Coloring methods for aluminum and aluminum alloys
Assignee: Honny Chemicals Co Ltd
•
Filing: 1975-01-23
•
Granted: 1977-05-17
•
Expires: 1995-01-23
Abstract
Abstract A method for coloring aluminum and aluminum alloys comprising passing an alternating current from the article of aluminum or aluminum alloys having an oxidized film thereon through an aqueous solution of one or more salts of one or more metals of Group VIII of the periodic table, and thereafter passing a direct current through an aqueous solution of electrolyte utilizing the aluminum material as the anode wherein said solution may have a conductivity of more than 10 μΩ - 1 cm - 1 , be the same as the one used when employing the alternating current or contain a water-soluble resin. The electrolyte is free of added acid.
Inventors
- 👤 Shoji Yoshida
- 👤 Yoshizo Ito
- 👤 Yoshihiro Sakasita
- 👤 Tatsuhiko Kobata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 04:02
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/18; C25D11/20; C25D11/22; C25D13/00; C25D13/20
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
122 words
In a method of coloring articles of aluminum and aluminum alloys which comprises passing for from 2 to 30 minutes an alternating current at up to 30 volts from the article of aluminum or aluminum alloys having an oxidized film thereon through an aqueous solution containing Group 8 metal salts at a temperature of from 5- 40° C. and then passing direct current at from 10-200 volts for from 0.5 to 10 minutes with the aluminum material article acting as an anode through an aqueous solution of electrolyte the improvement which comprises rendering said aqueous solution containing metal salts devoid of added acids and/or salts of metals thereof where they are other than Group 8 metals to form a uniformly colored article.
Claim 2
Dependent Claim
122 words
In a method of coloring articles of aluminum and aluminum alloys which comprises passing for from 2 to 30 minutes an alternating current at up to 30 volts from the article of aluminum or aluminum alloys having an oxidized film thereon through an aqueous solution containing Group 8 metal salts at a temperature of from 5- 40° C. and then passing direct current at from 10-200 volts for from 0.5 to 10 minutes with the aluminum material article acting as an anode through an aqueous solution of electrolyte the improvement which comprises rendering said aqueous solution containing metal salts devoid of added acids and/or salts of metals thereof where they are other than Group 8 metals to form a uniformly colored article.
Claim 3
Dependent Claim
32 words
The method of claim 1 in which the aqueous solution of electrolyte through which the direct current is passed is an aqueous solution of more than 10 μΩ.sup. -1 cm.sup. -1 conductivity.
Claim 4
Dependent Claim
19 words
The method of claim 2 in which the pH of the solution of electrolyte is from 2 to 11.
Claim 5
Dependent Claim
24 words
The method of claim 2 in which the article colored by the previous treatment is coated with resin after the passage of direct current.
Claim 6
Dependent Claim
32 words
The method of claim 1 in which the aqueous solution of electrolyte through which the direct current is passed is the same solution as that through which the alternating current is passed.
Claim 7
Dependent Claim
24 words
The method of claim 5 in which the article colored by the previous treatment is coated with resin after the passage of direct current.
Claim 8
Dependent Claim
29 words
The method of claim 1 in which the aqueous solution of electrolyte through which the direct current is passed is a dispersion, emulsion or aqueous solution containing water-soluble resins.
Claim 9
Dependent Claim
62 words
The method of claim 7 in which the direct current is passed through an aqueous solution of electrolyte containing a water-soluble, emulsion or dispersion of resin which is selected from acrylic, alkyd, acrylic-alkyd, epoxy and phenolic resins, reaction products of such resins with organic amines or ammonium hydroxide, a mixture of said resins and a mixture of said resins with melamine resins.
Claim 10
Dependent Claim
25 words
The method of claim 1 in which the temperature of the solution through which the alternating current is passed is from 10° to 35° C.
Claim 11
Dependent Claim
19 words
The method of claim 1 in which the voltage of the alternating current is from 5 to 25 volts.
Claim 12
Dependent Claim
30 words
The method of claim 1 in which the total concentration of salt(s) of metal(s) in the solution through which the alternating current is passed is from 0.5 to 15 wt.%.
Claim 13
Dependent Claim
154 words
In a method of coloring articles of aluminum and aluminum alloys which comprises passing for from 2 to 30 minutes an alternating current at up to 30 volts from the article of aluminum or aluminum alloys having an oxidized film thereon through an aqueous solution containing group 8 salts at a temperature of from 5°-40° C. and then passing direct current at from 50-300 volts for from 0.5 to 5 minutes with the aluminum material article acting as an anode through an aqueous solution of electrolyte containing a water-soluble resin having a temperature of from 10° to 30° C. and a pH of from 7.5 to 10.5, said electrolyte having a concentration of resin of from 3 to 4 wt.%, the improvement which comprises rendering said aqueous solution containing metal salts devoid of added acids and/or salts of metals thereof where they are other than Group 8 metals to form a uniformly colored article.
Claim 14
Dependent Claim
154 words
In a method of coloring articles of aluminum and aluminum alloys which comprises passing for from 2 to 30 minutes an alternating current at up to 30 volts from the article of aluminum or aluminum alloys having an oxidized film thereon through an aqueous solution containing group 8 salts at a temperature of from 5°-40° C. and then passing direct current at from 50-300 volts for from 0.5 to 5 minutes with the aluminum material article acting as an anode through an aqueous solution of electrolyte containing a water-soluble resin having a temperature of from 10° to 30° C. and a pH of from 7.5 to 10.5, said electrolyte having a concentration of resin of from 3 to 4 wt.%, the improvement which comprises rendering said aqueous solution containing metal salts devoid of added acids and/or salts of metals thereof where they are other than Group 8 metals to form a uniformly colored article.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-16 | 1980-11-15 | 1981-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-16 | 1984-11-15 | 1985-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-16 | 1988-11-15 | 1989-05-17 | $7700.00 | Window Closed / Lapsed |