Method of manufacturing a porous carbon body
Assignee: US Philips Corp
•
Filing: 1975-11-10
•
Granted: 1977-05-17
•
Expires: 1995-11-10
Abstract
Abstract A foamed synthetic body is impregnated with a resin which can be converted into vitreous carbon by heating, after which by raising the temperature the body is dried and the resin is hardened, after which, if desired, one or more surfaces of the body are again treated with the impregnating agent and the body is then carbonized by further rise in temperature. In order to ensure that the foamed synthetic body remains stable during the whole preparation, the body is soaked with liquid epoxide resin or an aqueous polyvinyl alcohol solution before impregnation.
Inventors
- 👤 Bernhard Lersmacher
- 👤 Siegfried Nerche
- 👤 Karlheinz Schelhas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:24
CPC Classifications
C; C03; C03B; C03B40/00; B; B32; B32B; B32B15/00; B32B15/04; B32B15/046; B32B15/18; B32B5/00; B32B5/18; C03B40/005; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/524; C08; C08J; C08J9/00; C08J9/26; C08J9/36; C08J9/40; C08J9/42; B32B2266/00; B32B2266/04; C08J2201/00; C08J2201/04; C08J2201/046; C08J2363/00; C08J2375/00; C08J2375/04; C08J2463/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
93 words
In the method of forming a porous carbon body wherein a foamed polyurethane body is first impregnated with a resin convertable to vitreous carbon upon heating and the resultant impregnated foamed body is first heated to drying, further heated to a temperature sufficiently high to harden the body and then heated to a temperature sufficiently high to cause the resultant impregnated polyurethane foamed body to be carbonized, the improvement wherein prior to the step of impregnation the foamed polyurethane body is soaked with a liquid epoxide resin or an aqueous polyvinyl alcohol solution.
Claim 2
Dependent Claim
93 words
In the method of forming a porous carbon body wherein a foamed polyurethane body is first impregnated with a resin convertable to vitreous carbon upon heating and the resultant impregnated foamed body is first heated to drying, further heated to a temperature sufficiently high to harden the body and then heated to a temperature sufficiently high to cause the resultant impregnated polyurethane foamed body to be carbonized, the improvement wherein prior to the step of impregnation the foamed polyurethane body is soaked with a liquid epoxide resin or an aqueous polyvinyl alcohol solution.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein epoxide resin is employed in a solvent capable at most of having only a slight solvent effect on the foamed polyurethane body.
Claim 4
Dependent Claim
24 words
The method of claim 1 wherein, after hardening, at least one surface of the body is treated with the resin convertable to vitreous carbon.
Claim 5
Dependent Claim
32 words
A method as claimed in claim 1, characterized in that the foamed polyurethane body is soaked with an aqueous polyvinyl alcohol solution containing from 1 to 10% by weight of polyvinyl alcohol.
Claim 6
Dependent Claim
36 words
A method as claimed in claim 4, characterized in that the polyvinyl alcohol is dissolved in water which is heated to 80° to 90° C and the polyurethane foamed body is soaked with said hot solution.
Claim 7
Dependent Claim
23 words
A method as claimed in claim 5, characterized in that the polyurethane foamed body is internally wetted with polyvinyl alcohol solution before soaking.
References Cited (Backward Citations)
US3387940A
Cited
US3446593A
Cited
US3666526A
Cited
NL6815254A
Cited
US3574548A
Cited
US3922334A
Cited
US3927186A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-16 | 1980-11-15 | 1981-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-16 | 1984-11-15 | 1985-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-16 | 1988-11-15 | 1989-05-17 | $7700.00 | Window Closed / Lapsed |