Assignee: Nouryon Pulp and Performance Chemicals AB
•
Filing: 1975-05-16
•
Granted: 1977-07-05
•
Expires: 1995-05-16
Abstract
Abstract A method for modifying the physical characteristics of cellulose materials by the impregnation of the cellulose fibers with acidic solutions of monomer and oligomeric silicic acid to form a capillary cellulose-polysilicic acid structure to which selective binder materials may be adhered.
Inventors
- 👤 Olof Sunden
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 11:48
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/63; D21H17/67; D21H17/68; C; C08; C08B; C08B5/00; C08K; C08K3/00; C08K3/18; C08K3/24; C08K3/34; C08K3/36; C08K5/00; C08K5/04; C08K5/07; C08K5/09; C08L; C08L1/00; C08L1/02; C08L33/00; C08L33/04; C08L33/06; C08L33/08; D06; D06M; D06M11/00; D06M11/77; D06M11/79; D21H11/00; D21H11/16; D21H11/20; D21H17/65
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
81 words
A composition comprising cellulose fibers, polysilicic acid, and a binder material, said cellulose fibers and polysilicic acid forming a cellulose polysilicic acid capillary structure having an internal capillarity corresponding to a BET-surface of 200-800 m 2 /g polysilicic acid by absorbing a water based solution of monomer and oligomer silicic acids having a pH of between 1 and 5 into said cellulose fibers and polycondensating said monomer and oligomer silicic acids, and said binder material being adhered to said capillary structure.
Claim 2
Dependent Claim
81 words
A composition comprising cellulose fibers, polysilicic acid, and a binder material, said cellulose fibers and polysilicic acid forming a cellulose polysilicic acid capillary structure having an internal capillarity corresponding to a BET-surface of 200-800 m 2 /g polysilicic acid by absorbing a water based solution of monomer and oligomer silicic acids having a pH of between 1 and 5 into said cellulose fibers and polycondensating said monomer and oligomer silicic acids, and said binder material being adhered to said capillary structure.
Claim 3
Dependent Claim
23 words
The composition of claim 1 in which said solution of monomer and oligomer silicic acids has a pH of between 1.5 and 3.0.
Claim 4
Dependent Claim
29 words
The composition of claim 1 in which the amount of silicic acid incorporated in said cellulose-polysilicic acid structure is equal to 2-100% based on the weight of cellulose fibers.
Claim 5
Dependent Claim
32 words
The composition of claim 3 in which the amount of silicic acid incorporated in said cellulose-polysilicic acid structure is equal to 8-40% as SiO 2 based on the weight of cellulose fibers.
Claim 6
Dependent Claim
38 words
A composition according to claim 1 in which the cellulose fibers are selected from the group consisting of wood cellulose, sulfite cellulose, sulfate-craft cellulose, semi-chemical cellulose, mechanical pulp cellulose, cotton and vegetable cellulose, regenerated cellulose and cellulose esters.
Claim 7
Dependent Claim
31 words
A composition according to claim 1 in which the binder is selected from the group of plastic binders consisting of polyacrylates, polyvinylacetates, polyvinylchlorides and copolymers, polyesters, nylon polymers, and polyacrylonitrile polymers.
Claim 8
Dependent Claim
24 words
A composition according to claim 1 in which the binder is selected from the group of elastomers consisting of styrene-butadiene polymers, polybutadienes, and polychloroprenes.
Claim 9
Dependent Claim
27 words
The composition of claim 1 in which the binder is selected from a group of inorganic hydraulic binders consisting of cement, gypsum, and alkaline silicates and aluminates.
Claim 10
Dependent Claim
61 words
A composition comprising cellulose fibers, polysilicic acid and a buffering acid, said buffering acid having a pK between 2 and 6 and which is decomposable upon drying to form a less acidic residue, and said cellulose fibers and polysilicic acid forming a cellulose-polysilicic acid capillary structure having an internal capillarity corresponding to a BET-surface of 200-800 m 2 /g polysilicic acid.
