Assignee: Celotex Corp
•
Filing: 1976-01-19
•
Granted: 1977-06-07
•
Expires: 1996-01-19
Abstract
Abstract A structural laminate comprises at least one planar facing sheet with a rigid foam attached to one surface of the facing sheet. The rigid foam may be any polymeric material which is capable of being foamed. Distributed substantially evenly throughout the foam is a mat of long straight glass fibers arranged in layers substantially parallel to the facing sheet. The process for producing this structural laminate comprises the steps of contacting a thin, substantially incompressible yet expansible mat of long straight glass fibers with a foam-forming mixture on each face of the mat, and passing the facing sheets having the mat and the foam-forming mixture there between through the nip of two rotating rolls.
Inventors
- 👤 Donald E. Hipchen
- 👤 Michael J. Skowronski
- 👤 Joseph R. Hagan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:57
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/18; B32B5/20; B29; B29C; B29C44/00; B29C44/20; B29C44/30; B29C70/00; B29C70/003; B29K; B29K2309/00; B29K2309/08; B32B38/00; B32B2038/0052; B32B2038/0088; B32B2262/00; B32B2262/10; B32B2262/101; B32B2309/00; B32B2309/08; B32B2309/10; B32B2309/105; B32B2309/14; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24058; Y10T428/24124; Y10T428/249921; Y10T428/249953; Y10T428/249967; Y10T428/249969; Y10T442/00; Y10T442/60; Y10T442/643; Y10T442/644; Y10T442/647
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
111 words
A process for producing a structural laminate comprising the steps of: I. contacting a thin, substantially incompressible yet expansible mat of glass fibers with a foam-forming mixture, Ii. positioning a facing sheet on each face of the mat, and Iii. passing the facing sheets having the mat and the foam-forming mixture therebetween through the nip of two rotating rolls, the mat of glass fibers being further characterized by A. the glass fibers being arranged in layers, B. the glass fibers within each layer being long, straight and substantially parallel, and C. the glass fibers in each layer being at an acute angle to the glass fibers in each next adjacent layer.
Claim 2
Dependent Claim
111 words
A process for producing a structural laminate comprising the steps of: I. contacting a thin, substantially incompressible yet expansible mat of glass fibers with a foam-forming mixture, Ii. positioning a facing sheet on each face of the mat, and Iii. passing the facing sheets having the mat and the foam-forming mixture therebetween through the nip of two rotating rolls, the mat of glass fibers being further characterized by A. the glass fibers being arranged in layers, B. the glass fibers within each layer being long, straight and substantially parallel, and C. the glass fibers in each layer being at an acute angle to the glass fibers in each next adjacent layer.
Claim 3
Dependent Claim
35 words
The process of claim 1 wherein the mat of glass fibers has an initial thickness less than 1 and 1/2 times the separation of the facing sheets at the nip of the two rotating rolls.
Claim 4
Dependent Claim
131 words
A process for producing a structural laminate comprising the steps of: I. contacting a thin, substantially incompressible yet expansible mat of glass fibers with a foam-forming mixture, Ii. positioning a facing sheet on each face of the mat, Iii. passing the facing sheets having the mat and the foam-forming mixture therebetween through the nip of two rotating rolls, the mat of glass fibers being further characterized by A. the glass fibers being arranged in layers, B. the glass fibers within each layer being long, straight and substantially parallel, and C. the glass fibers in each layer being at an acute angle to the glass fibers in each next adjacent layer, and Iv. permitting the mat of glass fibers to expand under the sole influence of the expansion of the foam-forming mixture.
Claim 5
Dependent Claim
131 words
A process for producing a structural laminate comprising the steps of: I. contacting a thin, substantially incompressible yet expansible mat of glass fibers with a foam-forming mixture, Ii. positioning a facing sheet on each face of the mat, Iii. passing the facing sheets having the mat and the foam-forming mixture therebetween through the nip of two rotating rolls, the mat of glass fibers being further characterized by A. the glass fibers being arranged in layers, B. the glass fibers within each layer being long, straight and substantially parallel, and C. the glass fibers in each layer being at an acute angle to the glass fibers in each next adjacent layer, and Iv. permitting the mat of glass fibers to expand under the sole influence of the expansion of the foam-forming mixture.
Claim 6
Dependent Claim
34 words
The process of claim 1 wherein the mat of glass fibers has a low loft such that pressure applied to the faces of the mat will not substantially reduce the thickness of the mat.
