Method of applying a firmly adherent metallic coating to titanium and titanium alloy
Assignee: Airbus Defence and Space GmbH
•
Filing: 1975-09-02
•
Granted: 1977-05-17
•
Expires: 1995-09-02
Abstract
Abstract A structural part made of titanium and/or titanium alloy is given a surface treatment by sandblasting or chemical pickling and is provided with a protective film of a strong reducing agent such as a solution of a derivative of hydrazine or hydroxylamine which is applied directly over the titanium and immediately thereafter a slide layer of a nickel is applied over the reducing agent layer preferably by spraying. Complex derivatives of hydrazine and hydroxylamine in the form of salts may be applied during a pickling and descaling treatment. The adhesion of the wear-resistant layer of metal is improved by a refining at a temperature of about 300° C to obtain an intermetallic bond between the titanium and nickel at the interfacial boundary.
Inventors
- 👤 Hans-Jurgen Hahn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 05:22
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/14; C; C23; C23C; C23C4/00; C23C4/02; C23C4/04; C23C4/06; C23C4/08; C23C4/18; F16C2220/00; F16C2220/20; F16C2220/60; F16C2223/00; F16C2223/02; F16C2223/08; F16C2223/30; F16C2223/42; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12806
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
87 words
A method of facing a constructional part made of a titanium and/or titanium alloy with a metal coating, comprising subjecting the surface of the titanium or titanium alloy to a reducing agent to form a clean oxide free titanium surface having a protective film thereon, spraying an intermediate layer of nickel over the protective film so as to effect a diffusion of the nickel into the protective film and the surface of the constructional part, and thereafter applying the metal coating over the intermediate layer of nickel.
Claim 2
Independent Claim
87 words
A method of facing a constructional part made of a titanium and/or titanium alloy with a metal coating, comprising subjecting the surface of the titanium or titanium alloy to a reducing agent to form a clean oxide free titanium surface having a protective film thereon, spraying an intermediate layer of nickel over the protective film so as to effect a diffusion of the nickel into the protective film and the surface of the constructional part, and thereafter applying the metal coating over the intermediate layer of nickel.
Claim 3
Dependent Claim
15 words
A method according to claim 1, wherein the reducing agent comprises a derivative of hydrazine.
Claim 4
Dependent Claim
15 words
A method according to claim 1, wherein the reducing agent comprises a derivative of hydroxylamine.
Claim 5
Dependent Claim
39 words
A method according to claim 1, including exposing the surface of the titanium or titanium alloy to a pickling bath which contains the reducing agent so as to clean the surface of titanium and to also descale the surface.
Claim 6
Dependent Claim
29 words
A method according to claim 4, wherein the pickling agent is in the form of a derivative of hydrazine in the form of salts added to the pickling bath.
Claim 7
Dependent Claim
45 words
A method according to claim 1, wherein the adhesion of the metal layer to the constructional part is improved by spraying the nickel layer onto the part at a temperature of about 300° C to effect an intermetallic bond between the titanium and the nickel.
Claim 8
Dependent Claim
15 words
A method according to claim 1, wherein the outer metal layer is applied by spraying.
Claim 9
Independent Claim
116 words
A method of facing a constructional part made of titanium and/or titanium alloy, comprising subjecting the constructional part to a surface treatment by sandblasting or chemical pickling, in order to clean the surface, immediately after the cleaning, spraying the constructional part with a solution of unsymmetrical dimethyl-hydrazine in dioxan to form a continuous, thin protective film on the surface of the part, preventing any oxidation of the exposed metal surface to air action for at least three minutes and during this three minutes, applying a nickel layer by spraying to form an intermediate sliding layer, thereafter without delay, applying a layer of the metal coating to be applied by spraying on the still hot constructional part.
Claim 10
Independent Claim
116 words
A method of facing a constructional part made of titanium and/or titanium alloy, comprising subjecting the constructional part to a surface treatment by sandblasting or chemical pickling, in order to clean the surface, immediately after the cleaning, spraying the constructional part with a solution of unsymmetrical dimethyl-hydrazine in dioxan to form a continuous, thin protective film on the surface of the part, preventing any oxidation of the exposed metal surface to air action for at least three minutes and during this three minutes, applying a nickel layer by spraying to form an intermediate sliding layer, thereafter without delay, applying a layer of the metal coating to be applied by spraying on the still hot constructional part.
Claim 11
Dependent Claim
38 words
A method according to claim 8, wherein the metal part which is sprayed over the nickel layer is porous and including impregnating the metal coating in a vacuum at 50° C with an oil comprising a high-pressure additive.
Claim 12
Dependent Claim
28 words
A method according to claim 8, wherein the slide layer is applied together with solid lubricants in the form of molybdenum disulfide or graphite which is sintered in.
References Cited (Backward Citations)
US2257186A
Cited
US2935428A
Cited
US2833668A
Cited
US3505181A
Cited
US3339271A
Cited
US3553015A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-16 | 1980-11-15 | 1981-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-16 | 1984-11-15 | 1985-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-16 | 1988-11-15 | 1989-05-17 | $7700.00 | Window Closed / Lapsed |