Method for making investment casting molds for casting of superalloys
Assignee: General Electric Co
•
Filing: 1976-06-23
•
Granted: 1977-05-31
•
Expires: 1996-06-23
Abstract
Abstract A metastable mullite phase is formed in the physical structure of investment casting molds by employing alumina flour of a particle size less than 100 microns.
Inventors
- 👤 Charles D. Greskovich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:41
CPC Classifications
B; B22; B22C; B22C9/00; B22C9/02; B22C9/04
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
194 words
A method for making a shell investment mold comprising the steps of (a) preparing a slurry of a mixture of alumina flour, having an average particle size of less than about 100 microns, and silica of an average particle size less than about 1000A, the composition of the slurry averaging from 65 to 73 weight percent alumina; (b) applying a coating of the slurry mixture to a wax pattern of a predetermined shape of a metal to be cast in the mold; (c) applying a coating of an alumina stucco aggregate on the slurry coating; (d) drying the material of the slurry coating and stucco coating; (e) repeating steps (b), (c) and (d) as often as necessary to apply a predetermined number of layers, disposed one upon the other, of the slurry composition mixture and interdisposed stucco coating on the pattern; (f) removing the pattern from the mold; (g) heating the material composition of the mold to an elevated temperature of from 1700° to 1825° C. in an inert atmosphere for a period of time of up to about 2 hours, and (h) reacting the alumina and silica with each other to form mullite.
Claim 2
Independent Claim
194 words
A method for making a shell investment mold comprising the steps of (a) preparing a slurry of a mixture of alumina flour, having an average particle size of less than about 100 microns, and silica of an average particle size less than about 1000A, the composition of the slurry averaging from 65 to 73 weight percent alumina; (b) applying a coating of the slurry mixture to a wax pattern of a predetermined shape of a metal to be cast in the mold; (c) applying a coating of an alumina stucco aggregate on the slurry coating; (d) drying the material of the slurry coating and stucco coating; (e) repeating steps (b), (c) and (d) as often as necessary to apply a predetermined number of layers, disposed one upon the other, of the slurry composition mixture and interdisposed stucco coating on the pattern; (f) removing the pattern from the mold; (g) heating the material composition of the mold to an elevated temperature of from 1700° to 1825° C. in an inert atmosphere for a period of time of up to about 2 hours, and (h) reacting the alumina and silica with each other to form mullite.
Claim 3
Dependent Claim
60 words
The method of claim 1 wherein the average particle size of the alumina flour is greater than about 10 microns, and heating the material composition forms a microstructure which is one selected from the group consisting of irregular shaped alumina grains in a mixture of an alumina-silica liquid phase and a mullite phase and equiaxed alumina grains surrounded by mullite.
Claim 4
Dependent Claim
87 words
The method of claim 2 wherein the heating of the material is practiced at an elevated temperature range of from 1700° to 1725° C. to form a microstructure of irregular shaped alumina grains in a mixture of an alumina-silica liquid phase and a mullite phase which is a stable mullite phase of an average chemical composition of the stable mullite phase is from about 72 weight percent alumina to about 74 weight percent alumina, balance silica, having a melting point range from about 1825° to 1830° C.
Claim 5
Dependent Claim
52 words
The method of claim 2 wherein the heating of the material is practiced at an elevated temperature range of from about 1800° to 1825° C. to form a microstructure of equiaxed alumina grains surrounded by mullite which is, in part, of the stable mullite phase and, in part, the metastable mullite phase.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein the average particle size of the alumina flour is less than about 10 microns.
Claim 7
Dependent Claim
60 words
The method of claim 5 wherein the heating of the material is practiced at an elevated temperature of about 1725° C. for a period of time of up to about 1 hour to produce a material having a microstructure of equiaxed grains of alumina completely surrounded by a stable mullite phase and a substantial absence of the alumina-silica liquid phase.
Claim 8
Dependent Claim
25 words
The method of claim 6 wherein the average chemical composition of the stable mullite phase is from 72 to 74 weight percent alumina, balance silica.
Claim 9
Dependent Claim
51 words
The method of claim 5 wherein the heating of the material is practiced at an elevated temperature of at least about 1800° C. to produce a material having a microstructure of equiaxed grains of alumina completely surrounded by a metastable mullite phase and a substantial absence of the alumina-silica liquid phase.
Claim 10
Dependent Claim
25 words
The method of claim 8 wherein the average chemical composition of the metastable mullite phase is from 77 to 78 weight percent alumina, balance silica.
Claim 11
Dependent Claim
21 words
The method of claim 7 wherein the elapsed time at the elevated temperature is less than the order of 10 minutes.
Claim 12
Dependent Claim
26 words
The method of claim 6 wherein the heating of the material of the mold is practiced prior to the casting of the metal into the mold.
Claim 13
Dependent Claim
38 words
The method of claim 6 wherein the heating of the material of the mold is practiced simultaneously with a process embodying the casting of a melt of metal in the mold and solidification of the same therein thereafter.
Claim 14
Dependent Claim
25 words
The method of claim 4 wherein the average chemical composition of the metastable mullite phase is from 77 to 78 weight percent alumina, balance silica.
Claim 15
Dependent Claim
42 words
The method of claim 4 wherein the material is heated first at the elevated temperature range of from 1700° to 1725° C. and subsequently, as a separate process step, heated at the elevated temperature range of from about 1800° to 1825° C.
Claim 16
Dependent Claim
21 words
The method of claim 4 wherein the melting point of the metastable mullite phase is of the order of 1900° C.
Claim 17
Dependent Claim
21 words
The method of claim 9 wherein the melting point of the metastable mullite phase is of the order of 1900° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-30 | 1980-11-29 | 1981-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-30 | 1984-11-29 | 1985-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-30 | 1988-11-29 | 1989-05-31 | $7700.00 | Window Closed / Lapsed |