Process for cube-on-edge oriented boron-bearing silicon steel including normalizing
Assignee: Allegheny Ludlum Corp
•
Filing: 1976-06-17
•
Granted: 1977-06-21
•
Expires: 1996-06-17
Abstract
Abstract A process for producing electromagnetic silicon steel having a cube-on-edge orientation and a permeability of at least 1870 (G/Oe) at 10 oersteds. The process includes the steps of: preparing a melt of silicon steel containing from 0.02 to 0.06% carbon, from 0.0006 to 0.0080% boron, up to 0.0100% nitrogen, no more than 0.008% aluminum and from 2.5 to 4.0% silicon; casting said steel; hot rolling said steel; cold rolling said steel; normalizing said steel at a temperature of from 1300 DEG to 2000 DEG F in a hydrogen-bearing atmosphere having a dew point of from +20 DEG to +110 DEG F; applying a refractory oxide base coating to said steel; and final texture annealing said steel. The variables of time, temperature and dew point are monitored during normalizing so as to result in a steel having at least 320 parts per million of oxygen, based on the total weight of the steel, within 10 microns of the surfaces of said steel.
Inventors
- 👤 Jack W. Shilling
- 👤 Amitava Datta
- 👤 Frank A. Malagari, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:37
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/14766; H01F1/14775; H01F1/14783; C; C21; C21D; C21D8/00; C21D8/12; C21D8/1244; C21D8/1255
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
195 words
In a process for producing electromagnetic silicon steel having a cube-on-edge orientation and a permeability of at least 1870 (G/O e ) at 10 oersteds, which process includes the steps of: preparing a melt of silicon steel containing from 0.02 to 0.06% carbon, from 0.0006 to 0.0080% boron, up to 0.0100% nitrogen, no more than 0.008% aluminum and from 2.5 to 4.0% silicon; casting said steel; hot rolling said steel; cold rolling said steel; decarburizing said steel, applying a refractory oxide base coating to said steel; and final texture annealing said steel; the improvement comprising the steps of normalizing said cold roller steel at a temperature of from 1300 to 2000° F in a hydrogen-bearing atmosphere having a dew point of from +20 to +110° F for a period of time sufficient to lower said steel's carbon content to a level below 0.005%, said temperature, dew point and time being monitored so as to result in a steel having at least 320 parts per million of oxygen, based on the total weight of the steel, within 10 microns of the surfaces of said steel; and forming an opaque refractory oxide base coating on said steel.
Claim 2
Dependent Claim
195 words
In a process for producing electromagnetic silicon steel having a cube-on-edge orientation and a permeability of at least 1870 (G/O e ) at 10 oersteds, which process includes the steps of: preparing a melt of silicon steel containing from 0.02 to 0.06% carbon, from 0.0006 to 0.0080% boron, up to 0.0100% nitrogen, no more than 0.008% aluminum and from 2.5 to 4.0% silicon; casting said steel; hot rolling said steel; cold rolling said steel; decarburizing said steel, applying a refractory oxide base coating to said steel; and final texture annealing said steel; the improvement comprising the steps of normalizing said cold roller steel at a temperature of from 1300 to 2000° F in a hydrogen-bearing atmosphere having a dew point of from +20 to +110° F for a period of time sufficient to lower said steel's carbon content to a level below 0.005%, said temperature, dew point and time being monitored so as to result in a steel having at least 320 parts per million of oxygen, based on the total weight of the steel, within 10 microns of the surfaces of said steel; and forming an opaque refractory oxide base coating on said steel.
Claim 3
Dependent Claim
14 words
The improvement according to claim 1, wherein said melt has at least 0.0008% boron.
Claim 4
Dependent Claim
20 words
The improvement according to claim 2, wherein said steel is normalized at a temperature of from 1400° to 1500° F.
Claim 5
Dependent Claim
25 words
The improvement according to claim 2, wherein said steel is normalized in a hydrogen-bearing atmosphere having a dew point of from +40° to +85° F.
Claim 6
Dependent Claim
21 words
The improvement according to claim 2, wherein said steel is normalized for a period of from ten seconds to ten minutes.
Claim 7
Dependent Claim
16 words
The improvement according to claim 2, wherein said hydrogen-bearing atmosphere consists essentially of hydrogen and nitrogen.
Claim 8
Dependent Claim
16 words
The improvement according to claim 4, wherein said hydrogen-bearing atmosphere consists essentially of hydrogen and nitrogen.
Claim 9
Dependent Claim
16 words
The improvement according to claim 2, wherein said refractory oxide coating contains at least 50% MgO.
Claim 10
Dependent Claim
46 words
The improvement according to claim 2, wherein said hot rolled steel has a thickness of from 0.050 to 0.120 inch and wherein said hot rolled steel is cold rolled to a thickness of no more than 0.020 inch without an intermediate anneal between cold rolling passes.
Claim 11
Dependent Claim
58 words
The improvement according to claim 1, wherein said melt consists essentially of, by weight, 0.02 to 0.06% carbon, 0.015 to 0.15% manganese, 0.01 to 0.05% of material from the group consisting of sulfur and selenium, 0.0006 to 0.0080% boron, up to 0.0100% nitrogen, 2.5 to 4.0% silicon, up to 1.0% copper, no more than 0.008% aluminum, balance iron.
Claim 12
Dependent Claim
14 words
The improvement according to claim 10, wherein said melt has at least 0.0008% boron.
Claim 13
Dependent Claim
28 words
A cube-on-edge oriented silicon steel having a permeability of at least 1870 (G/O e ) at 10 oersteds, and made in accordance with the process of claim 2.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-20 | 1980-12-20 | 1981-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-20 | 1984-12-20 | 1985-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-20 | 1988-12-20 | 1989-06-21 | $7700.00 | Window Closed / Lapsed |