Process for producing convoluted, fiberized, cellulose fibers and sheet products therefrom

Claim 2

A process for producing convoluted, fiberized cellulose fibers which are twisted and bent in a substantially lasting manner, without appreciable reduction of fiber length or freeness, comprising subjecting low moisture content cellulose pulp at a consistency of from about 70%, up to about 90% by weight, based on the dry basis weight of the pulp, said consistency being sufficient to preclude substantial fibrillation and the attendant strength and bonding development, while at the same time preventing fiber damage and scorching, to mechanical treatment which gives rise to structural deformation of the fibers causing them to become convoluted and at the same time fiberizing and fluffing the pulp, the mechanical treatment including continuously feeding the pulp at a relatively high through-put rate into and through a work space formed between opposed, spaced-apart working elements to a point of discharge from the work space, the elements including opposed surfaces capable of engaging the pulp, the feeding step being conducted at a rate correlated with the rate of relative movement of the working elements and the spacing between the working surfaces so as to maintain the work space filled with a mass of fibers under sufficient compression so that the pulp is engaged by the working surfaces and contortive forces are imparted to the fibers which are effective to produce convoluted, fiberized fibers which are substantially nonfibrillated.

Claim 3

The process of claim 1, wherein in order to further minimize and prevent fiber damage and scorching, the low moisture content cellulose pulp is maintained at a consistency from about 70% up to about 85% by weight.

Claim 4

The process of claim 1, wherein the magnitude of the contortive forces applied to the pulp within the work space by the working surfaces is at least about 0.75 HPD/ADT.

Claim 5

The process of claim 1, wherein the amount of compression applied to the mass of fibers filling the work space by the opposed working elements so that the pulp is engaged by the working surfaces and contortive forces are imparted to the fibers is at least 5 pounds per square inch.

Claim 6

The process of claim 1, wherein the contortive forces applied to the fibers filling the work space are such that the convoluted, fiberized cellulose fibers produced, in the dry state, substantially retain their convoluted quality for a period of time of appreciably in excess of 48 hours.

Claim 7

The process of claim 1, wherein the contortive forces imparted to the fibers are sufficient to cause a reduction in the Young's modulus of sheets produced from said convoluted, fiberized cellulose fibers of at least about 50% as compared to the Young's modulus of sheets made from similar fibers which have not been subjected to said contortive forces.

Claim 8

The process of claim 1, wherein the working elements are equipped with opposed co-axially disposed working surfaces in a generally facing relationship throughout the entire extent of the work space, at least one of the working surfaces rotating in a fixed plane relative to the other.

Claim 9

The process of claim 7, wherein the rotatable working surfaces include bars projecting inwardly therefrom, and rotating at a relative rate capable of providing an ICPM value of at least about 300 × 10 6 .

Claim 10

The process of claim 1, wherein the operating condition is maintained at a level of at least about 3 pounds of pulp per square inch of effective cross-sectional area of work space per rpm.

Claim 11

The process of claim 7, wherein the feed rate is correlated with the spacing between the working surfaces and the rate of relative movement of the working elements so as to maintain the work space filled with a mass of pulp under sufficient pressure and contortive forces being imparted to the fibers, the feed rate being at least about 20 pounds per minute up to about 80 pounds per minute, and the spacing between the working surfaces being at least 0.04 inch up to about 0.12 inch.

Claim 12

The process of claim 8, wherein the tangential velocity of the working surfaces sufficient to impart contortive forces to the pulp within the work space is such that the working elements rotate at a relative tangential velocity of not less than about 1,000 feet per minute.

