Hydrophilic modified acrylic polymers particularly hydrodispersible or hydrosoluble modified acrylic polymers and method of preparing the same
Assignee: Societe Nationale Elf Aquitaine Production SA
•
Filing: 1975-07-23
•
Granted: 1977-05-24
•
Expires: 1995-07-23
Abstract
Abstract Novel hydrophilic modified acrylic polymers, particularly hydrodispersible or hydrosoluble modified acrylic polymers, containing, expressed in molar percentages, p % units derived from an acrylic acid or ester, q % units derived from an alkanolamide of said acid, r % units derived from the alkanolammonium salt of said acid, and s % units derived from a vinyl monomer, wherein p, q, r, s represent integers so selected that 1≦p≦95, O≦q≦99, O≦r≦99 and O≦s≦40, the sum (p+q+r+s) being equal to 100, and q and r never being nil simultaneously.
Inventors
- 👤 Rene Pornin
- 👤 Jean-Henri Blanc
- 👤 Robert Voirin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:50
CPC Classifications
C; C08; C08F; C08F220/00; C08F220/02; C08F220/04; C08F220/10; C08F220/12; C08F220/52; C08F220/54; C08F220/58; C08F8/00; C08F8/30; C08F8/32; C08F8/44
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
162 words
Novel hydrodispersible or hydrosoluble modified acrylic polymer comprising expressed in molar percentages, p % units A having the formula: ##STR21## q % units B having the formula: ##STR22## r % units C having the formula: ##STR23## and s % units D having the formula: ##STR24## wherein each R stands for hydrogen, methyl or ethyl groups, and R 1 designates hydrogen or an alkyl group containing 1 to 4 carbon atoms, the symbols R and R 1 never representing at the same time an hydrogen atom or a methyl group, i, j and k designate integers comprised between 1 and 6, and α and β, which may be identical or different, are equal to 0 or 1, R 2 represents an hydrogen atom or a methyl group, R 3 designates a monovalent amido, amino, pyridyl or pyrrolidonyl group, and p, 1, r and s represent integers which are so selected that 1≦p≦85, 0≦q≦90, 5≦r≦95 and 0≦s≦30, the sum (p+q+r+s) being equal to 100.
Claim 2
Dependent Claim
162 words
Novel hydrodispersible or hydrosoluble modified acrylic polymer comprising expressed in molar percentages, p % units A having the formula: ##STR21## q % units B having the formula: ##STR22## r % units C having the formula: ##STR23## and s % units D having the formula: ##STR24## wherein each R stands for hydrogen, methyl or ethyl groups, and R 1 designates hydrogen or an alkyl group containing 1 to 4 carbon atoms, the symbols R and R 1 never representing at the same time an hydrogen atom or a methyl group, i, j and k designate integers comprised between 1 and 6, and α and β, which may be identical or different, are equal to 0 or 1, R 2 represents an hydrogen atom or a methyl group, R 3 designates a monovalent amido, amino, pyridyl or pyrrolidonyl group, and p, 1, r and s represent integers which are so selected that 1≦p≦85, 0≦q≦90, 5≦r≦95 and 0≦s≦30, the sum (p+q+r+s) being equal to 100.
Claim 3
Dependent Claim
21 words
Polymer according to claim 1, the molecular weight of which is comprised between 0.2× 10 6 and 100× 10 6 .
Claim 4
Dependent Claim
20 words
Polymer according to claim 1, the molecular weight of which is between 0.4× 10 6 and 50× 10 6 .
Claim 5
Dependent Claim
21 words
Polymer according to claim 3, the molecular weight of which is comprised between 1× 10 6 and 20× 10 6 .
Claim 6
Dependent Claim
9 words
Polymer according to claim 1 wherein s is 0.
Claim 7
Dependent Claim
17 words
Polymer according to claim 5, wherein the molar percentage proportions are such that 5≦p≦80, 2≦q≦80 and 7≦r≦80.
Claim 8
Dependent Claim
61 words
Polymer according to claim 5, wherein the units A comprise at least one radical having the formula: ##STR25## wherein the units B comprise at least one radical having the formula: ##STR26## and wherein the units C comprise at least one radical having the formula: ##STR27## while α and β, which may be identical or different, are equal to 0 or 1.
Claim 9
Dependent Claim
84 words
A method of preparing hydrophilic modified acrylic polymers according to claim 1 comprising the steps of reacting between 50°-150° C. an acrylic polymer which is derived from one or more monomers producing units A, with at least one alkanolamine having the formula: ##STR28## wherein i, j, k represent numbers comprised between 1 and 6, and wherein α and β, which may be identical or different, are equal to 0 or 1, and then separating the thus obtained modified acrylic polymer from the reaction medium.
Claim 10
Dependent Claim
39 words
A method according to claim 8, wherein the amount of alkanolamine reacted with said acrylic polymer is so selected that the molar ratio of said amount of alkanolamine to the amount of polymer is comprised between 0.1 and 15.
Claim 11
Dependent Claim
59 words
A method according to claim 8, wherein the acrylic polymer to be modified is derived from at least one monomer selected from the group consisting of methacrylic and ethylacrylic acids, alkyl acrylates and ethylacrylates the alkyl radical of which contains 1 to 4 carbon atoms, and alkyl methacrylates the alkyl radical of which contains 2 to 4 carbon atoms.
Claim 12
Dependent Claim
20 words
A method according to claim 8, wherein said alkanolamine is selected from the group consisting of monoethanolamine, diethanolamine and triethanolamine.
Claim 13
Dependent Claim
22 words
A method according to claim 8 wherein the monomer producing units A is mixed with at least one monomer producing units D.
Claim 14
Dependent Claim
38 words
A method according to claim 8 wherein the amount of alkanolamine reacted with said acrylic polymer is so selected that the molar ratio of said amount of alkanolamine to the amount of polymer is between 0.3 and 5.
Claim 15
Dependent Claim
39 words
A method according to claim 8, wherein the reaction of alkanolamine with acrylic polymer is carried out in a solvent or diluent, and the acrylic polymer concentration in the solvent or diluent is between 1 and 60% by weight.
Claim 16
Dependent Claim
31 words
A method according to claim 14 wherein the reaction of alkanolamine with said acrylic polymer is performed at a temperature substantially equal to the boiling temperature of said solvent or diluent.
Claim 17
Dependent Claim
17 words
A process according to claim 14 wherein the solvent or diluent is a polar solvent or diluent.
Claim 18
Dependent Claim
17 words
A process according to claim 14 wherein the solvent or diluent is a non-polar solvent or diluent.
Claim 19
Dependent Claim
14 words
A process according to claim 16 wherein the polar solvent or diluent is water.
Claim 20
Dependent Claim
21 words
A method according to claim 18 wherein the acrylic polymer concentration in the water is between 3 and 40% by weight.
Claim 21
Dependent Claim
19 words
A method according to claim 17 wherein said non-polar solvent or diluent is an aliphatic, cycloaliphatic or aromatic hydrocarbon.
Claim 22
Dependent Claim
16 words
A method according to claim 20 wherein said non-polar solvent or diluent is xylene or toluene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-23 | 1980-11-22 | 1981-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-23 | 1984-11-22 | 1985-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-23 | 1988-11-22 | 1989-05-24 | $7700.00 | Window Closed / Lapsed |