Catalysis

Claim 2

A process for the oxidation of carbon monoxide or a hydrocarbon present in a gas stream together with uncombined oxygen, to carbon dioxide and water, the process comprising passing the said gas stream at an elevated temperature through a supported catalyst consisting essentially of an inert material, an intermediate coating thereon containing at least one oxide selected from the group consisting of the oxides of scandium, yttrium and the lanthanides and a catalytically active surface coating on said intermediate coating of an alloy selected from the group consisting of platinum/rhodium/base metal alloys wherein the rhodium constitutes 1-50 weight % of the total metal content of the alloy, the base metal from 0.01 to 25 weight % of said total metal content and the platinum the balance, the base metal being selected from the group consisting of aluminium, magnesium, chromium, molybdenum, tungsten, manganese, iron, cobalt, nickel, titanium, vanadium, thorium, uranium, copper, silver, zinc, cadmium, mercury, indium, thallium, bismuth, tin, lead, antimony and neodymium.

Claim 3

A process according to claim 1 wherein the base metal is selected from the group consisting of nickel, cobalt, iron, copper, neodymium, indium, tin, zinc, silver and chromium.

Claim 4

A process according to claim 1 in which the inert material is a unitary porous refractory compound.

Claim 5

A process according to claim 3 in which the refractory compound is selected from the group consisting of oxides of Mg, Ca, Sr, Ba, Al, Sc, Y, the lanthanides, the actinides, Ti, Ga, In, Rl, Si, Zr, Hg, Ge, Sn, Pb, V, Nb, Ta, Cr, Mo, W, U, transition metal cabides, borides and silicides.

Claim 6

A process according to claim 3 in which the refractory compound is in the form of a ceramic material.

Claim 7

A process according to claim 5 in which the catalyst is in the form of a corrugated cellular structure.

Claim 8

A process according to claim 6 in which the corrugated cellular structure is a honeycomb.

Claim 9

A process according to claim 5 in which the ceramic material is selected from the group consisting of zircon-mullite, mullite, alpha alumina, sillimanite, magnesium silicates, zircon, petalite, spodumene, cordierite and alumino silicates.

Claim 10

A process according to claim 6 in which the inert material has applied thereto as a first coating a layer or deposit of a refractory oxide which is unreactive with the said material.

Claim 11

A process according to claim 9 in which the refractory oxide is in the form of a film 0.0004 to 0.001 inches thick.

Claim 12

A process according to claim 9 in which the refractory oxide has a high surface area.

Claim 13

A process according to claim 9 in which the refractory oxide has a large internal pore volume.

Claim 14

A process according to claim 12 in which the refractory oxide is a mixture of at least one oxide selected from the group consisting of oxides of scandium, yttrium and the lanthanides and at least one of the oxides selected from the group consisting of the oxides of Be, Mg, B, Al, Si, Ti, Zr, Hf and Th.

Claim 15

A process according to claim 13 wherein the alloy contains 5 to 45 weight % of rhodium relative to the total metal content.

Claim 16

A process according to claim 14 wherein the alloy contains 35 weight % rhodium.

Claim 17

A process according to claim 1 wherein the base metal is present in an amount of 0.01 to 10 weight % of the total metal content.

Claim 18

A process according to claim 1 in which the supported catalyst comprises: (a) an ultimate inert support material in ceramic honeycomb form; (b) particles of second inert material on said material (a) which is the same or different from the ultimate inert support material coated with; (c) an intermediate refractory oxide coating containing at least one Group IIIA metal oxide selected from the group consisting of oxides of scandium, yttrium and the lanthanides; and (d) a catalytically active metal layer on said coating (c) consisting essentially of a platinumrhodium alloy containing up to 25% by weight of a base metal selected from the group consisting of nickel, cobalt, iron, copper, neodymium, indium, tin, zinc, silver and chromium.

