Sintered cermets for tool and wear applications
Assignee: Individual
•
Filing: 1976-05-11
•
Granted: 1977-05-10
•
Expires: 1996-05-11
Abstract
Abstract A composition of material comprising aluminum oxide and refractory transition metal diborides, with additions of magnesium oxide and, optionally, transition metal carbides, nitrides, carbonitrides and iron group metals for sintering and grain morphology control, is disclosed, which is particularly useful as a cutting tool for steels, cast iron, and hard to machine materials, such as superalloys. In contrast to the TiC-Al 2 O 3 cermets of the prior art which have to be hot pressed for optimum properties, a large portion of the cermets of the invention can also be fabricated, without detriment to performance, by sintering the cold pressed powder compacts in an inert furnace atmosphere at temperatures between 1650° and 1820° C.
Inventors
- 👤 Erwin Rudy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:26
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/06; B23; B23B; B23B27/00; B23B27/14; B23B27/148; C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C04B35/71; C22; C22C; C22C29/00; C22C29/12; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12007
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
112 words
A composition of material consisting essentially of aluminum oxide, magnesium oxide, refractory transition metal diborides, refractory transition metal carbides and nitrides and alloying metals selected from the group consisting of the iron metals, chromium, molybdenum and tungsten, in which the aluminum oxide comprises at least 48 weight percent of the composition, the refractory transition metal diborides comprise from 5 to 50 weight percent of the composition, the refractory transition metal carbides and nitrides comprise from 0 to 35 weight percent of the composition, in which said magnesium oxide comprises between 0.3 and 3 weight percent of the composition and the alloying metals comprise from 0 to 6 weight percent of the composition.
Claim 2
Dependent Claim
112 words
A composition of material consisting essentially of aluminum oxide, magnesium oxide, refractory transition metal diborides, refractory transition metal carbides and nitrides and alloying metals selected from the group consisting of the iron metals, chromium, molybdenum and tungsten, in which the aluminum oxide comprises at least 48 weight percent of the composition, the refractory transition metal diborides comprise from 5 to 50 weight percent of the composition, the refractory transition metal carbides and nitrides comprise from 0 to 35 weight percent of the composition, in which said magnesium oxide comprises between 0.3 and 3 weight percent of the composition and the alloying metals comprise from 0 to 6 weight percent of the composition.
Claim 3
Dependent Claim
34 words
A composition of material according to claim 1 which is a sintered material with the aluminum oxide and the additional components combined forming two separate, but each continuous interpenetrating skeletons in the sintered structure.
Claim 4
Dependent Claim
30 words
A composition of material according to claim 1 in which the refractory transition metal diborides are diborides of a metal selected from the group consisting of titanium, zirconium and hafnium.
Claim 5
Dependent Claim
38 words
A composition of material according to claim 1 in which the refractory metal carbides and nitrides are carbides and nitrides of metals selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum and tungsten.
Claim 6
Dependent Claim
62 words
A composition of material according to claim 1 in which the transition metal diborides contain up to 20 weight percent of a diboride of a metal selected from the group consisting of vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, with the balance of the transition metal diboride being a diboride of metal selected from the group consisting of titanium, zirconium and hafnium.
Claim 7
Dependent Claim
66 words
The method of forming a composition of material according to claim 1, comprising the steps of: preparing a mixture of alloy ingredients under inert fluids or gases, until it has uniform consistency and the desired grain size distribution; compacting the mixture into a desired shape; and sintering the compacts so formed at temperatures between 1650° C and 1830° C under vacuum or an inert gas atmosphere.
Claim 8
Dependent Claim
68 words
The method of forming a composition of material according to claim 1, comprising the steps of: preparing a mixture of alloy ingredients under inert fluid and gases, until it has uniform consistency and the desired grain size distribution; pressure-sintering the mixture for 15 to 60 minutes at temperatures between 1650° C and 1830° C; and shaping the thus formed compact by cutting to the desired shape and size.
Claim 9
Dependent Claim
32 words
The method of claim 6 which further comprises the step of affixing a thin plate of the sintered compact to a carbide cutting tool so as to form a composite cutting tool.
Claim 10
Dependent Claim
32 words
The method of claim 7 which further comprises the step of affixing a thin plate of the sintered compact to a carbide cutting tool so as to form a composite cutting tool.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-09 | 1980-11-08 | 1981-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-09 | 1984-11-08 | 1985-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-09 | 1988-11-08 | 1989-05-10 | $7700.00 | Window Closed / Lapsed |