Claim 13

A process for making a soft, absorbent, bulky paper sheet which comprises: a. producing convoluted, fiberized cellulose fibers which are twisted and bent in a substantially lasting manner, without appreciable reduction of fiber length or freeness, by subjecting low moisture content cellulose pulp at a consistency of from about 70%, up to about 90% by weight, based on the dry basis weight of the pulp, said consistency being sufficient to preclude substantial fibrillation and the attendant strength and bonding development, while at the same time preventing fiber damage and scorching, to mechanical treatment which gives rise to structural deformation of the fibers causing them to become convoluted and at the same time fiberizing and fluffing the pulp, the mechanical treatment including continuously feeding the pulp at a relatively high through-put rate into and through a work space formed between opposed, spaced-apart working elements to a point of discharge from the work space, the elements including opposed surfaces capable of engaging the pulp, the feeding step being conducted at a rate correlated with the rate of relative movement of the working elements and the spacing between the working surfaces so as to maintain the work space filled with a mass of fibers under sufficient compression so that the pulp is engaged by the working surfaces and contortive forces are imparted to the fibers which are effective to produce convoluted, fiberized fibers which are substantially nonfibrillated; b. forming an aqueous fiber furnish including said convoluted, fiberized cellulose fibers; c. forming a wet web from said aqueous fiber furnish; and d. thermally drying said wet web to form said soft, absorbent, bulky paper sheet, said sheet having a basis weight of from about 5 pounds per 3,000 square feet up to about 100 pounds per 3,000 square feet, and a bulk softness of from about 0.25 HOM/(caliper) 2 × 10 5 up to about 1.25 HOM/(caliper) 2 × 10 5 .

Claim 14

A process for making a soft, absorbent, bulky paper sheet which comprises: a. producing convoluted, fiberized cellulose fibers which are twisted and bent in a substantially lasting manner, without appreciable reduction of fiber length or freeness, by subjecting low moisture content cellulose pulp at a consistency of from about 70%, up to about 90% by weight, based on the dry basis weight of the pulp, said consistency being sufficient to preclude substantial fibrillation and the attendant strength and bonding development, while at the same time preventing fiber damage and scorching, to mechanical treatment which gives rise to structural deformation of the fibers causing them to become convoluted and at the same time fiberizing and fluffing the pulp, the mechanical treatment including continuously feeding the pulp at a relatively high through-put rate into and through a work space formed between opposed, spaced-apart working elements to a point of discharge from the work space, the elements including opposed surfaces capable of engaging the pulp, the feeding step being conducted at a rate correlated with the rate of relative movement of the working elements and the spacing between the working surfaces so as to maintain the work space filled with a mass of fibers under sufficient compression so that the pulp is engaged by the working surfaces and contortive forces are imparted to the fibers which are effective to produce convoluted, fiberized fibers which are substantially nonfibrillated; b. forming an aqueous fiber furnish including said convoluted, fiberized cellulose fibers; c. forming a wet web from said aqueous fiber furnish; and d. thermally drying said wet web to form said soft, absorbent, bulky paper sheet, said sheet having a basis weight of from about 5 pounds per 3,000 square feet up to about 100 pounds per 3,000 square feet, and a bulk softness of from about 0.25 HOM/(caliper) 2 × 10 5 up to about 1.25 HOM/(caliper) 2 × 10 5 .

Claim 15

The process of claim 12, wherein a substantial amount of water is removed from said web, prior to said thermal-drying step, by nonthermal dewatering means.

Claim 16

The process of claim 13, wherein said nonthermal dewatering means comprises means for applying mechanical compression to said web.

Claim 17

The process of claim 12, wherein said aqueous furnish includes convoluted, fiberized cellulose fibers and cellulosic papermaking fibers, respectively.

Claim 18

The process of claim 15, wherein said sheet is comprised of up to about 70% by weight of said convoluted, fiberized cellulose fibers, based on the total weight of fibers in said sheet.

Claim 19

The process of claim 13, wherein the consistency of the web, after being subjected to said nonthermal dewatering step, is from about 20%, up to about 60% by weight, based on the total weight of fibers in said web on a dry basis.

Claim 20

The process of claim 12, wherein the reduction in the Young's modulus of the soft, absorbent, bulky sheet product made from fibers which have undergone said mechanical treatment is at least 50%, as compared to the Young's modulus of a sheet made from similar fibers which are untreated.

Claim 21

The process of claim 12, wherein the conditions under which convolution is conducted is correlated so that contortive forces are applied to the pulp resulting in an average fiber width reduction of up to about 20% from their original flat, ribbon-like state.

Claim 22

The process of claim 12, wherein said bulk softness is from about 0.4 HOM/(caliper) 2 × 10 5 , up to about 1.00 HOM/(caliper) 2 × 10 5 .

Claim 23

The process of claim 12, wherein after said wet web is thermally dried, the dried sheet is pneumatically embossed to improve the bulk and softness of said dried web.

Claim 24

The process of claim 12, wherein a percent reduction in sheet stiffness of at least about 50% is provided for sheets subjected to said mechanical treatment as compared to the stiffness of sheets made from comparable, untreated fibers.