Method of enhancing the refractoriness of high purity fused silica
Assignee: Corning Glass Works
•
Filing: 1976-04-26
•
Granted: 1977-07-05
•
Expires: 1996-04-26
Abstract
Abstract A method is disclosed wherein high purity fused silica is produced from a liquid flowable form of a silica slurry or sol and the refractoriness of the fused silica is enhanced by homogeneously doping the silica with elemental silicon.
Inventors
- 👤 Charles E. Baumgartner
- 👤 Peter P. Bihuniak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:18
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/14; C03; C03B; C03B19/00; C03B19/06; C03B19/066; C03B20/00; C03C; C03C3/00; C03C3/04; C03C3/06; C03B2201/00; C03B2201/06; C03B2201/30; C03B2201/58
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
69 words
In a method of producing a high purity fused silica product, wherein a liquid containing silica is dried to form solid silica bodies which are then thermally vitrified, the improvement, whereby the refractoriness of the fused silica is enhanced, which comprises doping a liquid flowable form of silica slurry or sol with 200 to 2500 parts per million by weight, as based on the fused silica, of elemental silicon.
Claim 2
Dependent Claim
69 words
In a method of producing a high purity fused silica product, wherein a liquid containing silica is dried to form solid silica bodies which are then thermally vitrified, the improvement, whereby the refractoriness of the fused silica is enhanced, which comprises doping a liquid flowable form of silica slurry or sol with 200 to 2500 parts per million by weight, as based on the fused silica, of elemental silicon.
Claim 3
Independent Claim
74 words
A method of producing a high purity fused silica product which comprises the steps of doping a liquid flowable form of silica slurry or sol with 200 to 2500 ppm by weight, as based on the fused silica, of elemental silicon, drying the silicon doped source of silica to rigid silica fragments containing dispersed silicon, calcining the silica fragments at about 1000°-1500° C., and then firing said silica fragments to a fused silica product.
Claim 4
Independent Claim
74 words
A method of producing a high purity fused silica product which comprises the steps of doping a liquid flowable form of silica slurry or sol with 200 to 2500 ppm by weight, as based on the fused silica, of elemental silicon, drying the silicon doped source of silica to rigid silica fragments containing dispersed silicon, calcining the silica fragments at about 1000°-1500° C., and then firing said silica fragments to a fused silica product.
Claim 5
Dependent Claim
38 words
A method in accordance with claim 2 wherein the calcined product is milled to form a slip which is cast in a mold and the product thus formed is fired to a fused silica body of corresponding shape.
Claim 6
Dependent Claim
19 words
A method in accordance with claim 2 wherein the amount of silicon dopant present is less than 1500 ppm.
Claim 7
Independent Claim
61 words
A method of enhancing the refractoriness of a fused silica product which comprises doping a liquid flowable form of silica slurry or sol with 200 to 2500 ppm by weight, as based on the fused silica, of elemental silicon, drying the silicon doped source of silica to form solid silica bodies, and firing said silica bodies to a fused silica product.
Claim 8
Independent Claim
61 words
A method of enhancing the refractoriness of a fused silica product which comprises doping a liquid flowable form of silica slurry or sol with 200 to 2500 ppm by weight, as based on the fused silica, of elemental silicon, drying the silicon doped source of silica to form solid silica bodies, and firing said silica bodies to a fused silica product.
Claim 9
Dependent Claim
20 words
A method in accordance with claim 4 wherein the silicon dopant is present in an amount less than 1500 ppm.
References Cited (Backward Citations)
US3370921A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-04 | 1981-01-03 | 1981-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-04 | 1985-01-03 | 1985-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-04 | 1989-01-03 | 1989-07-05 | $7700.00 | Window Closed / Lapsed |