Method for producing coated electrical steel sheets having excellent punchability, weldability, electrical insulation and heat resistance
Assignee: JFE Steel Corp
•
Filing: 1975-10-14
•
Granted: 1977-06-28
•
Expires: 1995-10-14
Abstract
Abstract Coated electrical steel sheets having excellent punchability, weldability and insulation resistance are produced by applying an electrical steel sheet with a treating dispersion obtained by compounding the particle separating resin emulsion and the compatible resin to an aqueous solution containing chromic acid in the particularly defined amount and baking the thus applied steel sheets. To the treating dispersion may be added saccharides or polyhydric alcohols as a reducing agent or boric acid or phosphoric acid.
Inventors
- 👤 Toshio Irie
- 👤 Toshikuni Tanda
- 👤 Tomoyuki Ichi
- 👤 Toshio Sadayori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:02
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/08; C09D5/12; C23; C23C; C23C22/00; C23C22/73; C23C22/74; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/14766; H01F1/14775; H01F1/14783
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
161 words
A method for producing coated electrical steel sheets having excellent punchability, weldability and insulation characteristics comprising applying on an electrical steel sheet, a treating dispersion obtained by compounding: (a) a resin emulsion which separates agglomerated particles having an average particle diameter of 3-40 microns when compounded in an aqueous solution containing chromic acid; (b) a resin compatible with an aqueous solution containing chromic acid; and (c) an aqueous solution containing chromic acid so that the total amount of non volatile matter of both the resins is 5-150 parts by weight per one hundred parts of chromic acid by weight expressed as CrO 3 with the amount of the resin emulsion being at least one part by weight of the total weight amount of the resin and resin emulsion and said resin emulsion provides at least 5% by weight of the total amount of the non volatile matter of the resin and the resin emulsion; and baking the thus treated steel sheets.
Claim 2
Independent Claim
161 words
A method for producing coated electrical steel sheets having excellent punchability, weldability and insulation characteristics comprising applying on an electrical steel sheet, a treating dispersion obtained by compounding: (a) a resin emulsion which separates agglomerated particles having an average particle diameter of 3-40 microns when compounded in an aqueous solution containing chromic acid; (b) a resin compatible with an aqueous solution containing chromic acid; and (c) an aqueous solution containing chromic acid so that the total amount of non volatile matter of both the resins is 5-150 parts by weight per one hundred parts of chromic acid by weight expressed as CrO 3 with the amount of the resin emulsion being at least one part by weight of the total weight amount of the resin and resin emulsion and said resin emulsion provides at least 5% by weight of the total amount of the non volatile matter of the resin and the resin emulsion; and baking the thus treated steel sheets.
Claim 3
Dependent Claim
45 words
The method as claimed in claim 1 in which the treating dispersion includes 10-60 parts by weight based upon one hundred parts by weight of chromic acid of at least one member of the group consisting of polyhydric alcohols and saccharides as a reducing agent.
Claim 4
Dependent Claim
40 words
The method as claimed in claim 1 wherein said particle separating resin is added in an amount such that the non volatile matter of said resin is 1-30 parts by weight per one hundred parts by weight of chromic acid.
Claim 5
Dependent Claim
38 words
The method as claimed in claim 1 wherein said compatible resin is added in an amount such that non volatile matter of said resin is 5-120 parts by weight per one hundred parts by weight of chromic acid.
Claim 6
Dependent Claim
40 words
The method as claimed in claim 1 wherein the particle separating resin is added in the amount of 5-15 parts by weight and the compatible resin at 10-50 parts by weight per one hundred parts by weight of chromic acid.
Claim 7
Dependent Claim
24 words
The method as claimed in claim 1 wherein at least one member of the group consisting of boric acid and phosphoric acid is added.
Claim 8
Dependent Claim
14 words
The method as claimed in claim 1 wherein the baking temperature is 300°-700° C.
Claim 9
Dependent Claim
68 words
The method as claimed in claim 1, wherein the particle separating resin is an acrylic resin emulsion obtained by copolymerizing 5-13 parts by weight of α,β-ethylenically unsaturated carboxylic acid and 95-87 parts by weight of α,β-ethylenical monomer together with at least one of emulsifiers added with 0.8-5.5 parts by weight based on 100 parts by weight of the nonvolatile matter in the emulsion, of a water soluble amine.
Claim 10
Dependent Claim
63 words
The method as claimed in claim 1, wherein the compatible resin is an acrylic resin containing less than 5 parts by weight based on 100 parts by weight of the total monomers of α,β-ethylenically unsaturated carboxylic acid and less than 0.5 part by weight based on 100 parts by weight of the non volatile matter in the emulsion, of a water soluble amine.
Claim 11
Dependent Claim
30 words
The method as claimed in claim 1 wherein the chromate salt is selected from at least one member of the group consisting of calcium, magnesium, zinc and aluminum chromate salts.
Claim 12
Dependent Claim
35 words
The method as claimed in claim 1, wherein a concentration of the non volatile matter of the particle separating resin emulsion, when said emulsion is added to an aqueous solution containing chromic acid, is 5-60%.
Claim 13
Dependent Claim
19 words
The method as claimed in claim 1, wherein the aqueous solution containing chromic acid contains free CrO 3 .
Claim 14
Dependent Claim
20 words
The method as claimed in claim 1 wherein the weight of the coating is 1.2-4.8 g/m 2 per one side.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-27 | 1980-12-27 | 1981-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-27 | 1984-12-27 | 1985-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-27 | 1988-12-27 | 1989-06-28 | $7700.00 | Window Closed / Lapsed |