Mechanical seals
Assignee: U S GRAPHITE Inc A CORP OF MI
•
Filing: 1976-05-13
•
Granted: 1977-07-19
•
Expires: 1996-05-13
Abstract
Abstract A long wearing mechanical seal assembly comprising two paired sealing members of predetermined composition wherein the contacting surfaces are in rotating relationship with respect to one another, and wherein the members cooperate to prevent fluid flow between the contacting surfaces, a first one of said members being composed of a material suitable for a seal seat (e.g., cast iron, alumina ceramic or chrome plated steel) and the second member comprising a seal composed of a graphitic matrix that is filled with particulate, non-abrasive matter (e.g. Nepheline syenite, alpha-alumina or quartz) which is harder than the matrix and which has a microhardness greater than the matric to prevent the seal from wearing at the wear rate of the matrix.
Inventors
- 👤 James R. Floyd
- 👤 Paul N. Dalenberg
- 👤 Robert B. Slivensky
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:03
CPC Classifications
F; F16; F16J; F16J15/00; F16J15/16; F16J15/34; F16J15/3496; Y; Y10; Y10S; Y10S277/00; Y10S277/935; Y10S277/936; Y10S277/938; Y10S277/939; Y10S277/941
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
142 words
A mechanical seal and seat assembly of the class wherein a relatively movable seal and seat therefor have confronting lapped sealing interfaces to seal off a fluid which wets the interface and wherein the seat has an interface microhardness in the range of at least about 200 kilograms per square millimeter, the seal being formed by homogeneously dispersing non-abrasive particles in a particulate matrix mix comprising hydrocarbon binder and graphite, compressing the mix and particles into seal form, and baking the seal to substantially dehydrogenize the binder to create a non-graphitic free carbon bond for the graphite and particles, the seal having said particles in said seal interface; and the particles having a microhardness in the range of at least about 200 kilograms per square millimeter and being of a size, hardness and shape to be non-abrasively smooth to the seat interface.
Claim 2
Dependent Claim
142 words
A mechanical seal and seat assembly of the class wherein a relatively movable seal and seat therefor have confronting lapped sealing interfaces to seal off a fluid which wets the interface and wherein the seat has an interface microhardness in the range of at least about 200 kilograms per square millimeter, the seal being formed by homogeneously dispersing non-abrasive particles in a particulate matrix mix comprising hydrocarbon binder and graphite, compressing the mix and particles into seal form, and baking the seal to substantially dehydrogenize the binder to create a non-graphitic free carbon bond for the graphite and particles, the seal having said particles in said seal interface; and the particles having a microhardness in the range of at least about 200 kilograms per square millimeter and being of a size, hardness and shape to be non-abrasively smooth to the seat interface.
Claim 3
Dependent Claim
19 words
The improvement of claim 1 wherein said non-abrasive particles are less than 10 percent by weight of the seal.
Claim 4
Dependent Claim
25 words
The improvement of claim 1 wherein one of the seal and seat members is a stationary member and the other member is a rotating member.
Claim 5
Dependent Claim
18 words
The improvement of claim 3 wherein the member composed of a filled graphitic matrix is the rotating member.
Claim 6
Dependent Claim
34 words
The improvement of claim 4 wherein the stationary member is composed of cast iron and the non-abrasive particles in the rotating member have a microhardness of about 200 to 4500 kilograms per square millimeter.
Claim 7
Dependent Claim
24 words
The improvement of claim 5 wherein the non-abrasive particles in the rotating member are selected from the group consisting of nepheline syenite and quartz.
Claim 8
Dependent Claim
33 words
The improvement of claim 4 wherein the stationary member is composed of alpha-alumina ceramic and the non-abrasive particles in the rotating member are selected from the group consisting of alpha-alumina and tungsten carbide.
Claim 9
Dependent Claim
35 words
The improvement of claim 4 wherein the stationary member is composed of chrome plated steel and the non-abrasive particles in the rotating member have a microhardness of about 200 to 4500 kilograms per square millimeter.