Claim 7
Dependent Claim
38 words
The process of claim 1 wherein the fibers forming the mat are wetable by the foam-forming mixture to the extent that the foam-forming mixture will penetrate and completely fill the interstices between the glass fibers of the mat.
Claim 8
Dependent Claim
25 words
The process of claim 1 wherein the glass fibers of the mat are arranged in layers which are parallel to the faces of the mat.
Claim 9
Dependent Claim
34 words
The process of claim 1 wherein the glass fibers in each layer of the mat are at an angle of less than 60° to the glass fibers in each of the next adjacent layers.
Claim 10
Dependent Claim
40 words
The process of claim 1 wherein the glass fibers are attached to one another by an amount of fiber binder sufficient to make the mat of glass fibers dimensionally stable but insufficient to fill the interstices between the glass fibers.
Claim 11
Dependent Claim
149 words
A process for producing a structural laminate comprising the steps of: I. contacting a mat of glass fibers with a foam-forming mixture, Ii. positioning a facing sheet comprising a metal on each face of the mat, Iii. passing the facing sheets having the mat of glass fibers and the foam-forming mixture therebetween through the nip of two rotating rolls wherein: A. the thickness of the mat remains substantially the same as prior to passing through the nip, B. the velocity of the mat is equal to the velocity of the facing sheets, C. the glass fibers of the mat are arranged in layers, D. the glass fibers within each layer are substantially parallel, E. the glass fibers in each layer are at an acute angle to the glass fibers in each next adjacent layer, and F. the foam-forming mixture completely fills the interstices between the fibers of the mat.
Claim 12
Dependent Claim
149 words
A process for producing a structural laminate comprising the steps of: I. contacting a mat of glass fibers with a foam-forming mixture, Ii. positioning a facing sheet comprising a metal on each face of the mat, Iii. passing the facing sheets having the mat of glass fibers and the foam-forming mixture therebetween through the nip of two rotating rolls wherein: A. the thickness of the mat remains substantially the same as prior to passing through the nip, B. the velocity of the mat is equal to the velocity of the facing sheets, C. the glass fibers of the mat are arranged in layers, D. the glass fibers within each layer are substantially parallel, E. the glass fibers in each layer are at an acute angle to the glass fibers in each next adjacent layer, and F. the foam-forming mixture completely fills the interstices between the fibers of the mat.
Claim 13
Dependent Claim
56 words
The process of claim 9 further comprising the step of passing the facing sheets having the mat and the foam-forming mixture therebetween from the nip of the two rotating rolls into an expansion zone wherein the foam-forming mixture expands under the influence of heat generated in an exothermic reaction between the components of the foam-forming mixture.
Claim 14
Dependent Claim
24 words
The process of claim 3 wherein the layers of fibers in the mat separate under the influence of the expansion of the foam-forming mixture.
Claim 15
Dependent Claim
25 words
The process of claim 3 wherein the layers of fibers in the mat maintain their same order but are distributed throughout the resultant structural laminate.
Claim 16
Dependent Claim
31 words
The process of claim 3 wherein the layers of fibers in the mat are evenly distributed throughout the structural laminate in planes substantially parallel to the planes of the facing sheets.
Claim 17
Dependent Claim
23 words
The process of claim 3 wherein the foam-forming mixture cures under the influence of heat added by the controlled introduction of hot air.
Claim 18
Dependent Claim
22 words
The process of claim 9 wherein the thickness of the mat prior to passing through the nip is less than 0.1 inches.
Claim 19
Dependent Claim
23 words
The process of claim 15 wherein the thickness of the mat prior to passing through the nip is between 0.010 and 0.050 inches.
Claim 20
Dependent Claim
17 words
The process of claim 9 wherein the glass fibers have an average length that exceeds 5 feet.
Claim 21
Dependent Claim
34 words
The process of claim 9 wherein the glass fibers in each layer of the mat are an an angle of less than 60° to the glass fibers in each of the next adjacent layers.
Claim 22
Dependent Claim
58 words
The process of claim 9 wherein the glass fibers are attached to one another by an amount of fiber binder sufficient to make the mat of glass fibers dimensionally stable but insufficient to fill the interstices between the glass fibers and insufficient to resist the separation of the glass fibers under the influence of the expanding foam-forming mixture.
Claim 23
Dependent Claim
26 words
The process of claim 9 wherein the mat of glass fibers are included in the amount of 4-24 grams per board-foot of the resulting structural laminate.
