Manufacture of cement in rotary vessels

Claim 2

In a continuous process for the manufacture of cement clinker comprising: introducing unsintered cement raw materials comprising calcium carbonate containing material, silica containing material and alumina containing material into an inclined rotary vessel comprising a plurality of treatment zones including a calcination zone and a clinkering zone; heating said raw materials in said calcination zone under conditions of agitation due to the rotation of said vessel at calcination temperatures generally ranging from about 1000° to about 2000° F, said calcination temperatures being below the temperature of insipient fusion of said cement materials to effect thermal decomposition of calcium carbonate with evolution of carbon dioxide; continuously transferring calcined material from said calcination zone into said clinkering zone; heating said calcined material in said clinkering zone at sintering temperatures generally ranging from about 2300° to about 2900° F, said sintering temperatures being at or above the temperature of insipient fusion of said cement materials to effect clinkering; said heating in said rotary vessel being effected at least in part by the combustion of fuel within the gaseous atmosphere of said vessel; the improvement comprising incorporating into said cement raw materials introduced into said rotary vessel particulate residual fuels having a volatiles content not more than about 40%, an ignition temperature of the non-volatile portion of from about 750° to about 1500° F, and an ash content of less than about 30% to provide from about 5 to about 75% of the heat required for said process in said rotary vessel, said volatiles content and said non-volatiles ignition temperature of said residual fuels being such that the principal oxidation of said residual fuels occurs in the calcination zone.

Claim 3

The process of claim 1 wherein said residual fuel has a volatiles content of not more than about 20%.

Claim 4

The process of claim 2 wherein said residual fuel has a volatiles content of not more than about 10%.

Claim 5

The process of claim 1 wherein said residual fuel has an ash content of less than about 10%.

Claim 6

The process of claim 1 wherein the non-volatile portion of said residual fuel has an agitation temperature of from about 1000° to about 1500° F.

Claim 7

The process of claim 1 wherein said residual fuel provides from about 30 to about 50% of the heat required for the process.

Claim 8

The process of claim 6 wherein said inclined rotary vessel is a dry process rotary cement kiln.

Claim 9

The process of claim 1 wherein said cement raw materials and the exhaust gases from said inclined rotary vessel are passed through a suspension preheater system prior to introduction of the cement saw materials into said inclined rotary vessel to recover useful heat from the exhaust gases.

Claim 10

The process of claim 1 wherein said residual fuel is coke.

Claim 11

The process of claim 9 wherein said residual fuel is petroleum coke.

Claim 12

The process of claim 1 wherein said residual fuel is char.

Claim 13

The process of claim 1 wherein said residual fuel is coal gasification residue.

Claim 14

The process of claim 1 wherein said residual fuel is coal.

Claim 15

The process of claim 13 wherein said coal is anthracite.

Claim 16

Th process of claim 1 wherein at least a portion of said residual fuel is added in the calcining zone of the rotary vessel.

Claim 17

The process of claim 1 wherein all of said residual fuel is introduced into the kiln with the raw materials.

Claim 18

The process of claim 1 wherein a level of uncombined oxygen of from about 0.5 to about 5.0% is maintained in exhaust gases exiting from the inclined rotary vessel.

Claim 19

The process of claim 17 wherein the level of uncombined oxygen in the exhaust gases lies in the range from about 0.5 to about 2.0%.

Claim 20

The process of claim 1 wherein the particle size of said residual fuel lies in the range from about 8 U.S. screen mesh size to about 325 U.S. screen mesh size.

Claim 21

The process of claim 19 wherein the minimum particle size of said residual fuel is greater than about 200 U.S. screen mesh size.

Claim 22

The process of claim 19 wherein the maximum particle size of said residual fuel is less than about 20 U.S. screen mesh size.

Claim 23

The process of claim 1 wherein said residual fuel provides from about 5 to about 60% of the heat required for the process.

Claim 24

The process of claim 22 wherein the non-volatile portion of the residual fuel has an ignition temperature of from about 1000° to about 1500° F.

Claim 25

In a continuous process for the manufacture of cement clinker comprising: introducing unsintered cement raw materials comprising calcium carbonate containing material, silica containing material and alumina containing material into an inclined rotary vessel comprising a plurality of treatment zones including a calcination zone and a clinkering zone; heating said raw materials in said calcination zone under conditions of agitation due to the rotation of said vessel at calcination temperatures generally ranging from about 1000° to about 2000° F, said calcination temperatures being below the temperature of insipient fusion of said cement materials to effect thermal decomposition of calcium carbonate with evolution of carbon dioxide; continuously transferring calcined material from said calcination zone into said clinkering zone; heating said calcined material in said clinkering zone at sintering temperatures generally ranging from about 2300° to about 2900° F, said sintering temperatures being at or above the temperature of insipient fusion of said cement materials to effect clinkering; said heating in said rotary vessel being effected at least in part by the combustion of fuel within the gaseous atmosphere of said vessel; the improvement comprising incorporating into said cement raw materials introduced into said rotary vessel particulate residual fuels having a volatiles content not more than about 40%, the ignition temperature of the non-volatile portion being greater than the temperature reached prior to the calcining zone and less than about 1500° F; said residual fuel having an ash content of less than about 30% to provide at least 5% of the heat required for said process in said rotary vessel, said volatiles content and said non-volatiles ignition temperature of said residual fuels being such that oxidation of the residual fuels occurs primarily in the calcination zone.

Claim 26

In a continuous process for the manufacture of cement clinker comprising: introducing unsintered cement raw materials comprising calcium carbonate containing material, silica containing material and alumina containing material into an inclined rotary vessel comprising a plurality of treatment zones including a calcination zone and a clinkering zone; heating said raw materials in said calcination zone under conditions of agitation due to the rotation of said vessel at calcination temperatures generally ranging from about 1000° to about 2000° F, said calcination temperatures being below the temperature of insipient fusion of said cement materials to effect thermal decomposition of calcium carbonate with evolution of carbon dioxide; continuously transferring calcined material from said calcination zone into said clinkering zone; heating said calcined material in said clinkering zone at sintering temperatures generally ranging from about 2300° to about 2900° F, said sintering temperatures being at or above the temperature of insipient fusion of said cement materials to effect clinkering; said heating in said rotary vessel being effected at least in part by the combustion of fuel within the gaseous atmosphere of said vessel; the improvement comprising incorporating into said cement raw materials introduced into said rotary vessel particulate residual fuels having a volatiles content not more than about 40%, the ignition temperature of the non-volatile portion being greater than the temperature reached prior to the calcining zone and less than about 1500° F; said residual fuel having an ash content of less than about 30% to provide at least 5% of the heat required for said process in said rotary vessel, said volatiles content and said non-volatiles ignition temperature of said residual fuels being such that oxidation of the residual fuels occurs primarily in the calcination zone.