Process for manufacturing polymers of bicyclo [2.2.1] heptene-2 and its substitution derivatives
Assignee: Orkem SA
•
Filing: 1975-03-25
•
Granted: 1977-04-26
•
Expires: 1995-03-25
Abstract
Abstract Process for manufacturing finely divided polymers of bicyclo [2.2.1] heptene-2 compound comprising the steps of incompletely polymerizing said bicyclo [2.2.1] heptene-2 compound by the ring opening polymerizing technique in the presence of a catalyst system selected from the group comprising a compound of a noble metal of the platinum family and an alcohol-reducing solvent and tungsten hexachloride, an aluminum alkyl and an aromatic solvent, under superatmospheric pressure and in the presence of a quantity of solvent at least equal to that necessary for the solution of said catalyst system and abruptly reducing said pressure at a temperature higher than the vaporization temperature of the reaction mixture under said reduced pressure, whereby an expansion, a division and at least partial drying of the resulting polymer is obtained.
Inventors
- 👤 Jean Lahouste
- 👤 Maurice Lemattre
- 👤 Jean-Claude Muller
- 👤 Claude Stein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:26
CPC Classifications
C; C08; C08G; C08G61/00; C08G61/02; C08G61/04; C08G61/06; C08G61/08; Y; Y10; Y10S; Y10S526/00; Y10S526/909
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
132 words
In a method for manufacturing finely divided expanded ring opened polymers comprising polymerizing a bicyclo [2.2.1.] heptene-2 compound in the presence of a catalyst system selected from the group consisting of a noble metal compound with a reducing substance and a tungsten compound with a compound having at least one metal-hydrocarbon link, the improvement comprising: effecting said polymerization in a polymerization zone under super-atmospheric pressure and at an elevated temperature, passing the obtained mixture into an expansion zone maintained at a pressure substantially lower than that of said polymerizing zone and at a temperature higher than the vaporization temperature of the constituents of the reaction mixture to thereby simultaneously blow the so obtained polymer and dry said polymer, and dividing the resultant polymer to provide an apparent density from 0.2 to 0.8.
Claim 2
Dependent Claim
132 words
In a method for manufacturing finely divided expanded ring opened polymers comprising polymerizing a bicyclo [2.2.1.] heptene-2 compound in the presence of a catalyst system selected from the group consisting of a noble metal compound with a reducing substance and a tungsten compound with a compound having at least one metal-hydrocarbon link, the improvement comprising: effecting said polymerization in a polymerization zone under super-atmospheric pressure and at an elevated temperature, passing the obtained mixture into an expansion zone maintained at a pressure substantially lower than that of said polymerizing zone and at a temperature higher than the vaporization temperature of the constituents of the reaction mixture to thereby simultaneously blow the so obtained polymer and dry said polymer, and dividing the resultant polymer to provide an apparent density from 0.2 to 0.8.
Claim 3
Dependent Claim
34 words
Method in accordance with claim 1, wherein said ring opening polymerization is carried out in a double-screw extrusion machine having at least one expansion zone of reduced pressure upstream from the extrusion end thereof.
Claim 4
Dependent Claim
69 words
Method in accordance with claim 1 wherein, for a given range of temperatures and pressures and for a given quantity of catalyst, the flow-rates of said bicyclo [2.2.1.] heptene-2 and of the other constituents of the reaction mixture which may comprise a solvent are adjusted in order that the quantity of volatilisable materials leaving said polymerization zone represents between 50 and 100% of the weight of the resulting polymer.
Claim 5
Dependent Claim
21 words
Method in accordance with claim 1 wherein the polymerization is carried out in the presence of ruthenium trichloride dissolved in n-butanol.
Claim 6
Dependent Claim
25 words
Method in accordance with claim 1 wherein the polymerization is carried out in the presence of tungsten hexachloride, an aluminum alkyl and an aromatic solvent.
Claim 7
Dependent Claim
32 words
Method in accordance with claim 2 wherein said elevated temperature is from 100° C to 160° C in said polymerizing zone and from 140° C to 180° C in said expansion zone.
Claim 8
Dependent Claim
134 words
A process for manufacturing finely divided and expanded ring-opened polymers of bicyclo [2.2.1] heptene-2 having an apparent density of 0.2 to 0.8, comprising polymerizing said bicyclo [2.2.1] heptene-2 under super-atmospheric pressure and at an elevated temperature by the ring opening polymerization technique, in the presence of a catalyst selected from the group consisting of a compound of a noble metal of the platinum family with an alcohol-reducing solvent and tungsten hexachloride with an aluminum alkyl and an aromatic solvent, the quantity of solvent at least being equal to that necessary to solubilize said catalyst system, reducing the pressure and simultaneously increasing the temperature to a temperature higher than the vaporization temperature of the solvent and any unreacted monomer, and thereby simultaneously blowing ring-opened polymer, drying said polymer and dividing said polymer into particulate form.
Claim 9
Dependent Claim
134 words
A process for manufacturing finely divided and expanded ring-opened polymers of bicyclo [2.2.1] heptene-2 having an apparent density of 0.2 to 0.8, comprising polymerizing said bicyclo [2.2.1] heptene-2 under super-atmospheric pressure and at an elevated temperature by the ring opening polymerization technique, in the presence of a catalyst selected from the group consisting of a compound of a noble metal of the platinum family with an alcohol-reducing solvent and tungsten hexachloride with an aluminum alkyl and an aromatic solvent, the quantity of solvent at least being equal to that necessary to solubilize said catalyst system, reducing the pressure and simultaneously increasing the temperature to a temperature higher than the vaporization temperature of the solvent and any unreacted monomer, and thereby simultaneously blowing ring-opened polymer, drying said polymer and dividing said polymer into particulate form.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |