Continuous stream - inclined trough treatment of ductile iron

Claim 1

A method of producing treated iron, comprising: a. providing an inclined and enclosed course through which a molten stream of treatable iron may flow, said enclosed course having an expansion chamber interposed therein with an inlet and an outlet respectively connecting said course to said chamber while permitting said iron to flow therethrough, at least one of said inlet or outlet being controllable in aperture size, said chamber having another opening into which and through which a graduated supply of treating agent may be injected to contact, react, mix and expand with said iron flow, said chamber being comprised of refractory material substantially unreactive with the iron flow or agent and said chamber being maintained in a gas-tight condition, said course further being arranged so that the outflow from said expansion chamber is directed immediately to a mold solidifying said treated iron substantially independent of time and temperature variations, b. introducing a predetermined quantity of molten treatable iron to said course in a manner to flow into and through said chamber, said treatable iron having a sulfur content in the range of 0.01-0.015% by weight of the predetermined quantity of iron, c. simultaneous with flow through said chamber, injecting a predetermined and continuous supply of treating agent through said another opening, said treating agent being a modifier selected from the group consisting of a rod of solid magnesium, magnesium ferro-silicon in the form of either lumps or pellets and magnesium vapor, and d. adjusting the aperture of said controllable inlet or outlet so that a predetermined collection of iron is developed and maintained in said chamber for a substantial portion of said iron flow therethrough whereby reaction between said agent and iron can create turbulence to promote further reaction and uniform distribution of products of said iron treatment.

Claim 2

A method of producing treated iron, comprising: a. providing an inclined and enclosed course through which a molten stream of treatable iron may flow, said enclosed course having an expansion chamber interposed therein with an inlet and an outlet respectively connecting said course to said chamber while permitting said iron to flow therethrough, at least one of said inlet or outlet being controllable in aperture size, said chamber having another opening into which and through which a graduated supply of treating agent may be injected to contact, react, mix and expand with said iron flow, said chamber being comprised of refractory material substantially unreactive with the iron flow or agent and said chamber being maintained in a gas-tight condition, said course further being arranged so that the outflow from said expansion chamber is directed immediately to a mold solidifying said treated iron substantially independent of time and temperature variations, b. introducing a predetermined quantity of molten treatable iron to said course in a manner to flow into and through said chamber, said treatable iron having a sulfur content in the range of 0.01-0.015% by weight of the predetermined quantity of iron, c. simultaneous with flow through said chamber, injecting a predetermined and continuous supply of treating agent through said another opening, said treating agent being a modifier selected from the group consisting of a rod of solid magnesium, magnesium ferro-silicon in the form of either lumps or pellets and magnesium vapor, and d. adjusting the aperture of said controllable inlet or outlet so that a predetermined collection of iron is developed and maintained in said chamber for a substantial portion of said iron flow therethrough whereby reaction between said agent and iron can create turbulence to promote further reaction and uniform distribution of products of said iron treatment.

Claim 8

A method of making nodular cast iron, comprising: a. heating a charge of un-nodularized or grey iron to a temperature in the range of 2500° -2700° F, b. passing a stream of said heated iron at said temperature through an inclined trough while continuously adding a nodularizing agent at a measured ratio to the iron flowing through said trough to provide for a reaction between said iron (or impurities in said iron) and said agent, said nodularizing agent being added in the form of a pellet having a lump size not less than 750 microns, said nodularizing agent pellets being constituted of a high content of magnesium and being added in a predetermined ratio such that 0.2- 0.25 grams of said magnesium will be dissolved for each pound of iron flowing through said chamber, said trough being enclosed in a manner to provide an air-tight passage of a molten iron therethrough, said inclined trough further being defined to have inclined side walls forming a transverse V-shape whereby, in conjunction with the chemical reaction between said nodularizing agent and molten iron, a self-imposed turbulence is provided to insure adequate mixing of said agent and iron without the need for any independent mechanical mixing, c. controlling the egress of said iron flow through said trough to provide a turbulent pool of molten iron therein and so limited whereby the egress temperature of said reacted iron and agent is not substantially less than 2350° F, whereby at least 90% of said nodularizing agent is reacted with said iron, and d. immediately casting said reacted iron to provide a nodular cast iron consisting essentially of about 3.5 carbon, 2.5% silicon, about 0.6 manganese, a carbon to silicon ratio of 7:5, sulfur being no greater than 0.015% and the remainder being essentially iron.

