Assignee: US Philips Corp
•
Filing: 1975-03-17
•
Granted: 1977-07-26
•
Expires: 1995-03-17
Abstract
Abstract A method of manufacturing a homopolar electret from a foil of a non-polar polymer, preferably TEFLON-FEP or PFA. The polymer foil is formed into an electret by heating it above the transition temperature and below the melting temperature of the polymer under the influence of an electrostatic field of a magnitude such that a homopolar charge is injected into the foil which is greater than the desired value, and the foil then being cooled to room temperature. However, before the transition temperature is reached during cooling, the electrostatic field is switched off so that the charge surplus is thereby removed. If the foil is disposed between two electrodes, a better result can be obtained by providing the foil with a vacuum-deposited metal layer in contact with the positive electrode during the formation. The charging time lies between 0.02 secs. and 1 min. and is preferably smaller than 5 secs.
Inventors
- 👤 Jan van Turnhout
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:51
CPC Classifications
H; H01; H01G; H01G7/00; H01G7/02; H01G7/021; H01G7/023; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49226
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
101 words
A method for producing a homopolar electret from a foil of a non-polar polymer which comprises, heating said foil to a temperature above the glass-rubber transition temperature but below the melting temperature of the polymer and applying an electrostatic field thereto of a magnitude such that a homopolar charge is injected into the foil which is greater than the desired charge value thereby to form an electret foil, cooling the foil to room temperature but removing the electrostatic field before said glass-rubber transition temperature is reached whereby the surplus charge is removed from the electret foil after removal of the field.
Claim 2
Independent Claim
101 words
A method for producing a homopolar electret from a foil of a non-polar polymer which comprises, heating said foil to a temperature above the glass-rubber transition temperature but below the melting temperature of the polymer and applying an electrostatic field thereto of a magnitude such that a homopolar charge is injected into the foil which is greater than the desired charge value thereby to form an electret foil, cooling the foil to room temperature but removing the electrostatic field before said glass-rubber transition temperature is reached whereby the surplus charge is removed from the electret foil after removal of the field.
Claim 3
Dependent Claim
21 words
A method as claimed in claim 1 which comprises increasing the temperature still further after termination of charging the electret foil.
Claim 4
Dependent Claim
23 words
A method as claimed in claim 1 characterized in that the charging time of the foil lies between 0.01 sec. and 1 min.
Claim 5
Dependent Claim
19 words
A method as claimed in claim 3, characterized in that the foil charging time is less than 5 secs.
Claim 6
Dependent Claim
47 words
A method as claimed in claim 1, characterized in that the foil is disposed between two oppositely situated electrodes wherein at least one electrode is provided with a tissue-like intermediate layer, the electrodes being connected to a direct voltage source during the formation of the electret foil.
Claim 7
Dependent Claim
82 words
A method as claimed in claim 5 wherein the foil of a non-polar polymer is comprised of polymerized fluorine-carbon compounds, said foil being provided with a very thin vacuum-deposited metal layer at one side, characterized in that when the foil is disposed between the electrodes the metal layer of the foil is in direct contact with an electrode which is connected to the positive terminal of the direct voltage source, the intermediate layer being disposed between the foil and the other electrode.
Claim 8
Independent Claim
119 words
A method of making a homopolar electret from a foil of non-polar polymer material which comprises, heating the foil to a temperature above the glass-rubber transition temperature but below the melting temperature of the polymer during a given time interval, applying, during a part of said given time interval, an electrostatic field to the foil of a magnitude sufficient to inject a homopolar charge into the foil which is greater than the desired charge value thereby to polarize the foil and form an electret, removing the electrostatic field from the foil during a second part of said given time interval thereby to drain off the excess charge from the electret foil, and cooling the electret foil to room temperature.
Claim 9
Independent Claim
119 words
A method of making a homopolar electret from a foil of non-polar polymer material which comprises, heating the foil to a temperature above the glass-rubber transition temperature but below the melting temperature of the polymer during a given time interval, applying, during a part of said given time interval, an electrostatic field to the foil of a magnitude sufficient to inject a homopolar charge into the foil which is greater than the desired charge value thereby to polarize the foil and form an electret, removing the electrostatic field from the foil during a second part of said given time interval thereby to drain off the excess charge from the electret foil, and cooling the electret foil to room temperature.
Claim 10
Dependent Claim
22 words
A method as claimed in claim 7 wherein said part of the given time interval lies between 0.01 second and 1.0 minute.
Claim 11
Dependent Claim
29 words
A method as claimed in claim 8 further comprising heating the foil to a higher temperature subsequent to the polarization of the foil and during the given time interval.
Claim 12
Dependent Claim
22 words
A method as claimed in claim 7 wherein said part of the given time interval lies between 0.1 second and 5.0 seconds.
Claim 13
Dependent Claim
84 words
A method as claimed in claim 7 wherein the foil is disposed between two opposed spaced apart electrodes connected to a source of DC voltage during said part of the given time interval for applying the electrostatic field to the foil, one electrode having a thin intermediate layer of material between said one electrode and the foil, the DC voltage being of a magnitude to ionize the air between said one electrode and the foil thereby to form a homopolar charge in the foil.
Claim 14
Dependent Claim
17 words
A method as claimed in claim 11 wherein said intermediate layer is composed of a glass fabric.
Claim 15
Dependent Claim
39 words
A method as claimed in claim 7 wherein the foil is polarized for one minute at a temperature 200° C. and then further comprising heating the foil to a temperature of approximately 220° C. during said given time interval.
Claim 16
Dependent Claim
37 words
A method as claimed in claim 7 wherein the length of time of said second part of the given time interval is determined by the amount of excess charge to be drained off from the electret foil.
Claim 17
Dependent Claim
123 words
An electret foil comprising a thin body of dielectric polymer material having two substantially parallel surfaces, one of said surfaces having adhered thereto a metal layer, said dielectric material having a homopolar charge formed therein by heating the dielectric material to a temperature above the glass-rubber transition temperature but below the melting temperature of the polymer, applying an electrostatic field to the dielectric material of a magnitude to inject a homopolar charge into the foil greater than the desired charge value while the dielectric material is held above said transition temperature and removing the field before the dielectric material is cooled down to the transition temperature thereby to remove any surplus charge formed in the dielectric material while the field was applied thereto.
Claim 18
Dependent Claim
123 words
An electret foil comprising a thin body of dielectric polymer material having two substantially parallel surfaces, one of said surfaces having adhered thereto a metal layer, said dielectric material having a homopolar charge formed therein by heating the dielectric material to a temperature above the glass-rubber transition temperature but below the melting temperature of the polymer, applying an electrostatic field to the dielectric material of a magnitude to inject a homopolar charge into the foil greater than the desired charge value while the dielectric material is held above said transition temperature and removing the field before the dielectric material is cooled down to the transition temperature thereby to remove any surplus charge formed in the dielectric material while the field was applied thereto.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-25 | 1981-01-24 | 1981-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-25 | 1985-01-24 | 1985-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-25 | 1989-01-24 | 1989-07-26 | $7700.00 | Window Closed / Lapsed |