Ion exchange-strengthened silicate glass filter for ultraviolet light
Assignee: American Optical Corp
•
Filing: 1975-09-05
•
Granted: 1977-05-10
•
Expires: 1995-09-05
Abstract
Abstract There is provided by the process of the invention a silicate glass which provides protection against mechanical hazards and short and long wavelength ultraviolet radiation while at the same time high transmission of light in the visible range of the spectrum is maintained. By the process of the invention, the incorporation of cerium oxide into the glass followed by ion exchange strengthening using a mixture of potassium salt and silver nitrate provide a synergistic reduction in transmission of light in the ultraviolet range of the spectrum not heretofore obtainable by the use of either cerium oxide or silver staining of the glass alone.
Inventors
- 👤 Emil W. Deeg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:48
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/20; G02B5/22; G02B5/226; C; C03; C03C; C03C21/00; C03C21/001; C03C21/005; C03C3/00; C03C3/04; C03C3/076; C03C3/083; C03C3/085; C03C3/095; C03C4/00; C03C4/08; C03C4/085
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
123 words
An ion exchange-strengthened silicate glass made from a glass making batch in which each 100 parts by weight on an oxide basis consisting essentially of: about 64 to about 75 parts silicon dioxide, about 5 to about 10 parts potassium oxide, about 4 to about 8 parts sodium oxide, about 4 to about 8 parts calcium oxide, and about 2 to about 10 parts cerium oxide. whereby upon ion exchanging at a temperature either above or below the strain point of said glass in a bath comprising salts of potassium and silver said glass provides an impact-resistant glass filter for ultraviolet light having a wavelength below about 400 nanometers and wherein said filter is transparent to light having a wavelength about 400 nanometers.
Claim 2
Dependent Claim
123 words
An ion exchange-strengthened silicate glass made from a glass making batch in which each 100 parts by weight on an oxide basis consisting essentially of: about 64 to about 75 parts silicon dioxide, about 5 to about 10 parts potassium oxide, about 4 to about 8 parts sodium oxide, about 4 to about 8 parts calcium oxide, and about 2 to about 10 parts cerium oxide. whereby upon ion exchanging at a temperature either above or below the strain point of said glass in a bath comprising salts of potassium and silver said glass provides an impact-resistant glass filter for ultraviolet light having a wavelength below about 400 nanometers and wherein said filter is transparent to light having a wavelength about 400 nanometers.
Claim 3
Dependent Claim
38 words
The ion exchange-strengthened silicate glass filter of claim 1 wherein said glass comprises by weight on the oxide basis up to 2 percent aluminum oxide, up to 3 percent zinc oxide and up to 0.5 percent titanium oxide.
Claim 4
Dependent Claim
47 words
An ion exchange-strengthened silicate glass according to claim 1 wherein said glass comprises in parts by weight on the oxide basis: ______________________________________
silicon dioxide 65.4
sodium oxide 7.9
potassium oxide 8.5
calcium oxide 8.1
aluminum oxide 1.8
zinc oxide 2.8
titanium dioxide 0.5
cesium oxide 5.0
______________________________________
Claim 5
Dependent Claim
47 words
An ion exchange-strengthened silicate glass according to claim 1 wherein said glass comprises in parts by weight on the oxide basis: ______________________________________
silicon dioxide 67
sodium oxide 8
potassium oxide 8.8
calcium oxide 8.4
aluminum oxide 1.9
zinc oxide 2.9
titanium dioxide 0.5
cerium oxide 2
______________________________________
Claim 6
Dependent Claim
26 words
An ion exchange-strengthened silicate glass according to claim 1 wherein said glass comprises in parts by weight on the oxide basis 10 parts of cerium oxide.
Claim 7
Dependent Claim
141 words
The process of producing a silicate glass filter for ultraviolet light comprising ion exchange strengthening a silicate glass made by preparing a silicate glass making batch in which each 100 parts thereof by weight on an oxide basis consisting essentially of: about 64 to about 75 parts silicon dioxide, about 5 to about 10 parts potassium oxide, about 4 to about 8 parts sodium oxide, about 4 to about 8 parts calcium oxide, and about 2 to about 10 parts cerium oxide wherein said ion exchange is conducted at a temperature either above or below the strain point of said glass in a bath comprising salts of potassium and silver and whereby said glass provides an impact-resistant glass filter for ultraviolet light having a wavelength below 400 nanometers wherein said filter is transparent to light having a wavelength above 400 nanometers.
Claim 8
Dependent Claim
141 words
The process of producing a silicate glass filter for ultraviolet light comprising ion exchange strengthening a silicate glass made by preparing a silicate glass making batch in which each 100 parts thereof by weight on an oxide basis consisting essentially of: about 64 to about 75 parts silicon dioxide, about 5 to about 10 parts potassium oxide, about 4 to about 8 parts sodium oxide, about 4 to about 8 parts calcium oxide, and about 2 to about 10 parts cerium oxide wherein said ion exchange is conducted at a temperature either above or below the strain point of said glass in a bath comprising salts of potassium and silver and whereby said glass provides an impact-resistant glass filter for ultraviolet light having a wavelength below 400 nanometers wherein said filter is transparent to light having a wavelength above 400 nanometers.
Claim 9
Dependent Claim
72 words
The process of claim 6 wherein said silicate glass comprises in parts by weight on the oxide basis: ______________________________________
silicon dioxide 65.4
sodium oxide 7.9
potassium oxide 8.5
calcium oxide 8.1
aluminum oxide 1.8
zinc oxide 2.8
titanium dioxide 0.5
cesium oxide 5.0
______________________________________ and wherein said ion exchange strengthening is conducted at a temperature of about 350° C to about 450° C in a bath comprising silver nitrate and potassium nitrate.
Claim 10
Dependent Claim
38 words
The process of claim 7 wherein said bath comprises 98.3 weight percent potassium nitrate and 1.7 weight percent silver nitrate and said process is conducted at a bath temperature of 400° C over a period of 4 hours.
References Cited (Backward Citations)
US2647068A
Cited
US3424567A
Cited
US3533888A
Cited
US3495963A
Cited
US3923486A
Cited
US3790260A
Cited
US3899315A
Cited
US3898693A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-09 | 1980-11-08 | 1981-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-09 | 1984-11-08 | 1985-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-09 | 1988-11-08 | 1989-05-10 | $7700.00 | Window Closed / Lapsed |