Method of manufacturing insulated electric power cables
Assignee: Fujikura Cable Works Ltd
•
Filing: 1975-05-01
•
Granted: 1977-06-14
•
Expires: 1995-05-01
Abstract
Abstract Insulated electric power cables comprising a cured insulating material applied over a conductor and a layer of plastic compound comprising 100 parts by weight of a thermoplastic resin and 5-70 parts by weight of calcium oxide as a moisture-absorbing agent, overlying the insulating material and, optionally, lying between the conductor and the insulating material. The presence of calcium oxide serves to absorb steam before it penetrates into the insulating material through the layer of plastic compound being cured by steam, whereby the cured insulating material is free of microvoids and possess good insulation characteristics.
Inventors
- 👤 Shuji Yamamoto
- 👤 Setsuya Isshiki
- 👤 Mitsuru Igarashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 06:57
CPC Classifications
H; H01; H01B; H01B7/00; H01B7/02; H01B7/0275; H01B9/00; H01B9/02; H01B9/027; Y; Y02; Y02A; Y02A30/00; Y02A30/14; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
117 words
A method of manufacturing an insulated electric power cable comprising the steps of applying a curable polyethylene material on an electric conductor to form a polyethylene insulation layer, providing over said insulation layer, a layer of a plastic compound comprising 100 parts by weight of a thermoplastic resin and from 5 to 70 parts by weight of calcium oxide having an average diameter ≦50 μm and curing both the insulation layer and said layer of plastic compound at the same time with steam under a pressure of 1.5- 20 kg/cm 2 , said thermoplastic resin being selected from the group consisting of saturated or unsaturated olefin polymers and ethylene-vinyl acetate copolymers with or without vinyl chloride grafting.
Claim 2
Independent Claim
117 words
A method of manufacturing an insulated electric power cable comprising the steps of applying a curable polyethylene material on an electric conductor to form a polyethylene insulation layer, providing over said insulation layer, a layer of a plastic compound comprising 100 parts by weight of a thermoplastic resin and from 5 to 70 parts by weight of calcium oxide having an average diameter ≦50 μm and curing both the insulation layer and said layer of plastic compound at the same time with steam under a pressure of 1.5- 20 kg/cm 2 , said thermoplastic resin being selected from the group consisting of saturated or unsaturated olefin polymers and ethylene-vinyl acetate copolymers with or without vinyl chloride grafting.
Claim 3
Independent Claim
137 words
A method of manufacturing an insulated electric power cable comprising the steps of applying a curable polyethylene material on an electric conductor to form a polyethylene insulation layer, providing over said insulation layer, a layer of a plastic compound comprising 100 parts by weight of a thermoplastic resin composition containing 100 parts by weight of a thermoplastic resin, from 40 to 80 parts by weight of carbon black resin and from 5 to 70 parts by weight of calcium oxide having an average diameter ≦50 μm and curing both said insulation layer and said layer of plastic compound at the same time with steam under a pressure of 1.5-20 Kg/cm 2 , said thermoplastic resin being selected from the group consisting of saturated and unsaturated olefin polymers and ethylene-vinyl acetate copolymers with or without vinyl chloride grafting.
Claim 4
Independent Claim
137 words
A method of manufacturing an insulated electric power cable comprising the steps of applying a curable polyethylene material on an electric conductor to form a polyethylene insulation layer, providing over said insulation layer, a layer of a plastic compound comprising 100 parts by weight of a thermoplastic resin composition containing 100 parts by weight of a thermoplastic resin, from 40 to 80 parts by weight of carbon black resin and from 5 to 70 parts by weight of calcium oxide having an average diameter ≦50 μm and curing both said insulation layer and said layer of plastic compound at the same time with steam under a pressure of 1.5-20 Kg/cm 2 , said thermoplastic resin being selected from the group consisting of saturated and unsaturated olefin polymers and ethylene-vinyl acetate copolymers with or without vinyl chloride grafting.
Claim 5
Dependent Claim
33 words
The method as claimed in claim 1 wherein said plastic compound additionally contains a curing agent in an amount not exceeding half the amount of said curing agent in said curable polyethylene material.
Claim 6
Dependent Claim
35 words
The method as claimed in claim 2 wherein said semiconductive thermoplastic resin composition additionally contains a curing agent in an amount not exceeding half the amount of said curing agent in said curable polyethylene material.
Claim 7
Dependent Claim
17 words
The method as claimed in claim 1 wherein said steam is used in combination with ultrasonic radiation.
Claim 8
Dependent Claim
18 words
The method as claimed in claim 1 wherein said steam is used in combination with an ultrasonic radiation.
Claim 9
Dependent Claim
23 words
The method as claimed in claim 1 wherein said steam is used under a pressure of from 12 to 15 kg/cm 2 .
Claim 10
Dependent Claim
23 words
The method as claimed in claim 2 wherein said steam is used under a pressure of from 2 to 15 kg/cm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-13 | 1980-12-13 | 1981-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-13 | 1984-12-13 | 1985-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-13 | 1988-12-13 | 1989-06-14 | $7700.00 | Window Closed / Lapsed |