Method for preparation of inorganic flocculating composition
Assignee: Caffaro SpA
•
Filing: 1975-10-29
•
Granted: 1977-07-12
•
Expires: 1995-10-29
Abstract
Abstract The invention relates to an inorganic flocculating composition consisting of water soluble salts of Al, Fe, Mg and Ca and obtained by attacking clays containing the above chemical elements, the attack being carried out with an acid capable of forming water soluble salts of the said chemical elements. The said composition is capable of destroying the stability of colloidal slurries and can be employed without involving strict conditions, such as pH, temperature and so on.
Inventors
- 👤 Liborio Casale
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:13
CPC Classifications
C; C02; C02F; C02F1/00; C02F1/52; C02F1/5236
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
133 words
A method for the preparation of a liquid flocculating composition comprising the steps of: (a) slurrying raw clay containing Al, Fe, Mg and Ca elements so as to obtain a semi-fluid slurry with a percentage of dry matters between 33% and 55% on a weight basis, the particles of the clay being of a size of not over 1 millimeter in diameter; (b) treating while stirring the clay or suspension with an inorganic acid capable of forming Al, Fe, Mg and Ca water soluble salts at a temperature up to about 90° C; (c) completing the acid attack of the clay at a temperature of about 150° C. under a pressure of about 4 atmospheres; (d) progressively cooling the mixture and (e) filtrating said mixture into a solid residue and a liquid phase.
Claim 2
Independent Claim
133 words
A method for the preparation of a liquid flocculating composition comprising the steps of: (a) slurrying raw clay containing Al, Fe, Mg and Ca elements so as to obtain a semi-fluid slurry with a percentage of dry matters between 33% and 55% on a weight basis, the particles of the clay being of a size of not over 1 millimeter in diameter; (b) treating while stirring the clay or suspension with an inorganic acid capable of forming Al, Fe, Mg and Ca water soluble salts at a temperature up to about 90° C; (c) completing the acid attack of the clay at a temperature of about 150° C. under a pressure of about 4 atmospheres; (d) progressively cooling the mixture and (e) filtrating said mixture into a solid residue and a liquid phase.
Claim 3
Dependent Claim
20 words
The method according to claim 1, wherein said clay is bentonite clay and said acid is 98% concentrated sulphuric acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-11 | 1981-01-10 | 1981-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-11 | 1985-01-10 | 1985-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-11 | 1989-01-10 | 1989-07-12 | $7700.00 | Window Closed / Lapsed |