Titanium clad steel and process for making
Assignee: Lukens Inc
•
Filing: 1976-06-14
•
Granted: 1977-05-17
•
Expires: 1996-06-14
Abstract
Abstract A nickel innerlayer is sandwiched between a steel plate and a titanium plate in a steel assembly, the assembly being hermetically sealed and reduced in a hot rolling operation which results in a metallurgical bond with greatly improved ductility as measured by bending and shear tests. The nickel layer contains not more than 0.03 percent carbon and not less than about 0.05 percent of a carbide former in a ratio of between about 4-35 of carbide former to one of carbon.
Inventors
- 👤 Stephen Lewis Morse
- 👤 James J. McGlynn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:01
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/001; B23K20/00; B23K20/16; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/923; Y10S428/924; Y10S428/926; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12937; Y10T428/12944
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
172 words
A method for producing a titanium clad steel which comprises the steps of providing: a first plate of carbon steel; providing a second plate of nickel containing nor more than 0.03% carbon and not less than about 0.05% of a carbide former which where higher than said minimum of 0.05% is in a ratio of about 4-35 of carbide former to 1 of carbon; providing a third plate of titanium and sandwiching said second plate in a face-to-face contact between said first and third plates into an assembly, hermetically sealing at least second plate within said assembly, heating said assembly to a temperature of about 1650° - 1700° F., and rolling said assembly at said temperature sufficiently to produce a metallurgical bond between said plates which is characterized by a high relative ductility whereby specimens rolled to 1/2 inch gauge in the as-rolled condition may be bent with the titanium in compression or tension or both in side bends without bond cracking or separation to a one-half inch interior diameter and 180°.
Claim 2
Independent Claim
172 words
A method for producing a titanium clad steel which comprises the steps of providing: a first plate of carbon steel; providing a second plate of nickel containing nor more than 0.03% carbon and not less than about 0.05% of a carbide former which where higher than said minimum of 0.05% is in a ratio of about 4-35 of carbide former to 1 of carbon; providing a third plate of titanium and sandwiching said second plate in a face-to-face contact between said first and third plates into an assembly, hermetically sealing at least second plate within said assembly, heating said assembly to a temperature of about 1650° - 1700° F., and rolling said assembly at said temperature sufficiently to produce a metallurgical bond between said plates which is characterized by a high relative ductility whereby specimens rolled to 1/2 inch gauge in the as-rolled condition may be bent with the titanium in compression or tension or both in side bends without bond cracking or separation to a one-half inch interior diameter and 180°.
Claim 3
Dependent Claim
21 words
A method in accordance with claim 1, wherein the reduction to assembly achieved by said rolling is about 3 to 1.
Claim 4
Dependent Claim
21 words
A method in accordance with claim 1, wherein said carbide former is selected from a group consisting of titanium and columbium.
Claim 5
Dependent Claim
27 words
A method in accordance with claim 1, wherein said nickel plate is rolled within the said assembly to a thickness of not less than one thirty-second inch.
Claim 6
Dependent Claim
140 words
A titanium clad steel which is comprised of three layers which are metallurgically bonded together by rolling at a temperature of about 1650° to 1700° F., said three layers consisting essentially of a first layer of steel, a second layer of nickel and a third layer of titanium, said nickel layer containing not more than 0.03% carbon and not less than about 0.05% of a carbide former which where it is higher than said minimum of said 0.05% is in ratio of about 4-35 of carbide former to 1 of carbon, said titanium clad steel being characterized by high relative ductility whereby specimens rolled to 1/2 inch gauge in the as-rolled condition may be bent with the titanium in compression or tension or both in side bends without bond cracking or separation to a one-half inch interior diameter and 180°.
Claim 7
Dependent Claim
140 words
A titanium clad steel which is comprised of three layers which are metallurgically bonded together by rolling at a temperature of about 1650° to 1700° F., said three layers consisting essentially of a first layer of steel, a second layer of nickel and a third layer of titanium, said nickel layer containing not more than 0.03% carbon and not less than about 0.05% of a carbide former which where it is higher than said minimum of said 0.05% is in ratio of about 4-35 of carbide former to 1 of carbon, said titanium clad steel being characterized by high relative ductility whereby specimens rolled to 1/2 inch gauge in the as-rolled condition may be bent with the titanium in compression or tension or both in side bends without bond cracking or separation to a one-half inch interior diameter and 180°.
Claim 8
Dependent Claim
28 words
A titanium clad steel in accordance with claim 5, wherein said carbide former is from the group consisting of titanium, columbium, zirconium, vanadium, tantalum, chromium, molybdenum, and tungsten.
Claim 9
Dependent Claim
23 words
A titanium clad steel plate in accordance with claim 6, wherein said carbide former is from the group consisting of titanium and columbium.
Claim 10
Dependent Claim
26 words
A titanium clad steel plate in accordance with claim 5, wherein the minimum thickness of said nickel layer in the as-rolled condition is one thirty-second inch.
Claim 11
Dependent Claim
27 words
A titanium clad steel plate in accordance with claim 5 being characterized by an average shear strength at the titanium/nickel interface of in excess of 25,000 psi.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-16 | 1980-11-15 | 1981-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-16 | 1984-11-15 | 1985-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-16 | 1988-11-15 | 1989-05-17 | $7700.00 | Window Closed / Lapsed |