim
45 words
A method of claim 8 wherein the alkali metal sulfonates are chosen from among lithium methanesulfonate, sodium ethanesulfonate, potassium 2-propanesulfonate, sodium 1-butanesulfonate, rubidium 3-hexanesulfonate, lithium 1-decanesulfonate, sodium 2-ethyl-1-dodecanesulfonate, cesium 1-eicosanesulfonate, potassium cyclohexanesulfonate, lithium 3-methylcyclopentanesulfonate, sodium cyclohexylmethanesulfonate, sodium benzenesulfonate, rubidium p-toluenesulfonate, cesium 2-phenylethanesulfonate, and mixtures thereof.
Claim 13
Dependent Claim
60 words
A method of claim 10 wherein said p-dihalobenzene is p-dichlorobenzene, said alkali metal sulfide is sodium sulfide, said organic amide is N-methyl-2-pyrrolidone, and said alkali metal sulfonate is sodium benzenesulfonate, said reaction temperature is within the range of about 175° C. to about 350° C. and said reaction time is within the range of about 1 to about 8 hours.
Claim 14
Dependent Claim
60 words
A method of claim 10 wherein said p-dihalobenzene is p-dichlorobenzene, said alkali metal sulfide is sodium sulfide, said organic amide is N-methyl-2-pyrrolidone, and said alkali metal sulfonate is sodium 1-butanesulfonate, said reaction temperature is within the range of about 175° C. to about 350° C. and said reaction time is within the range of about 1 to about 8 hours.
References Cited (Backward Citations)
US3607843A
Cited
US3725362A
Cited
US3699087A
Cited
US3763124A
Cited
US3786035A
Cited
US3919177A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-25 | 1981-01-24 | 1981-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-25 | 1985-01-24 | 1985-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-25 | 1989-01-24 | 1989-07-26 | $7700.00 | Window Closed / Lapsed |