Precipitation of selenium from copper electrowinning solutions
Assignee: Cyprus Amax Minerals Co
•
Filing: 1976-04-19
•
Granted: 1977-05-31
•
Expires: 1996-04-19
Abstract
Abstract Selenium is removed from copper electrolytes by adding a substance selected from the group consisting of metals above copper in the electromotive series, excluding alkali metals, such as nickel powder, cobalt powder and iron powder. Sodium sulfide can also be used along with a subsequent addition of ferric sulfate. The amount of the reactive substance added should be sufficient to reduce the selenium content to below 2 ppm.
Inventors
- 👤 Cvetko B. Nikolic
- 👤 John M. Laferty
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:26
CPC Classifications
C; C22; C22B; C22B15/00; C22B15/0063; C22B15/0084; C22B15/0089; C22B15/0091; C25; C25C; C25C1/00; C25C1/12; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
109 words
A method for removing selenium from a copper-containing electrolyte solution containing over 2 ppm of total selenium which comprises, adding to said copper-containing solution a substance selected from the group consisting of metals above copper in the electromotive series, excluding alkali metals, in an amount at least sufficient to reduce the selenium content to below 2 ppm, subjecting said copper-containing electrolyte solution to an elevated temperature of at least about 190° C. and a pressure of at least about 180 psig to reduce the total selenium content of said solution to less than 2 ppm by forming a selenium-containing precipitate, and then separating the selenium-containing precipitate from said solution.
Claim 2
Independent Claim
109 words
A method for removing selenium from a copper-containing electrolyte solution containing over 2 ppm of total selenium which comprises, adding to said copper-containing solution a substance selected from the group consisting of metals above copper in the electromotive series, excluding alkali metals, in an amount at least sufficient to reduce the selenium content to below 2 ppm, subjecting said copper-containing electrolyte solution to an elevated temperature of at least about 190° C. and a pressure of at least about 180 psig to reduce the total selenium content of said solution to less than 2 ppm by forming a selenium-containing precipitate, and then separating the selenium-containing precipitate from said solution.
Claim 3
Dependent Claim
34 words
The method of claim 1, wherein the substance added to the copper electrolyte solution for removing selenium from said solution is selected from the group consisting of nickel powder, cobalt powder and iron powder.
Claim 4
Dependent Claim
16 words
The method of claim 2, wherein said selenium is removed by adding nickel to said solution.
Claim 5
Dependent Claim
16 words
The method of claim 2, wherein said selenium is removed by adding cobalt to said solution.
Claim 6
Dependent Claim
16 words
The method of claim 2, wherein said selenium is removed by adding iron to said solution.
Claim 7
Dependent Claim
53 words
The method of claim 1, wherein said copper-containing electrolyte solution is a sulfuric acid electrolyte solution and contains about 20 to 100 gpl copper, up to 70 gpl nickel, 5 to 250 gpl H 2 SO 4 and up to 5 gpl iron, the pH of said solution being less than about 3.
Claim 8
Independent Claim
131 words
A method of removing selenium from a copper-containing electrolyte solution containing over 2 ppm total selenium which comprises, adding an amount of Na 2 S to said solution sufficient to reduce said selenium to less than 2 ppm, the amount of said Na 2 S being such as not to exceed 100 ppm of sodium ions in solution, subjecting said solution to a temperature of at least about 190° C. and a pressure of at least about 180 psig in an autoclave, introducing into the autoclave an amount of Fe 2 (SO 4 ) 3 not exceeding an amount corresponding to 5 gpl of iron per liter, thereby reducing said selenium to less than 2 ppm by forming a selenium-containing precipitate, and then separating the selenium-containing precipitate from said electrolyte solution.
Claim 9
Independent Claim
131 words
A method of removing selenium from a copper-containing electrolyte solution containing over 2 ppm total selenium which comprises, adding an amount of Na 2 S to said solution sufficient to reduce said selenium to less than 2 ppm, the amount of said Na 2 S being such as not to exceed 100 ppm of sodium ions in solution, subjecting said solution to a temperature of at least about 190° C. and a pressure of at least about 180 psig in an autoclave, introducing into the autoclave an amount of Fe 2 (SO 4 ) 3 not exceeding an amount corresponding to 5 gpl of iron per liter, thereby reducing said selenium to less than 2 ppm by forming a selenium-containing precipitate, and then separating the selenium-containing precipitate from said electrolyte solution.
Claim 10
Dependent Claim
53 words
The method of claim 7, wherein said copper-containing electrolyte solution is a sulfuric acid electrolyte solution and contains about 20 to 100 gpl copper, up to 70 gpl nickel, 5 to 250 gpl H 2 SO 4 and up to 5 gpl iron, the pH of said solution being less than about 3.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-30 | 1980-11-29 | 1981-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-30 | 1984-11-29 | 1985-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-30 | 1988-11-29 | 1989-05-31 | $7700.00 | Window Closed / Lapsed |