US4022875A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for the preparation of vitreous carbon foams
Assignee: Chemotronics International Inc
•
Filing: 1975-11-24
•
Granted: 1977-05-10
•
Expires: 1995-11-24
Abstract
Abstract A rapid method for forming vitreous carbon foams from flexible polyurethane foams having membranes dividing contiguous cells, which faithfully reproduces the geometry of the uncarbonized polyurethane foams, by infusing the polyurethane foams with substantially unresinified or unpolymerized furfuryl alcohol which is capable of resinification at temperatures above room temperature is described. An important step in the method which permits rapid carbonization without cracking and which is essential to faithful foam geometry reproduction is the substantial removal of the liquid non-infused furfuryl alcohol from the polyurethane foam surfaces after the infusion or swelling step. The carbonized foam is in the form of vitreous, disordered or glassy carbon and is particularly useful for corrosive and/or high temperature applications such as insulation, corrosion resistant chemical processing components and the like.
Inventors
- 👤 Clarence S. Vinton
- 👤 Charles H. Franklin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 19:41
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/524; C04B38/00; C04B38/0022
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
178 words
The method for forming a vitreous carbon foam which comprises: a. infusing an unreticulated flexible polyurethane foam with substantially unresinified but resinifiable furfuryl alcohol so as to cause the foam to swell by infusion of the furfuryl alcohol; b. removing substantially all of the non-infused furfuryl alcohol from within the cells and from the surfaces of the foam; c. resinifying the furfuryl alcohol in the foam to form a thermoset resin wherein the infusing, removing of the excess and resinifying of the furfuryl alcohol produces a resulting weight up to about six times the weight of the foam alone; d. carbonizing the foam under neutral, non-oxidizing or reducing gas or vacuum conditions in an oven which rapidly heats the foam to a temperature sufficient to obtain carbonization, thereby allowing crack-free carbonization to be achieved in less than about 5 hours at a rate of temperature change which causes cracking of the foam when substantial resinified furfuryl alcohol remains on the surfaces; and, e. producing the crack-free vitreous carbon foam with a shape corresponding to the unreticulated polyurethane foam.
Claim 2
Independent Claim
178 words
The method for forming a vitreous carbon foam which comprises: a. infusing an unreticulated flexible polyurethane foam with substantially unresinified but resinifiable furfuryl alcohol so as to cause the foam to swell by infusion of the furfuryl alcohol; b. removing substantially all of the non-infused furfuryl alcohol from within the cells and from the surfaces of the foam; c. resinifying the furfuryl alcohol in the foam to form a thermoset resin wherein the infusing, removing of the excess and resinifying of the furfuryl alcohol produces a resulting weight up to about six times the weight of the foam alone; d. carbonizing the foam under neutral, non-oxidizing or reducing gas or vacuum conditions in an oven which rapidly heats the foam to a temperature sufficient to obtain carbonization, thereby allowing crack-free carbonization to be achieved in less than about 5 hours at a rate of temperature change which causes cracking of the foam when substantial resinified furfuryl alcohol remains on the surfaces; and, e. producing the crack-free vitreous carbon foam with a shape corresponding to the unreticulated polyurethane foam.
Claim 3
Independent Claim
192 words
The method of forming a vitreous carbon foam which comprises: a. infusing an unreticulated flexible polyurethane foam with substantially unresinified but resinifiable furfuryl alcohol so as to cause the foam to swell by infusion of the furfuryl alcohol; b. removing substantially all of the non-infused furfuryl alcohol from within the cells and from the surfaces of the foam; c. resinifying the furfuryl alcohol in the foam to form a resinified, thermoset and hardened structure wherein the infusing, excess removing and resinifying of the furfuryl alcohol produces a resulting weight up to about six times the weight of the foam alone; d. heating the resinified hardened pretreated foam under neutral, non-oxidizing or reducing gas or vacuum conditions in an oven which rapidly heats the foam to a temperature of at least about 500° C so as to form a vitreous carbon structure, whereby crack-free carbonization is achieved in less than about 5 hours at a rate of temperature change of the structure which causes cracking of pretreated foam with non-infused thermoset furan resin coated on the surfaces; and e. producing the crack-free carbon foam with a shape corresponding to the unreticulated polyurethane foam.