Claim 24
Dependent Claim
165 words
A process for producing a structural laminate comprising the steps of: I. providing a thin, substantially incompressible yet expansible mat of glass fibers wherein: A. the glass fibers are arranged in layers, B. the glass fibers within each layer are long, straight and substantially parallel, and C. the glass fibers in each layer are at an acute angle to the glass fibers in each next adjacent layer, D. the glass fibers are lightly bonded to each other at their intersections by means of interfiber bonds, E. the mat of glass fibers has an indefinite running length, Ii. stretching the mat of glass fibers in a direction parallel to its running length by an amount sufficient to rupture only some of the interfiber bonds, and then Iii. contacting the mat with a foam-forming mixture, Iv. positioning a facing sheet on each face of the mat, and V. passing the facing sheets having the mat and the foam-forming mixture therebetween through the nip of two rotating rolls.
Claim 25
Dependent Claim
165 words
A process for producing a structural laminate comprising the steps of: I. providing a thin, substantially incompressible yet expansible mat of glass fibers wherein: A. the glass fibers are arranged in layers, B. the glass fibers within each layer are long, straight and substantially parallel, and C. the glass fibers in each layer are at an acute angle to the glass fibers in each next adjacent layer, D. the glass fibers are lightly bonded to each other at their intersections by means of interfiber bonds, E. the mat of glass fibers has an indefinite running length, Ii. stretching the mat of glass fibers in a direction parallel to its running length by an amount sufficient to rupture only some of the interfiber bonds, and then Iii. contacting the mat with a foam-forming mixture, Iv. positioning a facing sheet on each face of the mat, and V. passing the facing sheets having the mat and the foam-forming mixture therebetween through the nip of two rotating rolls.
Claim 26
Dependent Claim
27 words
The process of claim 21 wherein the stretching results in an elongation of 1 to 10 percent based on the length of the mat prior to stretching.
Claim 27
Dependent Claim
69 words
The process of claim 21 wherein the stretching is accomplished by passing the mat through two pairs of rotating rolls wherein: A. the axes of the rolls are perpendicular to the running length of the mat, B. the nip of each pair of rolls engages the mat, C. the peripheral speed of the second pair of rolls is greater than the peripheral speed of the first pair of rolls.
Claim 28
Dependent Claim
30 words
The process of claim 21 wherein the stretching is accomplished by providing the mat in the form on a roll and then retarding the rate of advancement of the roll.
Claim 29
Dependent Claim
193 words
A process for producing a structural laminate comprising the steps of: I. providing a thin, substantially incompressible yet expansible mat of glass fibers wherein: A. the glass fibers are arranged in layers, B. the glass fibers within each layer are long, straight and substantially parallel, and C. the glass fibers in each layer are at an acute angle to the glass fibers in each next adjacent layer, D. to glass fibers are lightly bonded to each other at their intersections by means of interfiber bonds, E. the mat of glass fibers has an indefinite running length, Ii. stretching the mat of glass fibers in a direction parallel to its running length by an amount of 1 to 10 percent based on the length of the mat prior to stretching wherein: A. the stretching is accomplished by passing the mat through two pairs of rotating rolls, B. the axes of the rolls are perpendicular to the running length of the mat, C. the nip of each pair of rolls engages the mat, D. the peripheral speed of the second pair of rolls is greater than the peripheral speed of the first pair of rolls.
Claim 30
Dependent Claim
193 words
A process for producing a structural laminate comprising the steps of: I. providing a thin, substantially incompressible yet expansible mat of glass fibers wherein: A. the glass fibers are arranged in layers, B. the glass fibers within each layer are long, straight and substantially parallel, and C. the glass fibers in each layer are at an acute angle to the glass fibers in each next adjacent layer, D. to glass fibers are lightly bonded to each other at their intersections by means of interfiber bonds, E. the mat of glass fibers has an indefinite running length, Ii. stretching the mat of glass fibers in a direction parallel to its running length by an amount of 1 to 10 percent based on the length of the mat prior to stretching wherein: A. the stretching is accomplished by passing the mat through two pairs of rotating rolls, B. the axes of the rolls are perpendicular to the running length of the mat, C. the nip of each pair of rolls engages the mat, D. the peripheral speed of the second pair of rolls is greater than the peripheral speed of the first pair of rolls.
Claim 31
Dependent Claim
26 words
The process of claim 3 wherein the foam-forming mixture expands under the influence of heat generated in an exothermic reaction between components of the foam-forming mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-06 | 1980-12-06 | 1981-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-06 | 1984-12-06 | 1985-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-06 | 1988-12-06 | 1989-06-07 | $7700.00 | Window Closed / Lapsed |