Method for manufacture of graphitized hollow spheres and hollow spheres manufactured thereby
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1974-08-05
•
Granted: 1977-05-24
•
Expires: 1994-08-05
Abstract
Abstract Disclosed are graphitized hollow spheres and a method for the manufacture thereof which comprises coating a spherical core of foamed polystyrene with carbonaceous powder and a binder, heating the coated core under controlled conditions to decompose the spherical core of foamed polystyrene, and further heating the resultant carbonaceous body at a high temperature.
Inventors
- 👤 Kazuo Kobayashi
- 👤 Shiroh Ohmori
- 👤 Tetsuhiko Hasuda
- 👤 Minoru Shiraishi
- 👤 Satoshi Arai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:09
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/28; B01J20/28014; B01J20/28016; B01J20/28021; B01J19/00; B01J19/0006; B01J19/002; B01J2/00; B01J2/003; B01J20/02; B01J20/20; B29; B29C; B29C33/00; B29C33/44; B29C33/52; C; C01; C01B; C01B32/00; C01B32/30; C01B32/354; C01B32/382; C02; C02F; C02F1/00; C02F1/68; C02F1/681; C03; C03C; C03C11/00; C04; C04B; C04B28/00; C04B28/02; C04B28/06; C04B35/00; C04B35/01; C04B35/16; C04B35/515; C04B35/52; Y; Y10; Y10S; Y10S376/00; Y10S376/916; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
69 words
Light-weight hollow bodies consisting of shells each defining an empty interior space, the shells consisting of a graphitized carbonaceous substance defining a multiplicity of pores, each of the pores having a relatively large diameter opening facing the empty interior space and being ramified from the opening into a multiplicity of fine pores having smaller diameters than the diameter of the opening, the fine pores opening on the shell surface.
Claim 2
Dependent Claim
69 words
Light-weight hollow bodies consisting of shells each defining an empty interior space, the shells consisting of a graphitized carbonaceous substance defining a multiplicity of pores, each of the pores having a relatively large diameter opening facing the empty interior space and being ramified from the opening into a multiplicity of fine pores having smaller diameters than the diameter of the opening, the fine pores opening on the shell surface.
Claim 3
Independent Claim
226 words
A method for the manufacture of graphitized hollow bodies each defining an empty interior space, which comprises (1) coating spherical cores of foamed polystyrene with a layer of a mixture of at least one carbonaceous substance selected from the group consisting of petroleum coke, pitch coke and carbon black with a binder to form coated spheres having a diameter of 0.5 to 20 mm, (2) heating the coated spheres in an inert gas first to a temperature of 300° C. at a rate increasing by 1° C./minute until each spherical core of foamed polystyrene is melted and decomposed to generate gas and to cause the generated gas to penetrate through the layer and disperse into the ambient atmosphere while the layer forms a shell constituting a hollow body of the carbonaceous substance defining the empty interior space, (a) the gas penetrating through the shell producing a multiplicity of fine through pores, each of the pores having a relatively large diameter opening facing the empty interior space and being ramified from the opening into a multiplicity of fine pores having smaller diameters than the diameter of the opening, the fine pores opening on the outer shell surface, (3) then heating the hollow bodies in nitrogen gas to a temperature of 600° C. at a rate increasing from 300° to 600° C. by 0.5° to 1° C./minute, and
Claim 4
Independent Claim
226 words
A method for the manufacture of graphitized hollow bodies each defining an empty interior space, which comprises (1) coating spherical cores of foamed polystyrene with a layer of a mixture of at least one carbonaceous substance selected from the group consisting of petroleum coke, pitch coke and carbon black with a binder to form coated spheres having a diameter of 0.5 to 20 mm, (2) heating the coated spheres in an inert gas first to a temperature of 300° C. at a rate increasing by 1° C./minute until each spherical core of foamed polystyrene is melted and decomposed to generate gas and to cause the generated gas to penetrate through the layer and disperse into the ambient atmosphere while the layer forms a shell constituting a hollow body of the carbonaceous substance defining the empty interior space, (a) the gas penetrating through the shell producing a multiplicity of fine through pores, each of the pores having a relatively large diameter opening facing the empty interior space and being ramified from the opening into a multiplicity of fine pores having smaller diameters than the diameter of the opening, the fine pores opening on the outer shell surface, (3) then heating the hollow bodies in nitrogen gas to a temperature of 600° C. at a rate increasing from 300° to 600° C. by 0.5° to 1° C./minute, and
Claim 5
Dependent Claim
15 words
(4) thereafter heating the hollow bodies in argon gas to a temperature of 3000° C.
Claim 6
Dependent Claim
15 words
(4) thereafter heating the hollow bodies in argon gas to a temperature of 3000° C.
Claim 7
Dependent Claim
36 words
The method of claim 2, wherein the hollow bodies are heated from 300° to 450° C. at a rate increasing by 0.5° C./minute and from 450° to 600° C. at a rate increasing by 1° C./minute.
Claim 8
Dependent Claim
37 words
The method of claim 2, wherein the binder is composed of at least one member selected from the group consisting of water, starch paste, pitch, tar, spent pulp liquid, aqueous bentonite solution, carboxymethyl cellulose and water glass.
References Cited (Backward Citations)
US2127867A
Cited
US2553759A
Cited
US2627642A
Cited
US2676892A
Cited
US3010177A
Cited
US2987411A
Cited
US3258349A
Cited
US3247294A
Cited
US3470276A
Cited
US3467165A
Cited
US3533961A
Cited
US3591393A
Cited
US3663171A
Cited
US3891574A
Cited
US3953345A
Cited
US3917806A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-23 | 1980-11-22 | 1981-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-23 | 1984-11-22 | 1985-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-23 | 1988-11-22 | 1989-05-24 | $7700.00 | Window Closed / Lapsed |