Latex coagulation process using lignin compound
Assignee: Polysar Ltd
•
Filing: 1976-03-08
•
Granted: 1977-05-24
•
Expires: 1996-03-08
Abstract
Abstract Synthetic styrene-conjugated diolefin polymers, e.g. SBR rubbers, are recovered from their aqueous polymerization emulsion by coagulation with acid and a lignin compound. The conventional use of sodium chloride as a coagulant is avoided so as to overcome the problem of sodium chloride in the effluent. By this process of the invention, a rubber crumb of increased porosity is obtained, which is easier to dry.
Inventors
- 👤 Melvin John George Davidson
- 👤 Richard Helmut Wunder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 02:35
CPC Classifications
C; C08; C08C; C08C1/00; C08C1/14; C08C1/16
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
102 words
A process of recovering synthetic styrene-conjugated diolefin polymers from aqueous latex which comprises coagulating the latex, in the substantial absence of sodium chloride, at a temperature of from about 100° F. to about 180° F. in the presence of sufficient sulphuric acid to maintain the pH of coagulation at about 2.5 to about 3.5 and subsequently separating the coagulated polymer from the serum, the improvement being the addition of from about 0.2 to about 5 parts by weight, per 100 parts by weight of dry polymer solids, of a lignin compound selected from powdered lignin, sodium lignate, potassium lignate and ammonium lignate.
Claim 2
Dependent Claim
102 words
A process of recovering synthetic styrene-conjugated diolefin polymers from aqueous latex which comprises coagulating the latex, in the substantial absence of sodium chloride, at a temperature of from about 100° F. to about 180° F. in the presence of sufficient sulphuric acid to maintain the pH of coagulation at about 2.5 to about 3.5 and subsequently separating the coagulated polymer from the serum, the improvement being the addition of from about 0.2 to about 5 parts by weight, per 100 parts by weight of dry polymer solids, of a lignin compound selected from powdered lignin, sodium lignate, potassium lignate and ammonium lignate.
Claim 3
Dependent Claim
38 words
The process of claim 1 in which the lignin compound is added directly to the latex in an amount of from about 0.2 to about 1.5 parts by weight per 100 parts by weight of dry polymer solids.
Claim 4
Dependent Claim
53 words
The process of claim 1 in which at least a portion of the serum is recycled to the latex coagulation step and the lignin compound is added to the recycle serum in an amount of from about 0.5 to about 2 parts by weight per 100 parts by weight of dry polymer solids.
Claim 5
Dependent Claim
46 words
The process of claim 1 in which the coagulation is conducted in the presence of a water soluble polyamine, polyamide or cationic emulsifier in an amount of from about 0.02 parts to about 0.3 parts by weight per 100 parts by weight of dry polymer solids.
Claim 6
Dependent Claim
20 words
The process of claim 1 in which the styrene-conjugated diolefin polymer is a styrene-butadiene rubber optionally containing an extender oil.
References Cited (Backward Citations)
US3821185A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-23 | 1980-11-22 | 1981-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-23 | 1984-11-22 | 1985-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-23 | 1988-11-22 | 1989-05-24 | $7700.00 | Window Closed / Lapsed |