Method for coloring a stainless steel
Assignee: Nippon Steel Corp
•
Filing: 1975-10-17
•
Granted: 1977-05-31
•
Expires: 1995-10-17
Abstract
Abstract A method for coloring a stainless steel using a potential-time curve which comprises seeking for an individual coloring potential difference to be colored by compensating a standard coloring potential difference by difference between a standard inflexion point potential and an individual inflexion point potential, and stopping the coloring when the individual coloring potential changes in an amount corresponding to the individual coloring potential difference from the individual inflexion point potential.
Inventors
- 👤 Tomoo Takahari
- 👤 Shiyuichi Kondo
- 👤 Nobumasa Sone
- 👤 Kengi Hashimoto
- 👤 Tadashi Ishiguro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 09:32
CPC Classifications
C; C23; C23C; C23C22/00; C23C22/73; C23C22/77; C25; C25F; C25F1/00; C25F1/02; C25F1/04; C25F1/06; C25F3/00; C25F3/02; C25F3/06
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
217 words
In a method for coloring a stainless steel wherein the stainless steel is immersed in a coloring bath for a period of time, the improvement which comprises: (a) determining for a given sample of said steel in the bath the difference between the standard inflexion point potential and the potential present when the sample has the desired color, the potentials being determined against a reference electrode immersed in the bath; (b) determining the individual inflexion point potential for a sample of the steel to be colored; and (c) immersing the steel to be colored in the bath for a period of time such that the coloring process is stopped when the potential difference between the individual inflexion point potential and the instantaneous potential is determined by the formula: Potential difference = potential difference for the standard sample when the sample has the desired color ± α (Standard inflexion point potential -- individual inflexion point potential) wherein α is + when a saturated calomel electrode is used and is - when a platinum electrode is used; and wherein α is between 0.23 to 0.36 when the individual inflexion point potential is nobler than the standard inflexion point and is between 0.44 and 0.61 when the individual inflexion point potential is base compared to the standard inflexion point potential.
Claim 2
Dependent Claim
217 words
In a method for coloring a stainless steel wherein the stainless steel is immersed in a coloring bath for a period of time, the improvement which comprises: (a) determining for a given sample of said steel in the bath the difference between the standard inflexion point potential and the potential present when the sample has the desired color, the potentials being determined against a reference electrode immersed in the bath; (b) determining the individual inflexion point potential for a sample of the steel to be colored; and (c) immersing the steel to be colored in the bath for a period of time such that the coloring process is stopped when the potential difference between the individual inflexion point potential and the instantaneous potential is determined by the formula: Potential difference = potential difference for the standard sample when the sample has the desired color ± α (Standard inflexion point potential -- individual inflexion point potential) wherein α is + when a saturated calomel electrode is used and is - when a platinum electrode is used; and wherein α is between 0.23 to 0.36 when the individual inflexion point potential is nobler than the standard inflexion point and is between 0.44 and 0.61 when the individual inflexion point potential is base compared to the standard inflexion point potential.
Claim 3
Dependent Claim
32 words
A method according to any of claim 1, which further comprises removing a surfacial film layer and a denaturalized layer formed on the surface of the stainless steel prior to the coloring.
Claim 4
Dependent Claim
45 words
A method according to claim 2, in which an acid solution containing at least one acid selected from the group consisting of sulfuric acid, phosphoric acid, nitric acid, chromic acid and hydrochloric acid is used for removing the surfacial film layer and the denaturalized layer.
Claim 5
Dependent Claim
17 words
A method according to claim 3, in which the stainless steel is immersed in the acid solution.
Claim 6
Dependent Claim
25 words
A method according to claim 4, in which the immersion is done for 30 to 1200 seconds at a temperature between 40° and 60° C.
Claim 7
Dependent Claim
17 words
A method according to claim 3, in which the stainless steel is electrolized in the acid solution.
Claim 8
Dependent Claim
23 words
A method according to claim 6, in which the electrolysis is done at a current density between 0.5 and 30 A/dm 2 .
Claim 9
Dependent Claim
65 words
A method according to any of claim 1, in which the stainless steel is subjected to a pre-coloring treatment in an aqueous solution containing at least one acid selected from the group consisting of sulfuric acid, nitric acid, phosphoric acid, and at least one compound selected from the group consisting of chromic anhydride, potassium dichromate, sodium dichromate and iron salts, nickel salts and manganese salts.
Claim 10
Dependent Claim
19 words
A method according to claim 8, in which the precoloring treatment is done by immersion in the aqueous solution.
Claim 11
Dependent Claim
18 words
A method according to claim 9, in which the immersion is done for 30 seconds to 60 minutes.
Claim 12
Dependent Claim
19 words
A method according to claim 8, in which the precoloring treatment is done by electrolysis in the aqueous solution.
Claim 13
Dependent Claim
18 words
A method according to claim 11, in which the electrolysis is done for 5 seconds to 10 minutes.
Claim 14
Dependent Claim
99 words
A method of claim 1 which further comprises subjecting the stainless steel to a precoloring treatment in an aqueous solution containing at least one acid selected from the group consisting of sulfuric acid, nitric acid, phosphoric acid, chromic anhydride, potassium dichromate, sodium dichromate and iron salts, nickel salts and manganese salts, in an amount from 10 to 30 g/l for sulfuric, nitric and phosphoric acids, respectively, in an amount from 20 to 500 g/l for chromic anhydride, potassium dichromate and sodium dichromate, respectively, and in an amount from 5 to 200 g/l for iron, nickel and manganese salts, respectively.
Claim 15
Dependent Claim
19 words
A method according to claim 13, in which the pre-coloring treatment is done by immersion in the aqueous solution.
Claim 16
Dependent Claim
19 words
A method according to claim 13, in which the pre-coloring treatment is done by electrolysis in the aqueous solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-30 | 1980-11-29 | 1981-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-30 | 1984-11-29 | 1985-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-30 | 1988-11-29 | 1989-05-31 | $7700.00 | Window Closed / Lapsed |