Claim 19

A process according to claim 17 wherein the amount of oxide of scandium, yttrium or lanthanide in the intermediate coating is at least 5 weight % of that coating and the balance is mainly alumina.

Claim 20

A process according to claim 18 wherein the amount of said oxide present in the intermediate coating is 10 weight % of that coating.

Claim 21

A process according to claim 13 in which from 5- 50% by weight of the refractory metal oxide coating consists essentially of a molecular sieve zeolite having its sodium content ion-exchanged by a metal selected from the group consisting of scandium, yttrium and the lanthanides.

Claim 22

A process according to claim 20 in which the sodium content of the xeolite is ion-exchanged by neodymium.

Claim 23

A process according to claim 21 in which the ion-exchanged zeiolite constitutes about 10% by weight of the catalytically active refractory metal oxide.

Claim 24

A process fo the oxidation of carbon monoxide or a hydrocarbon present in a gas stream together with uncombined oxygen to carbon dioxide and water, the process comprising passing the said gas stream at an elevated temperature through a supported catalyst consisting essentially of (1) an inert material which is a unitary porous refractory compound selected from the group consisting of oxides of Mg, Ca, Sr, Ba, Al, Sc, Y, the lanthanides, the actinides, Ti, Ga, In, Rl, Si, Zr, Hg, Ge, Sn, Pb, V, Nb, Ta, Cr, Mo, W, U, transistion metal carbides, borides and silicides; (2) an intermediate coating thereon which is a high surface area refractory oxide having a large internal pore volume, said refractory oxide being a mixture of 5-20% by weight of at least one oxide selected from the group consisting of the oxides of scandium, yttrium and the lanthanides with the balance essentially at least one oxide selected from the group consisting of the oxides of Be, Mg, B, Al, Si, Ti, Zr, Hf and Th; and (3) a catalytically active surface coating on said intermediate coating of an alloy selected from the group consisting of platinum/rhodium/base metal alloys wherein the rhodium constitutes 1-50 weight % of the total metal content of the alloy, the base metal from 0.01 to to 25 weight % of said total metal content and the platinum the balance, the base metal being selected from the group consisting of aluminium, magnesium, chromium, molybdenum, tungsten, manganese, iron, cobalt, nickel, titanium, vanadium, theorium, uranium, copper, silver, zinc, cadmium, mercury, indium, thallium, bismuth, tin, lead, antimony and neodymium.

Claim 25

A process fo the oxidation of carbon monoxide or a hydrocarbon present in a gas stream together with uncombined oxygen to carbon dioxide and water, the process comprising passing the said gas stream at an elevated temperature through a supported catalyst consisting essentially of (1) an inert material which is a unitary porous refractory compound selected from the group consisting of oxides of Mg, Ca, Sr, Ba, Al, Sc, Y, the lanthanides, the actinides, Ti, Ga, In, Rl, Si, Zr, Hg, Ge, Sn, Pb, V, Nb, Ta, Cr, Mo, W, U, transistion metal carbides, borides and silicides; (2) an intermediate coating thereon which is a high surface area refractory oxide having a large internal pore volume, said refractory oxide being a mixture of 5-20% by weight of at least one oxide selected from the group consisting of the oxides of scandium, yttrium and the lanthanides with the balance essentially at least one oxide selected from the group consisting of the oxides of Be, Mg, B, Al, Si, Ti, Zr, Hf and Th; and (3) a catalytically active surface coating on said intermediate coating of an alloy selected from the group consisting of platinum/rhodium/base metal alloys wherein the rhodium constitutes 1-50 weight % of the total metal content of the alloy, the base metal from 0.01 to to 25 weight % of said total metal content and the platinum the balance, the base metal being selected from the group consisting of aluminium, magnesium, chromium, molybdenum, tungsten, manganese, iron, cobalt, nickel, titanium, vanadium, theorium, uranium, copper, silver, zinc, cadmium, mercury, indium, thallium, bismuth, tin, lead, antimony and neodymium.