US4038205A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing cadmium free green emitting cathodoluminescent phosphor
Assignee: GTE Sylvania Inc
•
Filing: 1976-07-06
•
Granted: 1977-07-26
•
Expires: 1996-07-06
Abstract
Abstract A green emitting ZnS : Cu, Al cathodoluminescent phosphor having x and y coordinate values of from 0.250 to 0.280 and 0.560 to 0.615 respectively, is produced by a critical firing schedule exemplified by slow heating to about 1000° C, soaking at this temperature for about 1 hour, followed by slow cooling at about 3° C per minute to 700° C, followed by air quenching. The phosphor is useful for example, in tri-color television color television cathode ray tube.
Inventors
- 👤 Henry B. Minnier
- 👤 H. David Layman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 11:48
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/64; C09K11/641; C09K11/642
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
74 words
Process for producing a green emitting cathodoluminescent phosphor consisting essentially of zinc sulfide activated by from 10 to 200 parts per million of copper and coactivated by from 20 to 600 parts per million of aluminum and containing less than 50 parts per million of halogen, the phosphor characterized by a cathodoluminescent emission having x and y coordinate values within the range of 0.250 to 0.280 and 0.560 to 0.6150, respectively, the process comprising:
Claim 2
Dependent Claim
74 words
Process for producing a green emitting cathodoluminescent phosphor consisting essentially of zinc sulfide activated by from 10 to 200 parts per million of copper and coactivated by from 20 to 600 parts per million of aluminum and containing less than 50 parts per million of halogen, the phosphor characterized by a cathodoluminescent emission having x and y coordinate values within the range of 0.250 to 0.280 and 0.560 to 0.6150, respectively, the process comprising:
Claim 3
Dependent Claim
35 words
(a) firing a powder mixture of zinc sulfide, a copper compound and an aluminum compound at a temperature of about 950° to 1010° C. for about 1 minute to 2 hours in a non-oxidizing atmosphere,
Claim 4
Dependent Claim
35 words
(a) firing a powder mixture of zinc sulfide, a copper compound and an aluminum compound at a temperature of about 950° to 1010° C. for about 1 minute to 2 hours in a non-oxidizing atmosphere,
Claim 5
Dependent Claim
43 words
(b) cooling the phosphor from the firing temperature at the rate of about 2° C. per minute up to about 30° C. per minute down to a temperature within the range of about 760° C. to 870° C., in a nonoxidizing atmosphere, and
Claim 6
Dependent Claim
43 words
(b) cooling the phosphor from the firing temperature at the rate of about 2° C. per minute up to about 30° C. per minute down to a temperature within the range of about 760° C. to 870° C., in a nonoxidizing atmosphere, and
Claim 7
Dependent Claim
34 words
(c) cooling the phosphor from a temperature within the range of about 760° to 870° C. at the rate of at least 50° C. per minute down to a temperature below about 40° C.
Claim 8
Dependent Claim
34 words
(c) cooling the phosphor from a temperature within the range of about 760° to 870° C. at the rate of at least 50° C. per minute down to a temperature below about 40° C.
Claim 9
Dependent Claim
41 words
Process of claim 1 wherein said mixture is fired for a time of about 15 minutes to 1 hour, and wherein said copper and aluminum compounds are each selected from the group consisting of chloride, bromide, sulfide, nitrate and carbonate compounds.
Claim 10
Dependent Claim
15 words
Process of claim 1 wherein said mixture is fired in the presence of elemental carbon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-25 | 1981-01-24 | 1981-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-25 | 1985-01-24 | 1985-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-25 | 1989-01-24 | 1989-07-26 | $7700.00 | Window Closed / Lapsed |