Process and composition for cementing casing in a well
Assignee: BP Corp North America Inc
•
Filing: 1976-07-12
•
Granted: 1977-07-19
•
Expires: 1996-07-12
Abstract
Abstract A process for reducing the waiting-on-cement (WOC) time associated with the cementing of a casing string in an oil well involving the specific improvement of pumping into the well a highly retarded cement slurry containing a dispersed encapsulated accelerator, such as calcium chloride or anhydrous sodium metasilicate, wherein the encapsulating material is specifically selected such that it will melt at a temperature above the bottom-hole circulating temperature but below the bottomhole static temperature of the well to be cemented. Petroleum-derived waxes and petroleum-derived waxes in combination with vinyl resins, such as wax-compatible copolymers of ethylene and vinyl acetate, are particularly suitable as the meltable encapsulating material exhibiting excellent strength and abrasion resistance as well as serving as a moisture barrier. The improved process is particularly useful in cementing deep hot wells.
Inventors
- 👤 Charles A. Powers
- 👤 George B. Holman
- 👤 Robert C. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 04:19
CPC Classifications
C; C09; C09K; C09K8/00; C09K8/42; C09K8/46; C04; C04B; C04B20/00; C04B20/10; C04B20/1018; C04B40/00; C04B40/06; C04B2103/00; C04B2103/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
121 words
A process of cementing casing in a deep hot well comprising the steps of: a. pumping a highly retarded cement slurry down said casing whereby said slurry will be forced up the annulus between said casing and the well bore wall wherein said highly retarded slurry contains a dispersed accelerator, said accelerator being encapsulated with a material capable of melting at a temperature below the bottom-hole static temperature of said well but not capable of melting at a temperature corresponding to the bottom-hole circulating temperature, and b. holding the cement slurry in a noncirculating static state at the desired level in said well such that said encapsulating material will melt releasing the accelerator and induce a flash set of said cement.
Claim 2
Dependent Claim
121 words
A process of cementing casing in a deep hot well comprising the steps of: a. pumping a highly retarded cement slurry down said casing whereby said slurry will be forced up the annulus between said casing and the well bore wall wherein said highly retarded slurry contains a dispersed accelerator, said accelerator being encapsulated with a material capable of melting at a temperature below the bottom-hole static temperature of said well but not capable of melting at a temperature corresponding to the bottom-hole circulating temperature, and b. holding the cement slurry in a noncirculating static state at the desired level in said well such that said encapsulating material will melt releasing the accelerator and induce a flash set of said cement.
Claim 3
Dependent Claim
21 words
A process of claim 1 wherein encapsulating material is selected such that its melting point is between 125° and 450° F.
Claim 4
Dependent Claim
13 words
A process of claim 2 wherein the encapsulating material is an organic wax.
Claim 5
Dependent Claim
21 words
A process of claim 3 wherein the accelerator is selected from the group consisting of calcium chloride and anhydrous sodium metasilicate.
Claim 6
Dependent Claim
22 words
A process of claim 1 wherein the accelerator is selected from a group consisting of calcium chloride, sodium chloride and sodium silicate.
Claim 7
Dependent Claim
123 words
An oil-well cement slurry for cementing in a well containing an effective amount up to about 15 percent by weight of an encapsulated cement accelerator wherein the encapsulating material covers the entire external surface of the accelerator, isolating said cement accelerator from said oil-well cement slurry and wherein said encapsulating material is capable of melting at a temperature below the bottom-hole static temperature of an oil or gas well to be cemented but not capable of melting at a temperature corresponding to the bottom-hole circulating temperature of said well, whereby, after placement, the cement slurry is held in a static noncirculating state such that the slurry temperature causes the encapsulating material to release the accelerator which induces a rapid set of the cement.
Claim 8
Dependent Claim
123 words
An oil-well cement slurry for cementing in a well containing an effective amount up to about 15 percent by weight of an encapsulated cement accelerator wherein the encapsulating material covers the entire external surface of the accelerator, isolating said cement accelerator from said oil-well cement slurry and wherein said encapsulating material is capable of melting at a temperature below the bottom-hole static temperature of an oil or gas well to be cemented but not capable of melting at a temperature corresponding to the bottom-hole circulating temperature of said well, whereby, after placement, the cement slurry is held in a static noncirculating state such that the slurry temperature causes the encapsulating material to release the accelerator which induces a rapid set of the cement.
Claim 9
Dependent Claim
12 words
A cement slurry of claim 6 wherein said slurry is highly retarded.
Claim 10
Dependent Claim
18 words
A cement slurry of claim 7 wherein said encapsulated accelerator is calcium chloride coated with an organic wax.
Claim 11
Dependent Claim
19 words
A cement slurry of claim 7 wherein said encapulsated accelerator is anhydrous sodium metasilicate coated with an organic wax.
Claim 12
Dependent Claim
22 words
A cement slurry of claim 9 wherein said organic wax is comprised of a petroleum-derived paraffinic wax and an ethylene vinylacetate copolymer.
Claim 13
Independent Claim
90 words
A method of preserving the desirable short wait-on-cement time characteristic of an accelerated cement slurry in cementing applications, wherein external retarder-type contamination is anticipated, involving the specific improvement of adding to the cement slurry, prior to placement, an encapsulated accelerator having a coating which will soften and melt at the temperatures characteristic of the cement placement, placing said cement slurry with said encapsulated accelerator and holding said encapsulated accelerator in place such that said coating softens and melts, releasing said accelerator which promotes a rapid set of said cement slurry.
Claim 14
Independent Claim
90 words
A method of preserving the desirable short wait-on-cement time characteristic of an accelerated cement slurry in cementing applications, wherein external retarder-type contamination is anticipated, involving the specific improvement of adding to the cement slurry, prior to placement, an encapsulated accelerator having a coating which will soften and melt at the temperatures characteristic of the cement placement, placing said cement slurry with said encapsulated accelerator and holding said encapsulated accelerator in place such that said coating softens and melts, releasing said accelerator which promotes a rapid set of said cement slurry.
Claim 15
Dependent Claim
37 words
A method of claim 11 wherein said accelerator is anhydrous sodium metasilicate and said coating is selected from the group consisting of petroleum-derived paraffinic wax and a mixture of petroleum-derived paraffinic wax with an ethylene vinylacetate copolymer.
Claim 16
Dependent Claim
45 words
A cement slurry comprising from about 2 parts by weight to about 15 parts by weight anhydrous sodium metasilicate granules per 100 parts by weight dry cement, wherein said anhydrous sodium metasilicate granules are isolated from the slurry by an external coating of organic wax.
Claim 17
Dependent Claim
45 words
A cement slurry comprising from about 2 parts by weight to about 15 parts by weight anhydrous sodium metasilicate granules per 100 parts by weight dry cement, wherein said anhydrous sodium metasilicate granules are isolated from the slurry by an external coating of organic wax.
References Cited (Backward Citations)
US2621132A
Cited
US2985239A
Cited
US2848340A
Cited
US3028913A
Cited
US3368623A
Cited
US3420299A
Cited
US3804058A
Cited
US3873332A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-18 | 1981-01-17 | 1981-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-18 | 1985-01-17 | 1985-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-18 | 1989-01-17 | 1989-07-19 | $7700.00 | Window Closed / Lapsed |