Claim 9

A method of making nodular cast iron, comprising: a. heating a charge of un-nodularized or grey iron to a temperature in the range of 2500° -2700° F, b. passing a stream of said heated iron at said temperature through an inclined trough while continuously adding a nodularizing agent at a measured ratio to the iron flowing through said trough to provide for a reaction between said iron (or impurities in said iron) and said agent, said nodularizing agent being added in the form of a pellet having a lump size not less than 750 microns, said nodularizing agent pellets being constituted of a high content of magnesium and being added in a predetermined ratio such that 0.2- 0.25 grams of said magnesium will be dissolved for each pound of iron flowing through said chamber, said trough being enclosed in a manner to provide an air-tight passage of a molten iron therethrough, said inclined trough further being defined to have inclined side walls forming a transverse V-shape whereby, in conjunction with the chemical reaction between said nodularizing agent and molten iron, a self-imposed turbulence is provided to insure adequate mixing of said agent and iron without the need for any independent mechanical mixing, c. controlling the egress of said iron flow through said trough to provide a turbulent pool of molten iron therein and so limited whereby the egress temperature of said reacted iron and agent is not substantially less than 2350° F, whereby at least 90% of said nodularizing agent is reacted with said iron, and d. immediately casting said reacted iron to provide a nodular cast iron consisting essentially of about 3.5 carbon, 2.5% silicon, about 0.6 manganese, a carbon to silicon ratio of 7:5, sulfur being no greater than 0.015% and the remainder being essentially iron.

Claim 12

A method of continuously making a plurality of nodular cast iron bodies by use of a multiple number of casting flasks, the method comprising: a. preparing a molten charge of untreated cast iron having a pour temperature of 2500° -2700° F, b. passing said molten iron along an inclined stream and through an enclosed expansion and reaction chamber devoid of ambient air, a nodularizing agent being injected into said chamber at a predetermined ratio to the flow of molten iron therethrough, said chamber being inclined and the ingress and egress of molten iron therethrough being controllable so as to maintain a predetermined pool of molten iron reacting with said nodularizing agent in said chamber substantially throughout the flow of said stream therethrough, and c. immediately directing the reacted flow from said chamber to several molding flasks whereby said reacted iron enters said mold cavity in each of said flasks in less than 5 seconds after reaction in said chamber.

Claim 13

A method of continuously making a plurality of nodular cast iron bodies by use of a multiple number of casting flasks, the method comprising: a. preparing a molten charge of untreated cast iron having a pour temperature of 2500° -2700° F, b. passing said molten iron along an inclined stream and through an enclosed expansion and reaction chamber devoid of ambient air, a nodularizing agent being injected into said chamber at a predetermined ratio to the flow of molten iron therethrough, said chamber being inclined and the ingress and egress of molten iron therethrough being controllable so as to maintain a predetermined pool of molten iron reacting with said nodularizing agent in said chamber substantially throughout the flow of said stream therethrough, and c. immediately directing the reacted flow from said chamber to several molding flasks whereby said reacted iron enters said mold cavity in each of said flasks in less than 5 seconds after reaction in said chamber.

