Hot melt adhesive
Assignee: Permacel
•
Filing: 1974-05-23
•
Granted: 1977-06-07
•
Expires: 1994-05-23
Abstract
Abstract A thermoplastic hot melt pressure-sensitive adhesive composition which is resistant to heat deterioration at elevated temperatures and, therefore, may be melted and maintained hot and ready for coating for extended periods of time without detracting from the properties of the adhesive. The composition is based upon a linear or radial A-B-A block copolymer and a mixture of solid and liquid tackifier resins and contains a heat stabilizing component which comprises an oil-soluble, heat-reactive phenol formaldehyde resin and a suitable antioxidant which preferably consists predominantly of a metal dithiocarbamate.
Inventors
- 👤 Ralf Korpman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 23:04
CPC Classifications
C; C09; C09J; C09J153/00; C09J153/02; C08; C08K; C08K5/00; C08K5/0008; C08K5/005; C08L; C08L101/00; C08L53/00; C08L53/02; C08L61/00; C08L61/04; C08L61/06; C09J201/00; C08L2666/00; C08L2666/02; C08L2666/28
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
180 words
A thermoplastic hot melt pressure-sensitive adhesive composition which comprises an elastomeric component comprising a major amount by weight of said component of a linear or radial elastomeric and thermoplastic A-B-A block copolymer wherein B is an elastomeric polymer block derived from a conjugated diene and A is a thermoplastic polymer block derived from styrene or a styrene homologue and said A blocks constitute about 10-50 percent by weight of the block copolymer; about 125-300 parts by weight of the elastomeric component of a tackifying component consisting essentially of a blend of normally solid and liquid tackifier resins, the proportion of solid resin to liquid resin in the blend being between about 4 to 1 and 1 to 3, said solid resins being normally friable at about 25° C. and said liquid resins being in a liquid state at about 25° C.; and an essentially non-catalyzed heat stabilizing component comprising about 1-5 percent by weight of the adhesive composition of an oil-soluble heat-reactive phenol formaldehyde resin and at least about 0.5 percent by weight of the composition of an antioxidant therefor.
Claim 2
Dependent Claim
180 words
A thermoplastic hot melt pressure-sensitive adhesive composition which comprises an elastomeric component comprising a major amount by weight of said component of a linear or radial elastomeric and thermoplastic A-B-A block copolymer wherein B is an elastomeric polymer block derived from a conjugated diene and A is a thermoplastic polymer block derived from styrene or a styrene homologue and said A blocks constitute about 10-50 percent by weight of the block copolymer; about 125-300 parts by weight of the elastomeric component of a tackifying component consisting essentially of a blend of normally solid and liquid tackifier resins, the proportion of solid resin to liquid resin in the blend being between about 4 to 1 and 1 to 3, said solid resins being normally friable at about 25° C. and said liquid resins being in a liquid state at about 25° C.; and an essentially non-catalyzed heat stabilizing component comprising about 1-5 percent by weight of the adhesive composition of an oil-soluble heat-reactive phenol formaldehyde resin and at least about 0.5 percent by weight of the composition of an antioxidant therefor.
Claim 3
Dependent Claim
22 words
A pressure-sensitive adhesive composition according to claim 1, which comprises about 0.5-2 percent of the antioxidant by weight of the adhesive composition.
Claim 4
Dependent Claim
15 words
A pressure-sensitive adhesive composition according to claim 1, wherein said antioxidant comprises a metal dithiocarbamate.
Claim 5
Dependent Claim
27 words
A pressure-sensitive adhesive composition according to claim 3, wherein said dithiocarbamate constitutes a major proportion of the antioxidant and said antioxidant also comprises 1,3,5-trimethyl-2,4,6-tris(3,5di-tertiary butyl-4hydroxy phenyl) benzene.
Claim 6
Dependent Claim
16 words
A pressure-sensitive adhesive composition according to claim 4, wherein said dithiocarbamate is a zinc dialkyl dithiocarbamate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-06 | 1980-12-06 | 1981-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-06 | 1984-12-06 | 1985-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-06 | 1988-12-06 | 1989-06-07 | $7700.00 | Window Closed / Lapsed |