Method for producing synthetic sodium aluminosilicate ion-exchange material from calcined kaolin clay

Claim 2

In a process for producing crystals of an ion-exchange crystalline alkali metal aluminosilicate wherein calcined kaolin clay is reacted with a source of alkali metal oxide and optionally additional sources of silica and alumina, the improvement which comprises chlorinating kaolin clay previously calcined to metakaolin condition in a gas-solid reaction at a temperature in the range of 600° to 980° C. to volatilize iron impurities in the clay before using said calcined clay as a reactant to produce said alkali metal aluminosilicate.

Claim 3

In a process for producing finely divided particles of a synthetic crystalline sodium aluminosilicate zeolite by heating an aqueous alkaline reaction mixture consisting essentially of oxides of aluminum, silicon and sodium, the major portion of said aluminum and silicon oxides being provided by the inclusion in the reaction mixture of finely divided particles of metakaolin until finely divided zeolite crystals form, separating the zeolite crystals from the reaction liquid and washing the crystals, which process results in a zeolite product having a brightness substantially less than the brightness of the clay used to produce said metakaolin reactant, the improvement whereby the zeolite product will have a substantially higher brightness, which comprises removing iron-bearing impurities from the metakaolin by volatilizing the impurities with a chlorine-bearing gas at a temperature in the range of 600° to 980° C. before including the metakaolin in the aqueous alkaline reaction mixture used to produce the zeolite.

Claim 4

In a process for producing finely divided particles of a synthetic crystalline sodium aluminosilicate zeolite by heating an aqueous alkaline reaction mixture consisting essentially of oxides of aluminum, silicon and sodium, the major portion of said aluminum and silicon oxides being provided by the inclusion in the reaction mixture of finely divided particles of metakaolin until finely divided zeolite crystals form, separating the zeolite crystals from the reaction liquid and washing the crystals, which process results in a zeolite product having a brightness substantially less than the brightness of the clay used to produce said metakaolin reactant, the improvement whereby the zeolite product will have a substantially higher brightness, which comprises removing iron-bearing impurities from the metakaolin by volatilizing the impurities with a chlorine-bearing gas at a temperature in the range of 600° to 980° C. before including the metakaolin in the aqueous alkaline reaction mixture used to produce the zeolite.

Claim 5

In a process for producing finely divided crystals of sodium zeolite A which comprises forming an aqueous reaction mixture consisting essentially of oxides of aluminum, silicon and sodium, the major portion of said aluminum and silicon oxides being provided by the inclusion in the reaction mixture of finely divided particles of metakaolin obtained by calcining naturally-occurring kaolin clay, heating the reaction mixture until sodium zeolite A crystals form, and recovering sodium zeolite A as the product, the improvement which comprises heating said metakaolin in an atmosphere of chlorine-bearing gas at a temperature in the range of 750° to 850° C. for a time sufficient to volatilize iron-bearing impurities in the metakaolin, removing the volatilized iron-bearing impurities from the metakaolin, and cooling the metakaolin thus treated before incorporating the metakaolin in the reaction mixture and crystallizing sodium zeolite A therefrom, whereby the sodium zeolite A product will have a higher brightness, when measured by the TAPPI procedure, than the product would have in the absence of the treatment of said metakaolin in the atmosphere of a chlorine-bearing gas.

Claim 6

In a process for producing finely divided crystals of sodium zeolite A which comprises forming an aqueous reaction mixture consisting essentially of oxides of aluminum, silicon and sodium, the major portion of said aluminum and silicon oxides being provided by the inclusion in the reaction mixture of finely divided particles of metakaolin obtained by calcining naturally-occurring kaolin clay, heating the reaction mixture until sodium zeolite A crystals form, and recovering sodium zeolite A as the product, the improvement which comprises heating said metakaolin in an atmosphere of chlorine-bearing gas at a temperature in the range of 750° to 850° C. for a time sufficient to volatilize iron-bearing impurities in the metakaolin, removing the volatilized iron-bearing impurities from the metakaolin, and cooling the metakaolin thus treated before incorporating the metakaolin in the reaction mixture and crystallizing sodium zeolite A therefrom, whereby the sodium zeolite A product will have a higher brightness, when measured by the TAPPI procedure, than the product would have in the absence of the treatment of said metakaolin in the atmosphere of a chlorine-bearing gas.

Claim 7

The method of claim 3 wherein the metakaolin reactant is obtained by removing discrete colored titania and iron-bearing impurities from naturally-occurring hydrated kaolin clay by flotation and bleaching the flotation beneficiated clay with a dithionite bleach in aqueous acidic media before calcining the hydrated clay to produce metakaolin whereby the treatment of the metakaolin with chlorine-bearing gas removes iron-bearing impurities not removed from the hydrated clay by flotation and bleaching.

Claim 8

The method of claim 3 wherein metakaolin is the sole source of oxides of aluminum and silicon in the reaction mixture and sodium hydroxide is the sole source of sodium oxide.

Claim 9

The method of claim 3 wherein the reaction mixture is formed by slurrying metakaolin in sodium hydroxide solution of about 10 percent concentration.