Claim 15

A method of making nodular cast iron, comprising: heating a charge of un-nodularized or grey iron to a temperature in the range of 2500° -2700° F, b. passing a stream of said heated iron at said temperature through an inclined trough while continuously adding a nodularizing agent at a measured ratio to the iron flowing through said trough to provide for a reaction between said iron (or impurities in said iron) and said agent, said trough being enclosed to a chamber facilitating atmosphere control therein and to trap gaseous emissions and pyrotechnics resulting from said reaction, the atmosphere within said chamber being non-oxidizing, c. controlling the egress of said iron flow through said trough to provide a turbulent pool of molten iron therein and so limited whereby the egress temperature of said reacted iron and agent is not substantially less than 2350° F, whereby at least 90% of said nodularizing agent is reacted with said iron, and d. immediately casting said reacted iron to provide a nodular cast iron consisting essentially of about 3.5 carbon, 2.5% silicon, about 0.6 manganese, a carbon to silicon ratio of 7:5, sulfur being no greater than 0.015% and the remainder being essentially iron.

Claim 16

A method of making nodular cast iron, comprising: heating a charge of un-nodularized or grey iron to a temperature in the range of 2500° -2700° F, b. passing a stream of said heated iron at said temperature through an inclined trough while continuously adding a nodularizing agent at a measured ratio to the iron flowing through said trough to provide for a reaction between said iron (or impurities in said iron) and said agent, said trough being enclosed to a chamber facilitating atmosphere control therein and to trap gaseous emissions and pyrotechnics resulting from said reaction, the atmosphere within said chamber being non-oxidizing, c. controlling the egress of said iron flow through said trough to provide a turbulent pool of molten iron therein and so limited whereby the egress temperature of said reacted iron and agent is not substantially less than 2350° F, whereby at least 90% of said nodularizing agent is reacted with said iron, and d. immediately casting said reacted iron to provide a nodular cast iron consisting essentially of about 3.5 carbon, 2.5% silicon, about 0.6 manganese, a carbon to silicon ratio of 7:5, sulfur being no greater than 0.015% and the remainder being essentially iron.

Claim 17

A method of making nodular cast iron, comprising: a. heating a charge of un-nodularized or grey iron to a temperature in the range of 2500° -2700° F, b. passing a stream of said heated iron at said temperature through an inclined trough while continuously adding a nodularizing agent at a measured ratio to the iron flowing through said trough to provide for a reaction between said iron (or impurities in said iron) and said agent, said nodularizing agent is added in the form of a pellet smaller in dimension than the diameter of said stream and consisting essentially of magnesium ferrosilicon with magnesium constituting 4- 9% by weight of the agent, c. controlling the egress of said iron flow through said trough to provide a turbulent pool of molten iron therein and so limited whereby the egress temperature of said reacted iron and agent is not substantially less than 2350° F, whereby at least 90% of said nodularizing agent is reacted with said iron, and d. immediately casting said reacted iron to provide a nodular cast iron consisting essentially of about 3.5 carbon, 2.5% silicon, about 0.6 manganese, a carbon to silicon ratio of 7:5, sulfur being no greater than 0.015% and the remainder being essentially iron.

Claim 18

A method of making nodular cast iron, comprising: a. heating a charge of un-nodularized or grey iron to a temperature in the range of 2500° -2700° F, b. passing a stream of said heated iron at said temperature through an inclined trough while continuously adding a nodularizing agent at a measured ratio to the iron flowing through said trough to provide for a reaction between said iron (or impurities in said iron) and said agent, said nodularizing agent is added in the form of a pellet smaller in dimension than the diameter of said stream and consisting essentially of magnesium ferrosilicon with magnesium constituting 4- 9% by weight of the agent, c. controlling the egress of said iron flow through said trough to provide a turbulent pool of molten iron therein and so limited whereby the egress temperature of said reacted iron and agent is not substantially less than 2350° F, whereby at least 90% of said nodularizing agent is reacted with said iron, and d. immediately casting said reacted iron to provide a nodular cast iron consisting essentially of about 3.5 carbon, 2.5% silicon, about 0.6 manganese, a carbon to silicon ratio of 7:5, sulfur being no greater than 0.015% and the remainder being essentially iron.