Cloth comprising asbestos fibers and method of producing said cloth
Assignee: Rhone Poulenc Industries SA
•
Filing: 1975-07-31
•
Granted: 1977-06-21
•
Expires: 1995-07-31
Abstract
Abstract A novel cloth comprising asbestos fibers, particularly in the form of a micro-porous membrane is provided and a method of obtaining this cloth. It is characterized in that said cloth is obtained by the dry mixing of asbestos fibers and at least one filler or charge substance, then working up by malaxation in the presence of a latex, forming the cloth and, optionally, elimination of the filler substance. The invention is particularly applicable in the production of a micro-porous membrane for use in electrolysis diaphragms.
Inventors
- 👤 Pierre Bouy
- 👤 Michel Juillard
- 👤 Jean-Luc Bourgeois
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 08:20
CPC Classifications
C; C25; C25B; C25B13/00; C25B13/04; C25B13/05; C25B13/06; C25B13/08; Y; Y10; Y10S; Y10S264/00; Y10S264/17; Y10T; Y10T428/00; Y10T428/31504; Y10T428/3154; Y10T428/31544
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
79 words
A method of obtaining a sheet comprising asbestos fibers and a fluorocarbon polymeric resin, which process comprises, in a first stage asbestos fibers and at least one solid particulate mineral filler substance are mixed at substantially high speed of at least about 800 R.P.M. in the dry state, in a second stage at least one fluorocarbon polymeric resin latex is added and mixed with the resulting dry mixture, and finally a sheet is then formed from the resulting mixture.
Claim 2
Independent Claim
79 words
A method of obtaining a sheet comprising asbestos fibers and a fluorocarbon polymeric resin, which process comprises, in a first stage asbestos fibers and at least one solid particulate mineral filler substance are mixed at substantially high speed of at least about 800 R.P.M. in the dry state, in a second stage at least one fluorocarbon polymeric resin latex is added and mixed with the resulting dry mixture, and finally a sheet is then formed from the resulting mixture.
Claim 3
Dependent Claim
44 words
A method according to claim 1, wherein a plasticizing agent is added in said second stage to the resulting dry mixture to slow malaxation, in a third stage, shaping the resulting mass into a sheet by rolling between at least one pair of rolls.
Claim 4
Dependent Claim
12 words
A method according to claim 2, wherein the resulting sheet is sintered.
Claim 5
Dependent Claim
145 words
A method according to claim 1, wherein said first stage mixing is carried out by means of a mixer having a high-speed screw, and said first stage mixing continuing during a period of between about 5 and 30 minutes, in a second stage a fluorocarbon polymeric resin latex and a plasticizing agent are added to the dry mixture thus produced by subjecting the entire mixture to malaxation by means of a low speed malaxator, the speed of revolution of the rotor of which is at most 100 r.p.m., malaxation continuing for a period of between 1 and 15 min., in a third stage shaping the mass into a sheet by rolling between at least two pair of rolls, the sheet then being dried, and in a fourth stage the sheet thus obtained is sintered at a temperature above the fusion-point of said fluorocarbon polymeric resin.
Claim 6
Dependent Claim
27 words
A method of obtaining a sheet comprising asbestos fibers according to claim 2, wherein rolling is carried out at a temperature of between 30° and 80° C.
Claim 7
Dependent Claim
27 words
A method according to claim 2, wherein rolling is carried out by passing the mixture between at least one pair of rolls driven at the same speed.
Claim 8
Dependent Claim
26 words
A method according to claim 2, wherein rolling is carried out by passing the mixture between at least one pair of rolls driven at different speeds.
Claim 9
Dependent Claim
55 words
A method according to claim 1, wherein the mixture contains, for each part of asbestos, 10 to 100 parts by weight of at least one particulate filler substance, 1 to 100 parts by weight of polymeric resin latex, 0.5 to 2 parts by weight of a plasticizing agent and 1 to 20 parts of water.
Claim 10
Dependent Claim
24 words
A method according to claim 1, wherein at least one particulate mineral filler substance is calcium carbonate and that the latex is of polytetrafluoroethylene.
Claim 11
Dependent Claim
41 words
A method of obtaining a micro-porous membrane according to claim 1, wherein at least one of the mineral filler substances introduced during the first stage is a pore-forming agent, and in that the pore-forming agent is removed at a later stage.
Claim 12
Dependent Claim
35 words
A method of obtaining a micro-porous membrane according to claim 10, wherein the pore-forming agent is constituted by calcium carbonate, and in that this pore-forming agent is eliminated by immersion in an aqueous acid solution.
Claim 13
Dependent Claim
20 words
A method according to claim 11, wherein the aqueous acid solution is a 10 to 25% solution of acetic acid.
Claim 14
Dependent Claim
15 words
A method according to claim 10, wherein the resulting membrane is degassed at reduced pressure.
Claim 15
Dependent Claim
21 words
A method according to claim 1, wherein the asbestos used is composed of fibers of 0.5 to 50 millimeters in length.
Claim 16
Dependent Claim
26 words
A method according to claim 10, wherein the pore-former used is a member selected from the class consisting of calcium carbonate, colloidal alumina and metallic oxides.
Claim 17
Dependent Claim
16 words
A novel sheet comprising asbestos fibers, wherein it is obtained by the method of claim 1.
Claim 18
Dependent Claim
78 words
A novel sheet according to claim 16, wherein it comprises, for each part of asbestos, 10 to 100 parts of at least one particulate filler substance, 1 to 100 parts of at least one fluorocarbon polymeric resin latex, 0.5 to 2 parts of a plasticizing agent and 1 to 20 parts of water, the ratio of the weight of the particulate filler substance to the combined weights of the latex and the asbestos being between 1:1 and 25:1.
Claim 19
Dependent Claim
31 words
A novel sheet according to claim 16, wherein it has an elongation of between about 1 and 200%, and a rupture strength of between about 5 and 50 kg/cm 2 .
Claim 20
Dependent Claim
14 words
A novel microporous sheet wherein it is obtained by the method of claim 10.
Claim 21
Dependent Claim
29 words
A novel micro-porous sheet according to claim 16, wherein it has a relative resistance of between about 1.5 and 10, and a micro-porosity of between about 50 and 90%.
Claim 22
Dependent Claim
17 words
A novel diaphragm for electrolysis cells, wherein it is constituted by a sheet according to claim 19.
References Cited (Backward Citations)
US2775569A
Cited
US2891921A
Cited
US3314916A
Cited
US3477865A
Cited
US3793287A
Cited
US3682859A
Cited
GB1410313A
Cited
US3930979A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-20 | 1980-12-20 | 1981-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-20 | 1984-12-20 | 1985-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-20 | 1988-12-20 | 1989-06-21 | $7700.00 | Window Closed / Lapsed |