Claim 11
Dependent Claim
61 words
A composition comprising cellulose fibers, polysilicic acid and a buffering acid, said buffering acid having a pK between 2 and 6 and which is decomposable upon drying to form a less acidic residue, and said cellulose fibers and polysilicic acid forming a cellulose-polysilicic acid capillary structure having an internal capillarity corresponding to a BET-surface of 200-800 m 2 /g polysilicic acid.
Claim 12
Dependent Claim
29 words
The composition of claim 9 in which said buffering acid is selected from the group of acids consisting of complex acids of acidic sulphites and acetones, ketones and aldehydes.
Claim 13
Independent Claim
115 words
The method of manufacturing compositions of cellulose fibers and a binder material comprising the following steps: (a) Impregnating cellulose fibers with a water base solution of monomer and oligomer silicic acids at a pH of 1-5 and having a silicic acid concentration of 3-15% calculated as SiO 2 ; (b) Polycondensating the monomer and oligomer silicic acid absorbed by the cellulose to form a hydrated cellulose-polysilicic acid structure which is insoluble in water; (c) Adding the binder while the cellulose-polysilicic acid structure is hydrated; (d) Drying the composition to form a cellulose-polysilicic acid structure having an internal capillary structure with a BET-surface of 200-800 m 2 /g silicic acid in which the binder is adhered.
Claim 14
Independent Claim
115 words
The method of manufacturing compositions of cellulose fibers and a binder material comprising the following steps: (a) Impregnating cellulose fibers with a water base solution of monomer and oligomer silicic acids at a pH of 1-5 and having a silicic acid concentration of 3-15% calculated as SiO 2 ; (b) Polycondensating the monomer and oligomer silicic acid absorbed by the cellulose to form a hydrated cellulose-polysilicic acid structure which is insoluble in water; (c) Adding the binder while the cellulose-polysilicic acid structure is hydrated; (d) Drying the composition to form a cellulose-polysilicic acid structure having an internal capillary structure with a BET-surface of 200-800 m 2 /g silicic acid in which the binder is adhered.
Claim 15
Dependent Claim
18 words
The method of claim 11 in which said water base silicic acid solution is a pH of 1.5-3.0.
Claim 16
Independent Claim
116 words
The method of manufacturing compositions of cellulose fibers and a binder material comprising the steps of: (a) Impregnating cellulose fibers in the form of cellulose sheets wiith a water base solution of monomer and oligomer silicic acids at a pH of 1-5 and having a silicis acid concentration of 3-15% calculated as SiO 2 ; (b) Adding a buffering acid having a pK value of between 2 and 6 and which is decomposable to a less acidic residue upon drying; (c) Drying the impregnated cellulose sheet to polycondensate the silicic acid monomers and oligomers to form a hydrated cellulose-polysilicic acid capillary structure into which excess monomer and oligomer silicic acid is adhered as a binding material.
Claim 17
Independent Claim
116 words
The method of manufacturing compositions of cellulose fibers and a binder material comprising the steps of: (a) Impregnating cellulose fibers in the form of cellulose sheets wiith a water base solution of monomer and oligomer silicic acids at a pH of 1-5 and having a silicis acid concentration of 3-15% calculated as SiO 2 ; (b) Adding a buffering acid having a pK value of between 2 and 6 and which is decomposable to a less acidic residue upon drying; (c) Drying the impregnated cellulose sheet to polycondensate the silicic acid monomers and oligomers to form a hydrated cellulose-polysilicic acid capillary structure into which excess monomer and oligomer silicic acid is adhered as a binding material.
Claim 18
Dependent Claim
22 words
The method of claim 13 in which acid monomer and oligomer silicic acid solution is at a pH between 1.5 and 3.
Claim 19
Dependent Claim
20 words
The method of claim 13 in which said buffering acid is an acid complex formed by acidic sulfites and acetones.
References Cited (Backward Citations)
US2549563A
Cited
US2703289A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-04 | 1981-01-03 | 1981-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-04 | 1985-01-03 | 1985-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-04 | 1989-01-03 | 1989-07-05 | $7700.00 | Window Closed / Lapsed |