US4033667A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Multimode optical fiber
Assignee: AT&T Inc
•
Filing: 1975-09-12
•
Granted: 1977-07-05
•
Expires: 1995-09-12
Abstract
Abstract A multimode optical fiber waveguide with graded refractive index for lessening modal dispersion depends upon simultaneous grading of both P 2 O 5 and B 2 O 3 within an otherwise generally unmodified silica glass. P 2 O 5 is at a maximum in the axial core region, while B 2 O 3 is generally the only modifier in the peripheral core region. The defined profile, which depends critically upon P 2 O 5 content in the axial composition and somewhat less critically upon the B 2 O 3 peripheral composition content, is near optimum from the standpoint of mode dispersion and remains so for the entire useful range of carrier wavelength (generally defined as from 0.5 to 1.1 μm). Numerical aperture for fibers of the invention are typically at a level of 0.3.
Inventors
- 👤 James William Fleming, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:52
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/028; G02B6/0288; C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018; C03B37/01807; C03C; C03C13/00; C03C13/04; C03C13/045; C03C13/046; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/10; C03B2201/20; C03B2201/28; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/26; G02B6/02214; G02B6/02285; G02B6/036; G02B6/03616; G02B6/03622; G02B6/03627
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
221 words
Glass transmission line for the transmission of electromagnetic radiation centering about a wavelength within the range of from 0.5 to 2.0 μm, said line comprising a core member manifesting a radially decreasing refractive index for said radiation from the axial core composition to the peripheral core composition, together with a cladding about said core, in which the said core consists essentially of SiO 2 and at least two refractive index modifying ingredients, in which the gradient within the said core is due at least in part to a radially increasing concentration of boron oxide, B 2 O 3 , to an ultimate peripheral core composition which is essentially borosilicate containing from 10 mole percent B 2 O 3 to 20 mole percent B 2 O 3 , the said gradient approximating the form: ##EQU9## in which the n 1 is the index maximum, r is the distance from the fiber axis, a is the core radius, Δ is the relative index difference between core center and cladding and α is a power law exponent which characterizes the profile, characterized in that the said gradient is due, at least in part, to a radially decreasing concentration of phosphorous pentoxide, P 2 O 5 , from an axial core composition containing from 10 mole percent P 2 O 5 to 15 mole percent.
Claim 2
Dependent Claim
221 words
Glass transmission line for the transmission of electromagnetic radiation centering about a wavelength within the range of from 0.5 to 2.0 μm, said line comprising a core member manifesting a radially decreasing refractive index for said radiation from the axial core composition to the peripheral core composition, together with a cladding about said core, in which the said core consists essentially of SiO 2 and at least two refractive index modifying ingredients, in which the gradient within the said core is due at least in part to a radially increasing concentration of boron oxide, B 2 O 3 , to an ultimate peripheral core composition which is essentially borosilicate containing from 10 mole percent B 2 O 3 to 20 mole percent B 2 O 3 , the said gradient approximating the form: ##EQU9## in which the n 1 is the index maximum, r is the distance from the fiber axis, a is the core radius, Δ is the relative index difference between core center and cladding and α is a power law exponent which characterizes the profile, characterized in that the said gradient is due, at least in part, to a radially decreasing concentration of phosphorous pentoxide, P 2 O 5 , from an axial core composition containing from 10 mole percent P 2 O 5 to 15 mole percent.
Claim 3
Dependent Claim
27 words
Line of claim 1 in which the axial core composition consists essentially of phosphosilicate glass and in which the peripheral core composition consists essentially of borosilicate glass.
Claim 4
Dependent Claim
49 words
Line of claim 2 in which Δ in the equation set forth in claim 1 is equal to ##EQU10## n 1 and n 2 are index values as measured in bulk samples of glass of the compositions represented, respectively, by the axial core composition and the peripheral core composition.
Claim 5
Dependent Claim
39 words
Line of claim 1 in which α, the exponent in the equation set forth in claim 1, is equal to approximately 1.9 and in which the electromagnetic radiation centers about a wavelength range of from 0.5 to 1.1 μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-04 | 1981-01-03 | 1981-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-04 | 1985-01-03 | 1985-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-04 | 1989-01-03 | 1989-07-05 | $7700.00 | Window Closed / Lapsed |