US4035467A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of injection molding a thermoset polyurethane article
Assignee: Motors Liquidation Co
•
Filing: 1975-11-21
•
Granted: 1977-07-12
•
Expires: 1995-11-21
Abstract
Abstract In accordance with a preferred embodiment of this invention, a controlled phase change is used to trigger an exothermic polymerization reaction in an injection molding process. The subject method comprises first, dispersing a crystalline urea reactant, 1,3-bis-(3-isocyanatotolyl) urea, in a liquid polyoxyalkylene polyol or mixtures thereof. Since the polyols do not dissolve the urea at room temperature, the dispersion is storage stable over an extended period of time. This is unexpected because the isocyanate and hydroxyl functionalities are normally quite reactive. In the barrel of the injection molding machine, the dispersion is heated to a temperature at which the polyol will begin to dissolve and thereby react with the crystalline urea to initiate a controllable polyurethane-forming reaction. At present, the specific urea disclosed above is preferred because of its ability to (1) form a storage stable dispersion, (2) dissolve in the polyol at a temperature below its decomposition temperature, and (3) react with the polyol at controllable rates once it has dissolved. All three properties are important to this invention and they enable the practitioner to use conventional injection molding equipment.
Inventors
- 👤 Gregory A. Campbell
- 👤 Howard W. Cox
- 👤 William C. Meluch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:15
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; B; B29; B29C; B29C45/00; B29C45/0001; B29C67/00; B29C67/24; B29C67/246; C08G18/70; C08G18/72; C08G18/77; C08G18/78; C08G18/7806; C08G18/7818; C08G18/7825; Y; Y10; Y10S; Y10S264/00; Y10S264/77
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
150 words
A method of forming a cross-linked polyurethane article in an injection molding machine comprising the steps of: (a) forming a room temperature storage stable dispersion comprising a liquid polyoxyalkylene triol, 1,3-bis-(3-isocyanatotolyl) urea and a catalyst which urea at about room temperature is insoluble in and therefore non-reactive with the triol; (b) feeding said dispersion into the barrel of the molding machine; (c) simultaneously moving said dispersion through the barrel and heating the dispersion therealong to a temperature at which the urea dissolves in the triol and initiates a polyurethane forming polymerization reaction between the isocyanate functionalities on the urea and the hydroxyl functionalities on the triol; (d) injecting the heated dispersion into the cavity of a mold to form the shape of said article; and (e) maintaining the heated and reacting dispersion in the mold until reaction has at least reached that point at which the article is substantially self-sustaining.
Claim 2
Independent Claim
150 words
A method of forming a cross-linked polyurethane article in an injection molding machine comprising the steps of: (a) forming a room temperature storage stable dispersion comprising a liquid polyoxyalkylene triol, 1,3-bis-(3-isocyanatotolyl) urea and a catalyst which urea at about room temperature is insoluble in and therefore non-reactive with the triol; (b) feeding said dispersion into the barrel of the molding machine; (c) simultaneously moving said dispersion through the barrel and heating the dispersion therealong to a temperature at which the urea dissolves in the triol and initiates a polyurethane forming polymerization reaction between the isocyanate functionalities on the urea and the hydroxyl functionalities on the triol; (d) injecting the heated dispersion into the cavity of a mold to form the shape of said article; and (e) maintaining the heated and reacting dispersion in the mold until reaction has at least reached that point at which the article is substantially self-sustaining.
Claim 3
Independent Claim
167 words
A method of molding a crosslinked polyurethane article in an injection molding machine comprising the steps of: (a) forming a storage stable dispersion comprising a polyfunctional isocyanatoaryl urea, a liquid polyoxyalkylene triol, and a catalyst, which urea at about room temperature is insoluble in and thereby nonreactive with the triol and which urea is soluble in and thereby will polymerize with said triol to form a polyurethane at an elevated temperature which is below the thermal decomposition temperature of the urea; (b) feeding the dispersion into the barrel of the molding machine; (c) simultaneously moving the dispersion through the barrel and heating the dispersion therealong to a temperature at which the urea becomes soluble in the triol to initiate the polymerization reaction; (d) injecting said heated dispersion into the cavity of a heated mold to form the shape of the article; and (e) maintaining the heated and reacting dispersion in the mold until reaction has at least reached that point at which the article is substantially self-sustaining.
Claim 4
Independent Claim
167 words
A method of molding a crosslinked polyurethane article in an injection molding machine comprising the steps of: (a) forming a storage stable dispersion comprising a polyfunctional isocyanatoaryl urea, a liquid polyoxyalkylene triol, and a catalyst, which urea at about room temperature is insoluble in and thereby nonreactive with the triol and which urea is soluble in and thereby will polymerize with said triol to form a polyurethane at an elevated temperature which is below the thermal decomposition temperature of the urea; (b) feeding the dispersion into the barrel of the molding machine; (c) simultaneously moving the dispersion through the barrel and heating the dispersion therealong to a temperature at which the urea becomes soluble in the triol to initiate the polymerization reaction; (d) injecting said heated dispersion into the cavity of a heated mold to form the shape of the article; and (e) maintaining the heated and reacting dispersion in the mold until reaction has at least reached that point at which the article is substantially self-sustaining.
References Cited (Backward Citations)
CA678250A
Cited
US2757185A
Cited
US2757184A
Cited
US2818404A
Cited
US2902474A
Cited
US3409461A
Cited
US3458373A
Cited
US3427639A
Cited
US3939222A
Cited
US3917792A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-11 | 1981-01-10 | 1981-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-11 | 1985-01-10 | 1985-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-11 | 1989-01-10 | 1989-07-12 | $7700.00 | Window Closed / Lapsed |