Method of making asymmetric cellulose triacetate membranes
Assignee: United States Department of the Interior
•
Filing: 1975-07-17
•
Granted: 1977-05-31
•
Expires: 1995-07-17
Abstract
Abstract Asymmetric cellulose triacetate semipermeable membranes cast from a solution of cellulose triacetate having an acetyl content of at least 43 percent in a solvent mixture having a ratio of dioxane to acetone of at least about 1.5 to 1, which solution also contains a swelling agent in the form of a low molecular weight alcohol or a low molecular weight mono- or poly-basic acid. Solvent is evaporated from one surface of the cast film to form a dense gel layer and the film is immersed in water to provide an asymmetric semipermeable membrane having a high salt-rejection capability and good flux.
Inventors
- 👤 Charles R. Mungle
- 👤 Ronald L. Fox
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 04:12
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/08; B01D71/12; B01D71/14; B01D71/16; B01D67/00; B01D67/0002; B01D67/0009; B01D67/0011
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
140 words
A method for making an asymmetric cellulose triacetate semipermeable membrane, which method comprises forming a solution of cellulose triacetate having an acetyl content of 43.5 percent, by dissolving said cellulose triacetate in a solvent mixture of acetone and dioxane wherein said casting solution contains a ratio of dioxane to acetone of about 3.8 to 1 and also contains a swelling agent consisting of a mixture of methanol and maleic acid, casting said solution to form a film, evaporating solvent from one surface of said film for sufficient time to form a dense gel layer at said surface, and then treating said film with water to form a gel, and thereafter annealing said gelled film by immersion in water at a temperature of about 85° C., to thereby provide an asymmetric semipermeable membrane having a high salt-rejection capability and good flux.
Claim 2
Independent Claim
140 words
A method for making an asymmetric cellulose triacetate semipermeable membrane, which method comprises forming a solution of cellulose triacetate having an acetyl content of 43.5 percent, by dissolving said cellulose triacetate in a solvent mixture of acetone and dioxane wherein said casting solution contains a ratio of dioxane to acetone of about 3.8 to 1 and also contains a swelling agent consisting of a mixture of methanol and maleic acid, casting said solution to form a film, evaporating solvent from one surface of said film for sufficient time to form a dense gel layer at said surface, and then treating said film with water to form a gel, and thereafter annealing said gelled film by immersion in water at a temperature of about 85° C., to thereby provide an asymmetric semipermeable membrane having a high salt-rejection capability and good flux.
Claim 3
Dependent Claim
27 words
A method for making an asymmetric semipermeable membrane in accordance with claim 1 wherein said evaporation is carried out for between about 25 and about 90 seconds.
Claim 4
Dependent Claim
29 words
A method for making a semipermeable membrane in accordance with claim 2 wherein said evaporation is carried out at a temperature between about 15° C. and about 35° C.
Claim 5
Dependent Claim
31 words
A method for making a semipermeable membrane in accordance with claim 3 wherein said solution being cast is maintained at a temperature of between about 0° C. and about 30° C.
Claim 6
Dependent Claim
30 words
A method for making an asymmetric semipermeable membrane in accordance with claim 1 wherein said solution contains cellulose triacetate in an amount between about 11 and about 18 weight percent.
Claim 7
Dependent Claim
48 words
A method for making a semipermeable membrane in accordance with claim 1 wherein said solution contains cellulose triacetate in an amount between about 15.5 and about 16.5 weight percent and has a viscosity between about 200 and about 2000 poises at the temperature at which casting takes place.
References Cited (Backward Citations)
US3497072A
Cited
US3884801A
Cited
US3878276A
Cited
US3883626A
Cited
US3917777A
Cited
US3846404A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-30 | 1980-11-29 | 1981-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-30 | 1984-11-29 | 1985-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-30 | 1988-11-29 | 1989-05-31 | $7700.00 | Window Closed / Lapsed |