Claim 10
Dependent Claim
24 words
The improvement of claim 8 wherein the non-abrasive particles in the rotating member are selected from the group consisting of quartz and tungsten carbide.
Claim 11
Dependent Claim
21 words
The improvement of claim 1 wherein the stationary member has a microhardness of about 200 to 4500 kilograms per square millimeter.
Claim 12
Dependent Claim
20 words
The improvement of claim 1 wherein the non-abrasive particles have a particle size in the range of about 100 microns.
Claim 13
Dependent Claim
14 words
The improvement of claim 1 wherein the non-abrasive particles are smooth surfaced and curvilinear.
Claim 14
Dependent Claim
24 words
The improvement of claim 1 wherein the volume of the non-abrasive particles is about 0.025 to 45 percent of the volume of the matrix.
Claim 15
Dependent Claim
22 words
The improvement of claim 1 wherein the non-abrasive particles have a particle size in the range of about 0.1 to 100 microns.
Claim 16
Dependent Claim
78 words
A mechanical seal member for use with a seat having an interface microhardness in the range of at least about 200 kilograms per square millimeter and composed of a graphitic matrix filled and carbon bonded with non-abrasive particulate matter having a microhardness of about 200 to 4500 kilograms per square millimeter, a particle size of about 0.1 to 100 microns, the volume of said filler matter being about 0.025 to 45 percent of the volume of the matrix.
Claim 17
Dependent Claim
78 words
A mechanical seal member for use with a seat having an interface microhardness in the range of at least about 200 kilograms per square millimeter and composed of a graphitic matrix filled and carbon bonded with non-abrasive particulate matter having a microhardness of about 200 to 4500 kilograms per square millimeter, a particle size of about 0.1 to 100 microns, the volume of said filler matter being about 0.025 to 45 percent of the volume of the matrix.
Claim 18
Dependent Claim
19 words
The improvement of claim 1 wherein the seat is an alumina ceramic and the non-abrasive particles comprise calcined alpha-alumina.
Claim 19
Dependent Claim
147 words
A mechanical seal and seat assembly of the class wherein a relatively movable seal and seat therefor have confronting lapped sealing interfaces to seal off a fluid which wets the interface and wherein the seat has an interface microhardness in the range of at least about 200 kilograms per square millimeter, the seal being formed by homogeneously dispersing carbide forming particles in a particulate matrix mix comprising hydrocarbon binder and graphite, compressing the mix and particles into seal form, and baking the seal to substantially dehydrogenize the binder to create a non-graphitic free carbon bond for the graphite and to form dispersed carbide particles in situ in said matrix at said seal interface; and the particles having a microhardness in the range of at least about 200 kilograms per square millimeter and being of a size, hardness and shape to be non-abrasively smooth to the seat interface.
Claim 20
Dependent Claim
147 words
A mechanical seal and seat assembly of the class wherein a relatively movable seal and seat therefor have confronting lapped sealing interfaces to seal off a fluid which wets the interface and wherein the seat has an interface microhardness in the range of at least about 200 kilograms per square millimeter, the seal being formed by homogeneously dispersing carbide forming particles in a particulate matrix mix comprising hydrocarbon binder and graphite, compressing the mix and particles into seal form, and baking the seal to substantially dehydrogenize the binder to create a non-graphitic free carbon bond for the graphite and to form dispersed carbide particles in situ in said matrix at said seal interface; and the particles having a microhardness in the range of at least about 200 kilograms per square millimeter and being of a size, hardness and shape to be non-abrasively smooth to the seat interface.
Claim 21
Dependent Claim
23 words
The improvement of claim 17 wherein the carbide particles have a microhardness in the range of 200 to 4500 kilograms per square millimeter.
Claim 22
Dependent Claim
12 words
The improvement of claim 17 wherein the carbide particles are tungsten carbide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-18 | 1981-01-17 | 1981-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-18 | 1985-01-17 | 1985-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-18 | 1989-01-17 | 1989-07-19 | $7700.00 | Window Closed / Lapsed |