Process for preparing a highly expanded polyvinyl chloride foam product
Assignee: Mitsubishi Chemical Corp
•
Filing: 1975-02-11
•
Granted: 1977-06-07
•
Expires: 1995-02-11
Abstract
Abstract An expanded polyvinyl chloride foam is prepared by a process characterized by admixing a polyvinyl chloride resin, which is prepared by emulsion copolymerization of a comonomer having an hydroxyl group, or a group capable of producing an hydroxyl group in the molecule under the processing conditions, with a plasticizer, a cross-linking agent, and a chemical blowing agent, introducing the admixture into a mold at a temperature lower than the melting temperature of said resin, and thereafter heating the resulting molded product to a temperature higher than the melting temperature of said resin to effect foam expansion.
Inventors
- 👤 Haruaki Kakitani
- 👤 Masao Maekawa
- 👤 Takashi Kokubo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:30
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/06; C08K; C08K5/00; C08K5/16; C08K5/22; C08L; C08L27/00; C08L27/02; C08L27/04; C08L27/06; C08L63/00; C08J2327/00; C08J2327/02; C08J2327/04; C08J2327/06; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/13; Y10S264/17; Y10S264/18
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
118 words
A process for preparing an expanded polyvinyl chloride foam, which comprises: admixing a polyvinyl chloride resin which is prepared by emulsion polymerization of vinylchloride and a comonomer having a hydroxyl group, with a plasticizer, a cross-linking agent and a chemical blowing agent; forming a preform of said mixture by introducing the mixture into a mold at a temperature lower than the melting temperature of said resin, wherein said melting temperature is defined as that temperature at which the cross-linkable polyvinyl chloride copolymer composition becomes a homogeneous melt by kneading at an elevated temperature; and thereafter effecting foam expansion of the resulting molded preform by heating said preform to a temperature higher than the melting temperature of said resin.
Claim 2
Dependent Claim
118 words
A process for preparing an expanded polyvinyl chloride foam, which comprises: admixing a polyvinyl chloride resin which is prepared by emulsion polymerization of vinylchloride and a comonomer having a hydroxyl group, with a plasticizer, a cross-linking agent and a chemical blowing agent; forming a preform of said mixture by introducing the mixture into a mold at a temperature lower than the melting temperature of said resin, wherein said melting temperature is defined as that temperature at which the cross-linkable polyvinyl chloride copolymer composition becomes a homogeneous melt by kneading at an elevated temperature; and thereafter effecting foam expansion of the resulting molded preform by heating said preform to a temperature higher than the melting temperature of said resin.
Claim 3
Dependent Claim
35 words
The process of claim 1, wherein said comonomer is selected from the group consisting of 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, 3-chloro-2-hydroxypropyl methacrylate, 3-chloro-2-hydroxypropyl acrylate, 3-hydroxybutyl acrylate, ethyl-2-hydroxyethyl fumarate and hydroxybutyl vinyl ether.
Claim 4
Dependent Claim
22 words
The process of claim 1, wherein the content of said comonomer in said vinyl chloride copolymer is 0.5 to 10% by weight.
Claim 5
Dependent Claim
73 words
The process of claim 1, wherein said cross-linking agent is selected from the group consisting of tolylene diisocyanate, diphenylmethane diisocyanate, hexamethylene diisocyanate, trimethylol propanetolylene diisocyanate adduct, polymethylene polyphenyl diisocyanate, n-butylated melamine resin, succinic acid, glutaric acid, adipic acid, pimellic acid, azelaic acid, phthalic acid, maleic acid, cyclohexane dicarboxylic acid and anhydrides thereof, triglycydyl diisocyanurate and an epoxy compound represented by the formula ##STR2## , wherein n is an integer from 1 to 10.
Claim 6
Dependent Claim
31 words
The process of claim 1, wherein said cross-linking agent is used in an amount of 0.5 to 10 parts by weight to 100 parts by weight of said vinyl chloride copolymer.
Claim 7
Dependent Claim
29 words
The process of claim 1, wherein said chemical blowing agent is selected from the group consisting of dinitrosopentamethylene tetramine, azodiacarbonamide,p,p'-oxybisbenzene sulfonyl hydrazide, para-toluene sulfonyl hydrazide and benzene sulfonyl hydrazide.
Claim 8
Dependent Claim
33 words
Th process of claim 1, wherein said chemical blowing agent is used in an amount of 5 to 40 parts by weight to 100 parts of weight of said vinyl chloride resin composition.
Claim 9
Dependent Claim
16 words
The process of claim 1, wherein a filler, stabilizer or pigment is added to said admixture.
Claim 10
Dependent Claim
16 words
The process of claim 1, wherein said admixture is kneaded prior to introduction into said mold.
Claim 11
Dependent Claim
24 words
The process of claim 9, wherein the kneading temperature of said vinyl chloride resin composition is within the range of 80° to 170° C.
References Cited (Backward Citations)
US3200089A
Cited
US3390105A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-06 | 1980-12-06 | 1981-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-06 | 1984-12-06 | 1985-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-06 | 1988-12-06 | 1989-06-07 | $7700.00 | Window Closed / Lapsed |