Method for preparation of polyolefin oil
Assignee: Lion Corp
•
Filing: 1976-07-22
•
Granted: 1977-06-21
•
Expires: 1996-07-22
Abstract
Abstract A method of preparing a polyolefin oil in the present invention comprises polymerizing an olefin having 6 or more carbon atoms in the presence of a catalyst mixture consisting of a polyester of polycarboxylic acid and an aluminum halide. The thus prepared polyolefin oil has a low viscosity and a high viscosity index. When the foregoing polymerization is effected by adding aluminum powder to said catalyst mixture, the content of halogen in the resulting polyolefin oil can be decreased all the more.
Inventors
- 👤 Hiroshi Mandai
- 👤 Toshiyuki Ukigai
- 👤 Anri Tominaga
- 👤 Michito Sato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:07
CPC Classifications
C; C08; C08F; C08F10/00; C08F10/14
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
75 words
A method of preparing a polyolefin oil comprising polymerizing an olefin having 6 or more carbon atoms at a temperature in the range of from 50° to 150° C in the presence of a catalyst mixture consisting of a polyester and an aluminum halide, said polyester being obtained by esterifying all the carboxyl groups of a polycarboxylic acid having 2 to 20 carbon atoms with an aliphatic saturated alcohol having 1 to 20 carbon atoms.
Claim 2
Independent Claim
75 words
A method of preparing a polyolefin oil comprising polymerizing an olefin having 6 or more carbon atoms at a temperature in the range of from 50° to 150° C in the presence of a catalyst mixture consisting of a polyester and an aluminum halide, said polyester being obtained by esterifying all the carboxyl groups of a polycarboxylic acid having 2 to 20 carbon atoms with an aliphatic saturated alcohol having 1 to 20 carbon atoms.
Claim 3
Dependent Claim
51 words
A method according to claim 1, wherein the amount of aluminum halide to be contained in said catalyst mixture is in the range of from 0.7 to 2.0 moles per 1 ester bond of said polyester and in the range of from 0.5 to 12 mol. % based on said olefin.
Claim 4
Dependent Claim
15 words
A method according to claim 1, wherein said catalyst mixture further contains metallic aluminum powder.
Claim 5
Dependent Claim
31 words
A method according to claim 3, wherein the amount of said metallic aluminum powder is in the range of from 2.7 to 135 g per 1 mole of said aluminum halide.
Claim 6
Dependent Claim
37 words
A method according to claim 1, wherein said polyester is selected from the group consisting of diethyl malonate, dipropyl malonate, dioctyl malonate, diethyl succinate, dibutyl succinate, dioctyl succinate, diethyl glutarate, diethyl adipate, diethyl pimelate, and diethyl suberate.
Claim 7
Dependent Claim
13 words
A method according to claim 1, wherein said aluminum halide is aluminum chloride.
Claim 8
Dependent Claim
32 words
A method according to claim 1, wherein a catalyst mixture is prepared by adding said aluminum halide to said polyester and then said olefin is added to the thus prepared catalyst mixture.
Claim 9
Dependent Claim
39 words
A method according to claim 1, wherein said polymerization is effected in a solvent selected from the group consisting of n-pentane, iso-octane, trichloroethane and tetrafluoroethane in an amount ranging from 25 to 100% by volume, based on the olefin.
References Cited (Backward Citations)
US3833678A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-20 | 1980-12-20 | 1981-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-20 | 1984-12-20 | 1985-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-20 | 1988-12-20 | 1989-06-21 | $7700.00 | Window Closed / Lapsed |