Claim 4
Independent Claim
192 words
The method of forming a vitreous carbon foam which comprises: a. infusing an unreticulated flexible polyurethane foam with substantially unresinified but resinifiable furfuryl alcohol so as to cause the foam to swell by infusion of the furfuryl alcohol; b. removing substantially all of the non-infused furfuryl alcohol from within the cells and from the surfaces of the foam; c. resinifying the furfuryl alcohol in the foam to form a resinified, thermoset and hardened structure wherein the infusing, excess removing and resinifying of the furfuryl alcohol produces a resulting weight up to about six times the weight of the foam alone; d. heating the resinified hardened pretreated foam under neutral, non-oxidizing or reducing gas or vacuum conditions in an oven which rapidly heats the foam to a temperature of at least about 500° C so as to form a vitreous carbon structure, whereby crack-free carbonization is achieved in less than about 5 hours at a rate of temperature change of the structure which causes cracking of pretreated foam with non-infused thermoset furan resin coated on the surfaces; and e. producing the crack-free carbon foam with a shape corresponding to the unreticulated polyurethane foam.
Claim 5
Dependent Claim
13 words
The method of claim 2 wherein the catalyst for resinification is oxalic acid.
Claim 6
Independent Claim
170 words
The method for forming a vitreous carbon foam which comprises: a. infusing a flexible unreticulated polyurethane foam with substantially unresinified furfuryl alcohol which is resinifiable in situ so as to cuase the foam to swell by infusion of the furfuryl alcohol; b. removing substantially all of the non-infused furfuryl alcohol from within the cells and from the surfaces of the foam wherein the infusing and removing of the non-infused furfuryl alcohol would produce upon curing an infused foam weight of up to about six times the weight of the foam alone; c. carbonizing the infused foam under neutral, nonoxidizing or reducing gas or vacuum conditions in an oven which rapidly heats the foam to a temperature sufficient to obtain carbonization, thereby allowing crack-free carbonization to be achieved in less than about five hours at a rate of temperature change which causes cracking of the foam when resinifiable furfuryl alcohol remains on the surfaces; and d. producing the crack-free vitreous carbon foam with a shape corresponding to the unreticulated polyurethane foam.
Claim 7
Independent Claim
170 words
The method for forming a vitreous carbon foam which comprises: a. infusing a flexible unreticulated polyurethane foam with substantially unresinified furfuryl alcohol which is resinifiable in situ so as to cuase the foam to swell by infusion of the furfuryl alcohol; b. removing substantially all of the non-infused furfuryl alcohol from within the cells and from the surfaces of the foam wherein the infusing and removing of the non-infused furfuryl alcohol would produce upon curing an infused foam weight of up to about six times the weight of the foam alone; c. carbonizing the infused foam under neutral, nonoxidizing or reducing gas or vacuum conditions in an oven which rapidly heats the foam to a temperature sufficient to obtain carbonization, thereby allowing crack-free carbonization to be achieved in less than about five hours at a rate of temperature change which causes cracking of the foam when resinifiable furfuryl alcohol remains on the surfaces; and d. producing the crack-free vitreous carbon foam with a shape corresponding to the unreticulated polyurethane foam.
Claim 8
Dependent Claim
21 words
The method of claim 4 wherein the infused resinifiable furfuryl alcohol is simultaneously cured during the first part of the carbonization.
References Cited (Backward Citations)
CA660107A
Cited
US3121050A
Cited
US3111396A
Cited
US3302999A
Cited
US3387940A
Cited
US3446593A
Cited
US3345440A
Cited
US3778336A
Cited
US3531248A
Cited
US3574548A
Cited
US3857913A
Cited
US3927186A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-09 | 1980-11-08 | 1981-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-09 | 1984-11-08 | 1985-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-09 | 1988-11-08 | 1989-05-10 | $7700.00 | Window Closed / Lapsed |