Method for preparing a photoconductive powder
Assignee: Panasonic Holdings Corp
•
Filing: 1975-08-27
•
Granted: 1977-06-14
•
Expires: 1995-08-27
Abstract
Abstract This invention provides a method for preparing a photoconductive powder comprising firing a combined starting mixture of CdSe, ZnS, ZnO, a Cu or Ag salt, and a Cd or Zn chloride or bromide as a flux, and preferably a Mn salt also, at a temperature higher than the melting point of the flux, cooling the fired product, and re-firing the cooled product in a sulfur vapor containing atmosphere. The photoconductive powder obtained by this method has high photosensitivity, high threshold voltage and fine particle size.
Inventors
- 👤 Yoshio Enoki
- 👤 Nobumasa Ohshima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 00:22
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/02; G03G5/04; G03G5/08
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
200 words
A method for preparing a photoconductive powder comprising: providing a starting mixture comprising (i) a host material consisting essentially of 65 to 95% by weight of CdSe powder, 3 to 15% by weight of ZnS powder and 2 to 20% by weight of ZnO powder, (ii) as an activator, 0.005 to 0.1 parts by weight, on the basis of 100 parts by weight of said host material, of a water soluble salt of one member selected from the group consisting of Cu and Ag and (iii) as a flux, 0.1 to 1 part by weight, on the basis of 100 parts by weight of said host material, of one member selected from the group consisting of CdCl 2 , CdBr 2 , ZnCl 2 and ZnBr 2 ; firing said starting mixture at a temperature higher than the melting point of said flux to fuse said flux and dissolve said host material in said flux; cooling the thus fired mixture to recrystallize said host material at least partially to a solid solution, the thus treated material having said activator diffused therein; and re-firing the thus treated material in a sulfur containing atmosphere to increase the threshold voltage of the material.
Claim 2
Independent Claim
200 words
A method for preparing a photoconductive powder comprising: providing a starting mixture comprising (i) a host material consisting essentially of 65 to 95% by weight of CdSe powder, 3 to 15% by weight of ZnS powder and 2 to 20% by weight of ZnO powder, (ii) as an activator, 0.005 to 0.1 parts by weight, on the basis of 100 parts by weight of said host material, of a water soluble salt of one member selected from the group consisting of Cu and Ag and (iii) as a flux, 0.1 to 1 part by weight, on the basis of 100 parts by weight of said host material, of one member selected from the group consisting of CdCl 2 , CdBr 2 , ZnCl 2 and ZnBr 2 ; firing said starting mixture at a temperature higher than the melting point of said flux to fuse said flux and dissolve said host material in said flux; cooling the thus fired mixture to recrystallize said host material at least partially to a solid solution, the thus treated material having said activator diffused therein; and re-firing the thus treated material in a sulfur containing atmosphere to increase the threshold voltage of the material.
Claim 3
Dependent Claim
32 words
A method for preparing a photoconductive powder according to claim 1, wherein the first firing step is performed at a temperature between 500 and 700° C for 15 minutes to 2 hours.
Claim 4
Dependent Claim
31 words
A method for preparing a photoconductive powder according to claim 1, wherein said re-firing step is performed at a temperature between 440° and 500° C for 15 minutes to 2 hours.
Claim 5
Dependent Claim
39 words
A method for preparing a photoconductive powder according to claim 1, wherein said CdSe powder has an average particle size less than 5 microns, and said ZnS and ZnO powders have an average particle size less than 1 micron.
Claim 6
Dependent Claim
37 words
A method for preparing a photoconductive powder according to claim 1, wherein said activator is one member selected from the group consisting of CuCl 2 , CuSO 4 , Cu(NO 3 ) 2 and AgNO 3 .
Claim 7
Dependent Claim
49 words
A method for preparing a photoconductive powder according to claim 1, wherein said starting mixture further comprises 0.1 to 5 parts by weight, on the basis of 100 parts of said host material of one member selected from the group consisting of NH 4 Cl and NH 4 Br.
Claim 8
Dependent Claim
50 words
A method for preparing a photoconductive powder according to claim 1, wherein said starting mixture further includes 0.005 to 0.5 parts by weight, on the basis of 100 parts by weight of said host material, of a water soluble Mn salt to increase the threshold voltage of the resultant material.
Claim 9
Dependent Claim
37 words
A method for preparing a photoconductive powder according to claim 9, wherein said water soluble Mn salt is one member selected from the group consisting of MnCl 2 , Mn(NO 3 ) 2 and MnSO 4 .
Claim 10
Dependent Claim
19 words
A method for preparing a photoconductive powder according to claim 8, wherein said Mn salt is MnCl 2 .
Claim 11
Dependent Claim
66 words
A method for preparing a photoconductive powder according to claim 1, which further comprises performing between said cooling and re-firing steps, the step of: adding to the cooled material as a flux, one member selected from the group consisting of CdCl 2 , CdBr 2 , ZnCl 2 and ZnBr 2 ; and again firing the thus treated material under the conditions of the first firing.
Claim 12
Dependent Claim
17 words
A method according to claim 1, wherein said firing is performed at between 580° and 620° C.
Claim 13
Dependent Claim
31 words
A method according to claim 5 wherein the amount of said activator is 0.01 to 0.04 parts by weight on the basis of 100 parts by weight of said host material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-13 | 1980-12-13 | 1981-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-13 | 1984-12-13 | 1985-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-13 | 1988-12-13 | 1989-06-14 | $7700.00 | Window Closed / Lapsed |