US4022858A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for the production of foamed thermoplastic film having improved resiliency and flexibility characteristics
Assignee: Mobil Oil AS
•
Filing: 1974-12-26
•
Granted: 1977-05-10
•
Expires: 1994-12-26
Abstract
Abstract Improvements in the production of foam form film or sheeting plastic products in order to increase the flexibility characteristics thereof by reducing the size of the voids and increasing the number of voids therein without substantially changing the bulk density, production rate or product size and by reducing the rate at which such foamed products solidify after formation.
Inventors
- 👤 Anthony John Cavanna
- 👤 Edward Armando Colombo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:34
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; B; B29; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/507; B29L; B29L2023/00; Y; Y10; Y10S; Y10S264/00; Y10S264/04; Y10S264/05; Y10S264/13; Y10S521/00; Y10S521/908
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
149 words
In a process for the production of thermoplastic foamed film or sheeting by plastifying a thermoplastic resin, blending such with a nucleating agent and a foaming agent, extruding such blend in the form of tubular film of sheeting while simultaneously foaming said film or sheeting, and cooling said foamed tubular film or sheeting to an extent sufficient to stabilize said foamed tubular film or sheeting; the improvement, whereby increasing the flexural characteristic of said foamed tubular film or sheeting, and products made therefrom which comprises utilizing about 0.4 to 0.6 parts by weight of said nucleating agent per 100 parts of said resin, and cooling said foamed tubular film or sheeting at a rate of about 500 to 600 BTU per minute, whereby providing about 25 to 55 void cells per 4in 2 of said foamed tubular film or sheeting, when viewed in two dimensions at 100 times magnification.
Claim 2
Dependent Claim
149 words
In a process for the production of thermoplastic foamed film or sheeting by plastifying a thermoplastic resin, blending such with a nucleating agent and a foaming agent, extruding such blend in the form of tubular film of sheeting while simultaneously foaming said film or sheeting, and cooling said foamed tubular film or sheeting to an extent sufficient to stabilize said foamed tubular film or sheeting; the improvement, whereby increasing the flexural characteristic of said foamed tubular film or sheeting, and products made therefrom which comprises utilizing about 0.4 to 0.6 parts by weight of said nucleating agent per 100 parts of said resin, and cooling said foamed tubular film or sheeting at a rate of about 500 to 600 BTU per minute, whereby providing about 25 to 55 void cells per 4in 2 of said foamed tubular film or sheeting, when viewed in two dimensions at 100 times magnification.
Claim 3
Dependent Claim
34 words
The improved process claimed in claim 1 wherein said resin is a styrene polymer and said foamed tubular film or sheeting has a bulk density of about 3.5 to 20 pounds per cubic foot.
Claim 4
Dependent Claim
37 words
The improved process claimed in claim 2 wherein said nucleating agent is a mixture of sodium bicarbonate and citric acid wherein the citric acid is present to the extent of 76% by weight of the sodium bicarbonate.
Claim 5
Dependent Claim
73 words
The improved process claimed in claim 2 including plastifying said styrene polymer at about 400° to 500° F, mixing said plastisized polymer with blowing and nucleating agents to form a blend, cooling said blend by transferring said blend to a second extruder and extruding said blend in the form of foamed tubular film or sheeting under ambient atmospheric conditions which are lower in both temperature and pressure than the conditions of said blending.
Claim 6
Dependent Claim
66 words
The improved process claimed in claim 2 wherein said extruded foamed tubular film or sheeting is passed about a mandrel having a length to diameter ratio of about 4 to 5 and passing water at about 60° to 75° F through said mandrel at a rate of about 7 to 15 gallons per minute sufficient to cool and dimensionally stabilize said foamed tubular film or sheeting.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-09 | 1980-11-08 | 1981-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-09 | 1984-11-08 | 1985-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-09 | 1988-11-08 | 1989-05-10 | $7700.00 | Window Closed / Lapsed |