Mix suitable for use in seams between carbon blocks
Assignee: Alcoa Corp
•
Filing: 1976-01-19
•
Granted: 1977-06-28
•
Expires: 1996-01-19
Abstract
Abstract A mix suitable for use as seam mix in an electrolytic cell for producing aluminum, of the type which has conventionally consisted essentially of carbon aggregate and binder and which has been heated for the purpose of obtaining sufficient workability to enable a tamping operation to produce liquid-tight and electrically conductive seams, wherein the improvement includes the presence of a solvent having a boiling point of from 150° to 350° C and consisting essentially of at least one compound selected from the group consisting of aromatic hydrocarbons having only saturated side chains, the solvent being present in an amount sufficient to render the mix capable of being tamped without the application of heat.
Inventors
- 👤 M. Benjamin Dell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:16
CPC Classifications
C; C25; C25C; C25C3/00; C25C3/06; C25C3/08; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/528; C04B35/532
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
108 words
A method of using a mix consisting essentially of calcined carbon aggregate, binder in the form of coal tar pitch or petroleum pitch, and only solvents having boiling points of from 150° to 350° C., said solvents consisting essentially of at least one compound selected from the group consisting of aromatic hydrocarbons having only saturated side chains, the solvent being present in an amount sufficient to render the mix capable of being tamped while the mix is at room temperature, said method comprising tamping the mix into the bottom of an electrolytic cell while the mix is at room temperature, and then bringing the cell to operating temperature.
Claim 2
Independent Claim
108 words
A method of using a mix consisting essentially of calcined carbon aggregate, binder in the form of coal tar pitch or petroleum pitch, and only solvents having boiling points of from 150° to 350° C., said solvents consisting essentially of at least one compound selected from the group consisting of aromatic hydrocarbons having only saturated side chains, the solvent being present in an amount sufficient to render the mix capable of being tamped while the mix is at room temperature, said method comprising tamping the mix into the bottom of an electrolytic cell while the mix is at room temperature, and then bringing the cell to operating temperature.
Claim 3
Dependent Claim
20 words
A method as claimed in claim 1, wherein the solvent has a boiling point of from 200° to 300° C.
Claim 4
Dependent Claim
15 words
A method as claimed in claim 1, wherein the solvent is crude methyl naphthalene solvent.
Claim 5
Independent Claim
99 words
A method of using a mix consisting essentially of (1) 7 to 17 weight-percent binder in the form of coal tar pitch or petroleum pitch of softening point of 48° to 54° C. and calcined carbon aggregate at a weight-percent of quantity 100 minus the weight-percent of binder, and (2) crude methyl naphthalene solvent at 8 to 16% of the weight of the binder, said method comprising tamping the mix into seams between carbon blocks in the bottom of an electrolytic cell while the cell and mix are at room temperature, and then bringing the cell to operating temperature.
Claim 6
Independent Claim
99 words
A method of using a mix consisting essentially of (1) 7 to 17 weight-percent binder in the form of coal tar pitch or petroleum pitch of softening point of 48° to 54° C. and calcined carbon aggregate at a weight-percent of quantity 100 minus the weight-percent of binder, and (2) crude methyl naphthalene solvent at 8 to 16% of the weight of the binder, said method comprising tamping the mix into seams between carbon blocks in the bottom of an electrolytic cell while the cell and mix are at room temperature, and then bringing the cell to operating temperature.
Claim 7
Dependent Claim
22 words
A method as claimed in claim 4, wherein the solvent is present at 10 to 14% of the weight of the binder.
Claim 8
Dependent Claim
89 words
A method as claimed in claim 4, wherein the binder is pitch having a softening point of 50° C. and being present at 12 weight-percent, as based on the weight of the pitch plus aggregate, the aggregate is calcined anthracite and is present at 88 weight-percent, as based on the weight of the pitch plus aggregate, and the solvent is present at 10% of the weight of the pitch and consists essentially of, on a weight-percent basis, 12% naphthalene, 55% alpha and beta methyl naphthalene, and 33% dimethyl naphthalene.
Claim 9
Dependent Claim
25 words
A method as claimed in claim 1, said cell being a cell for producing aluminum metal by the electrolysis of Al 2 O 3 .
Claim 10
Dependent Claim
25 words
A method as claimed in claim 4, said cell being a cell for producing aluminum metal by the electrolysis of Al 2 O 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-27 | 1980-12-27 | 1981-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-27 | 1984-12-27 | 1985-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-27 | 1988-12-27 | 1989-06-28 | $7700.00 | Window Closed / Lapsed |