Removal of residual monomer in the presence of water by dielectric heating
Assignee: BP PLC
•
Filing: 1975-12-11
•
Granted: 1977-04-26
•
Expires: 1995-12-11
Abstract
Abstract Residual vinyl halide is removed from vinyl halide polymer by radiofrequency dielectric heating while maintaining the presence of water in the polymer by impeding evaporation of water from the polymer.
Inventors
- 👤 Anthony John Park
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:56
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/28; C08F; C08F6/00; C08F6/001; C08J2327/00; C08J2327/02
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
89 words
A process for reducing the residual vinyl halide monomer content of a particulate vinyl halide polymer containing at least 1% by weight of water based on the weight of dry polymer which comprises subjecting the polymer to a radiofrequency dielectric heating step to remove vinyl halide while maintaining the presence of water in the polymer so that not more than 30% by weight of the water present at the beginning of the dielectric heating evaporates during the dielectric heating, and recovering particulate polymer from the radiofrequency dielectric heating step.
Claim 2
Dependent Claim
89 words
A process for reducing the residual vinyl halide monomer content of a particulate vinyl halide polymer containing at least 1% by weight of water based on the weight of dry polymer which comprises subjecting the polymer to a radiofrequency dielectric heating step to remove vinyl halide while maintaining the presence of water in the polymer so that not more than 30% by weight of the water present at the beginning of the dielectric heating evaporates during the dielectric heating, and recovering particulate polymer from the radiofrequency dielectric heating step.
Claim 3
Dependent Claim
20 words
The process according to claim 1 wherein any copolymerised monomer constitutes not more than 30% by weight of the polymer.
Claim 4
Dependent Claim
14 words
The process according to claim 2 wherein the polymer is vinyl halide polymer resin.
Claim 5
Dependent Claim
35 words
The process according to claim 3 wherein the vinyl halide polymer subjected to radiofrequency dielectric heating is in the particulate form in which it is recovered from the polymerisation process in which it was produced.
Claim 6
Dependent Claim
25 words
The process according to claim 4 wherein the polymer subjected to radio frequency dielectric heating is in the form of beads recovered from suspension polymerisation.
Claim 7
Dependent Claim
23 words
The process according to claim 1 wherein the polymer contains at least 5% by weight of water, based on weight of dry polymer.
Claim 8
Dependent Claim
23 words
The process according to claim 6 wherein the polymer contains at least 20% by weight of water, based on weight of dry polymer.
Claim 9
Dependent Claim
23 words
The process according to claim 7 wherein the polymer contains up to 30% by weight of water, based on weight of dry polymer.
Claim 10
Dependent Claim
40 words
The process according to claim 1 wherein the evaporation of water is restricted such that not more than 20% by weight of the water present in the polymer at the beginning of the dielectric heating evaporates during the dielectric heating.
Claim 11
Dependent Claim
25 words
The process according to claim 9 wherein the evaporation of water is restricted such that not more than 10% by weight of the water evaporates.
Claim 12
Dependent Claim
29 words
The process according to claim 1 wherein the weight ratio of water to residual vinyl chloride monomer in the polymer fed to the dielectric heating is at least 10:1.
Claim 13
Dependent Claim
14 words
The process according to claim 11 wherein the weight ratio is at least 30:1.
Claim 14
Dependent Claim
28 words
The process according to claim 1 wherein the radiofrequency dielectric heating step is carried out using microwave radiation at a frequency in the range 900 to 30,000 MHz.
Claim 15
Dependent Claim
29 words
The process according to claim 13 wherein the radiofrequency heating step is carried out for a time sufficient to give a polymer temperature of 70° C to 100° C.
Claim 16
Dependent Claim
32 words
The process according to claim 14 wherein the applied power and time are selected so that the polymer contains less than 1 ppm of vinyl halide at the end of the treatment.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |